• Journal of Welding and Joining
• /
• 제17권4호
• /
• pp.26-31
• /
• 1999

An attempt was made in this study to investigate the brazing characteristics of Zr-Be binary amorphous alloys for the development of a new brazing filler metal for joining Zircaloy-4 nuclear fuel cladding tubes. This study was also aimed at the feasibility study of rapidly solidified amorphous alloys to substitute the conventional physical vapor-deposited(PVD) metallic beryllium. The $Zr_{1-x}Be_{x}$($0.3\leq$x$\leq0.5$) binary amorphous alloys were produced in the ribbon form by the melt-spinning method. It was confirmed by x-ray diffraction that the ribbons were amorphous. The amorphous. the amorphous alloys were used to join bearing pads on Zircaloy-4 nuclear fuel cladding tubes. Using Zr-Be amorphous alloys as filler metals, it was found that the reduction in the tube wall thickness caused by erosion was prevented. Especially, in the case of using $Zr_{0.65}Be_{0.35}$ and $Zr_{0.7}Be_{0.3}$ amorphousalloys, the smooth and spherical primary $\alpha$-Zr particles appeared in the brazed layer, which was the most desirable microstructure from the corrosion-resistance standpoint.

• 한국재료학회지
• /
• 제12권2호
• /
• pp.140-145
• /
• 2002

This study was conducted to investigate the brazing characteristics between Zircaloy-4 nuclear fuel cladding tubes and bearing pads with filler metals of amorphous $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.5) binary alloy, in which they were produced in the ribbon form by the melt-spinning metod. The crystallization behavior, stability, hardness and micro-structure of brazed zone were examined by X-ray diffraction, differential scanning calorimetry, micro-Vickers hardness test, optical microscopy, and transmission electron microscopy. $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.4) amorphous alloys were crystallized to $\alpha$-Zr with increasing the temperature, and the rest were transformed to ZrBe$_2$at higher temperatures. On the other hand, $Zr_{1-x}Be_x$(0.4$\leq$x$\leq$0.5) amorphous alloys were crystallized to $\alpha$-Zr and ZrBe$_2$, simultaneously. The thickness of the layer brazed with amorphous alloy was increased with increasing the beryllium content due to the higher diffusion of Be. The morphology of brazed layer with PVD Be filler metal showed dendrite while that brazed with amorphous alloys appeared globular. Micro-Vickers hardness of brazed zone increased as the beryllium content of filler metal was decreased.

• 한국산학기술학회논문지
• /
• 제7권2호
• /
• pp.113-119
• /
• 2006

중수로형 핵연료 제조공정 중 연료봉 피복관에 간격체와 지지체 등의 부착물이 브레이징으로 접합된다. 본 연구에서는 베릴륨을 물리 증착법(PVD)으로 접합될 부착물의 표면에 증착한 것과 비정질 용가재[$Zr_{1-x}Be_{x}(0.3{\le}x{\le}0.5)$]를 사용하여 브레이징된 접합부의 미세조직과 경도 등의 특성을 비교하고 브레이징 온도가 접합부에 미치는 영향 조사하였다. 비정질 용가재에 의한 접합층의 두께는 PVD-Be의 경우와 비교하여 더 얇았고, Be 함량이 감소할수록 접합층의 두께는 감소하였으며 모재의 침식은 거의 없었다. PVD-Be의 경우 공정 반응, 액상 출현, 모세관 현상과 확산으로 브레이징 되나 비정질 합금은 용가재 만이 용융되어 액상 접합되는 것으로 사료된다. PVD-Be 접합부의 미세조직은 계면에서 수지상이 형성되어 내부로 성장하나, 비정질 합금에 의한 접합부는 석출된 제2상들이 구상으로 구성되며 브레이징 온도가 증가할수록 구상은 더욱 커졌다. 비정질 합금 접합부의 경도는 Be 함량이 감소할수록 경도는 증가하였다. 본 연구에 사용된 비정질 합금 중 $Zr_{0.7}Be_{0.3}$ 합금은 접합부에서 Be의 모재로의 확산이 적어 부드러운 계면과 모재의 침식이 없었고 높은 경도 때문에 핵연료 피복재 접합에 가장 적합한 용가재로 사료된다.