• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.1
• /
• pp.1-7
• /
• 2020

GGBFS(Ground Granulated Blast Furnace Slag) is one of the most actively used mineral admixtures with excellent long-aged strength and chloride diffusion resistance. Unlike Standard covering GGBFS in Japan and the U.K., the domestic standard for GGBFS does not contain low fineness of GGBFS under 4000 grade. In this paper, several basic tests are carried out for the concrete with 3,000 grade GGBFS concrete and ternary blended concrete for reducing hydration heat by mixing 4,000 grade GGBFS and fly ash, such as fresh concrete properties, compressive strength, and shrinkage properties. The air content and slump between the ternary blended concrete and the concrete with low-fineness GGBFS showed the similar level, and the results of difference in setting time from them were less than 20 minutes, showing no significant difference. In the evaluation of compressive strength and shrinkage characteristics, the ternary blended concrete showed lower long-aged strength and higher shrinkage than the low-fineness GGBFS concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.6
• /
• pp.9-17
• /
• 2019

Cement hydrates and the related characteristics change with ages, and the behaviors are much related with chloride diffusion. In this work, 30% replacement ratio with FA(Fly Ash) and GGBFS(Ground Granulated Blast Furnace Slag) are considered for concrete with three levels of W/B (Water to Binder ratio) and 2 years of curing period. Chloride diffusion coefficients from accelerated condition are obtained at 5 measurement period (28days, 56days, 180days, 365days, and 730days), and the results are compared with porosity, binding capacity, and permeability from program-DUCOM. The similar changing pattern between chloride diffusion and permeability is observed since permeability is proportional to the square of porosity. Curing period is grouped into 4 periods and the changing ratios are investigated. Cement hydrate characteristics such as porosity, permeability, and diffusion coefficient are dominantly changed at the early ages (28~56 days), and diffusion coefficient in OPC concrete with low W/B continuously changes to 180days.

• Journal of the Korean Institute of Rural Architecture
• /
• v.21 no.4
• /
• pp.45-52
• /
• 2019

Chemical grouting method is mainly used for construction of dams and reservoirs, stabilization and reinforcement of slopes, reinforcement of soft grounds such as embankments, dredging and landfills, the order of earthquake response method, and the reinforcement of structures. Recently, it is widely applied in construction sites such as highways, airfields, high-speed railways, subsea facilities, port construction works, tunnels, and subway works. As such, the demand for grouting continues to increase. The development of the grouting method was focused on increasing the strength of the ground, and the development of the chemical additives, the injection device, and the stirring device were mainly performed. But ordinary portland cement used for grouting is a product that consumes natural resources such as limestone, generates a large amount of greenhouse gases, consumes a large amount of energy sources, and it is time to develop products and new methods to replace them. In this study, Ordinary Portland Cement and New Grouting Binder (circulating fluidized bed boiler fly and blast furnace slag) were compared and analyzed by the following test. Homo-gel strength and homo-gel time, water quality analysis of the water used and soil contamination process tests of homo-gel samples were performed. In the case of NGB, when Using water is used as the reservoir water, the strength measured smaller than that of the other water. However, it shows about 2.5 times greater than the homo-gel compressive strength applied to OPC (7-day, reservoir water), so there is no problem with water quality when applied.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.4
• /
• pp.354-359
• /
• 2014

The objective of this study is to examine the fatigue behavior in compression of normal-weight and lightweight concrete mixtures with high volume supplementary cementitious material(SCM). The selected binder composition was 30% ordinary portland cement, 20% fly-ash, and 50% ground granulated blast-furnace slag. The targeted compressive strength of concrete was 40 MPa. For the cyclic loading, the constant maximum stress level varied to be 75%, 80%, and 90% of the static uniaxial compressive strength, whereas the constant minimum stress level was fixed at 10% of the static strength. The test results showed that fatigue life of high volume SCM lightweight concrete was lower than the companion normalweight concrete. The value of the fatigue strain at the maximum stress level intersected the descending branch of the monotonic stress-strain curve after approximately 90% of the fatigue life.

• Journal of the Korea Convergence Society
• /
• v.8 no.2
• /
• pp.157-162
• /
• 2017

Inorganic stiffening agents were prepared by mixing paper sludge incineration ash, blast furnace slag fine powder quicklime, anhydrous gypsum and fly ash. The main components of the solidifying agent developed for sludge treatment were SiO, $Al_2O_3$, $TiO_2$, $Fe_2O_3$, $Mn_2O_3$, CaO, MgO, $Na_2O$, $K_2O$, $P_2O$, and $SO_3$. Unlike cement, the developed solidifying agent did not contain $Cr^{6+}$, which is known as a carcinogen. Heavy metals and oil contaminated soil were mixed with solidifying agent and cured for 7 days and the heavy metal content was below the environmental standard. Sewage sludge cake, food waste and solidifying agent were mixed with each other, and after 7 days curing, soil component test showed that the heavy metal content was below the environmental standard. After mixing the sludge, solidifying agent and additive mixture into the beaker, the ammonia concentration was measured to be 0 after 3 days.

• Journal of Convergence for Information Technology
• /
• v.7 no.1
• /
• pp.67-73
• /
• 2017

Paper sludge ash, blast furnace slag, fine powder quicklime, anhydrous gypsum, and fly ash as the main ingredients were prepared to suit the salty soils of marine soils. The solidification component is a kind of recycled ceramic, and CaO plays an important role in solidification. The neutralization time after solidification was about 2 weeks, and the compressive strength was about 12N/mm2 in the mortar test after one week incubation with standard yarn. This is about 14 times stronger than the solidifying agent used in the metropolitan area. As a result of applying plate load test to saltous marine soils, we obtained the yield load that can pass the large scale even after 5 days. In the uniaxial compressive strength test, shear strength of about 300 kPa was obtained after 5 days. It will be useful for supplementing the soft ground in the area where marine reclamation is much like the Incheon area.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.559-568
• /
• 2015

In this study, multi-component blended concrete mix with fly ash and ground granulated blast furnace slag according to 3 level of type of warter reduction agent (type of 0%, 8% and 16%) and 3 level of water-binder ratio (40%, 45% and 50%) was prepared for evaluation of effect of physical characteristics of concrete using multi-component blended binder according to warter reduction efficiency of warter reduction agent. In addition, concrete mix was carried out repetition test of three times in order to secure the reliability. As a result, compressive strength according to type of warter reduction agent was found that difference of strength was about 20% occurred, warter reduction efficiency of warter reduction agent was showed that a great influence on qualities of concrete. Therefore, reflected the effect of warter reduction efficiency of warter reduction agent, prediction model equations of compressive strength for multi-component blended concrete was proposed, it was found that more than 90% of the high correlation.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.6
• /
• pp.553-559
• /
• 2015

In this study, to suggest the application method of recycled fine aggregate, the non-cement mortar was prepared and studied with the binders of blast furnace slag, fly ash, and fly ash from combined heat power plant. As a basic experiment, a series of tests was conducted to determine the potions of the binders and types of activator. When the binder was consisted with 20% of fly ash and 40% of fly ash from combined heat power plant, the highest strength of the mortar was obtained, and as an activator, the combination of sodium hydroxide 2.5%, and calcium hydroxide 7.5% showed the highest strength of the mortar. Therefore, this study focuses on engineering properties of mortar contains fly ash from combined heat power plant and recycled fine aggregate according to replacement ratio of recycled fine aggregate based on the optimum mix from the basic experiment. As a result, the best replacement ratio of recycled fine aggregate is 75%.

• Journal of the Korea Concrete Institute
• /
• v.27 no.4
• /
• pp.435-441
• /
• 2015

Concrete, as a porous media, has permeability and it is considered as a major parameter for durability evaluation. Cold joint caused by delayed placing of concrete accelerates water permeation and intrusion of harmful ions. In the paper, concrete specimens containing GGBFS (Ground Granulated Blast Furnace Slag) and OPC (Ordinary Portland Cement) are prepared with cold joint section, and water permeability and water flow at the age of 91 days are measured for 2 weeks. Sound concrete with GGBFS shows decreased permeability to 89% for sound concrete with OPC and 0.86 of decreasing ratio is evaluated in GGBFS concrete with cold joint. Through WPT (Water Penetration Test), the effects of mineral admixture and cold joint on water permeability are evaluated, and variation in water behavior via cold joint is analyzed through probabilistic method as well.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.94-101
• /
• 2011

In this study, in order to develop organic-inorganic hybrid packaging materials(PM) of bike paths using blast furnace slag(BS) as industrial by-products, fundamental properties of organic-inorganic hybrid packaging materials were performed. Test result, the increase of Acryl emulsion polymer(AEP)/binder(B) ratios tends to delay the setting time, to increase the table flow, to decrease the strength by material segregation and to increase the length change. The optimal mix proportion of AEP decides on 40%(AEP/B) due to workability and high strength. The increase of BS replacement ratios also tends to delay the setting time, to separate AEP from B and to decrease the strength by material segregation. When BS replacement ratios were lower than 40%, they are satisfied with goal properties.