• Progress in Superconductivity
• /
• 제2권2호
• /
• pp.65-70
• /
• 2001

$Pb/Bi_2Sr_2CaCu_2O_{8+\delta}$-single-crystal junctions with the tunneling direction along the c axis of the crystal were fabricated to obtain an s-wave-superconductor/d-wave-superconductor Josephson junctions. The tunneling R (T) curves and current-voltage characteristics show distinct features which can be explained only under the assumption that the order parameter of high-$T_c/Bi_2Sr_2CaCu_2O_{8+{\delta}}$ superconductors has a pure d-wave symmetry, which is in contrast to the case of $YBa_2Cu_3O_{7+{\delta$}}$erconductors where a minor s-wave component is also present..

• 한국세라믹학회지
• /
• 제38권4호
• /
• pp.360-364
• /
• 2001

고상반응법(solid-state reaction)으로 산화물 초전도체 Bi$_{2+x}$ Sr$_{1.8}$ $CaCu_2$$O_{8+\delta}$(-0.2$\leq$x$\leq$0.2)을 제조하여 조성변화에 따른 산소량과 Bi 이온의 하전가(valence)가 구조변조의 주기에 미치는 영향을 조사하였다. 2212상의 단일상 고용한계는 -0.1$\leq$x$\leq$0.1 영역이었다. 이 영역에서 x의 증가에 따라 격자상수 c는 감소를 보이며, 온셋 임계온도 Tc$^{on}$ 과 산소량은 증가하는 경향을 보였다. 또한, Bi 이온의 하전기와 구조변조의 주기는 단일상 고용한계 영역 내에서 x의 증가에 따라 감소하는 경향을 보이고 있다. 구조변조의 주기는 산소량이 증가함에 따라 감소하고 Bi 이온의 하전가 증가에 따라 증가함을 보였다. 즉, 산소의 절대량과 Bi 이온의 하전가에 따라 구조변조의 주기가 변화하는 것을 알 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제16권6호
• /
• pp.522-531
• /
• 2003

Samples with the nominal composition, B $i_{1.84}$P $b_{0.34}$S $r_{1.91}$C $a_{2.03}$C $u_{3.06}$ $O_{10+{\delta}}$ high- $T_{c}$ superconductors containing MgO as an additive were fabricated by a solid-state reaction method. Samples with MgO of 5~30 wt% each were sintered at 820~86$0^{\circ}C$ for 24 hours. The structural characteristics, critical temperature, grain size and image of mapping with respect to MgO contents were analyzed by XRD(X-Ray Diffraction), SEM(Scanning Electron Microscope) and EDS(Energy dispersive X-ray spectrometer) respectively. As MgO contents increased, intensity of MgO Peaks and ratio of Bi-2212 phase in superconductors intensified and the proportion of the phase transition from Bi-2223 to Bi-2212 was increased.

• 한국세라믹학회지
• /
• 제37권8호
• /
• pp.787-791
• /
• 2000

Samples with the nominal composition, Bi2-xGexSr2CaCu2O8＋$\delta$ (x=0, 0.1, 0.2, 0.3, 0.4, 0.5) were prepared by the solid-state reaction method. We have studied the effect of substitution Ge for Bi and investigated the superconducting properties by changing oxygen content with Ge substitution. It was found that temperature difference, ΔK, between TCon and TCzero was considerably smaller in the samples prepared by the intermediate pressing method than that in the samples by the solid-state reaction method. We found the solubility limit of Ge to the 80 K single phase was around x=0.3. Within the solubility limit, lattice constant c decreased with the increase of x. In the region of the 80K single phase, the onset critical temperature TCon increased and excess oxygen content decreased with increase of x.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1990년도 추계학술대회 논문집
• /
• pp.26-30
• /
• 1990

Bi$\_$0.7/Pb$\_$0.3/Sr$_1$Ca$_1$Cu$\_$1.8/Ox thick films were screen printed on magnesia(MgO), silver and yttrium stabilized zirconia (YSZ) substrates and were sintered in a boat with cover to prevent the evaporation. The high-Tc phase increase and the low-Tc phase and Ca$_2$PbO$_4$ decrease with an increase in sintering temperature from 835$^{\circ}C$ to 860$^{\circ}C$. YSZ substrate interact strongly with the oxide resulting in poor superconductor, while the Ag and MgO substrates were satisfactory to make screen printed superconductors. The Bi$\_$0.7/Pb$\_$0.3/Sr$_1$Ca$_1$Cu$\_$1.8/Ox thick films screen printed both on Ag and MgO substrates show high Tc phase of ~85% and Tc of 96K.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제52권6호
• /
• pp.249-256
• /
• 2003

Samples with the nominal composition, Ag-$Bi_{1.84}Pb_{0.34}Sr_{1.91}Ca_{2.03}Cu_{3.06}O_{10+{\delta}}$ high $T_{c}$ superconductors containing Ag as an additive were fabricated by a solid-state reaction method. Samples with Ag of 10 wt%, 30 wt%, and 50 wt% each were sintered at $860^{\circ}C$~$870^{\circ}C$ for 24 hours. The structural characteristics, the microstructures and the critical temperature with respect to the each samples were investigated by XRD, four-prove methode, SEM and EDS respectively. The $T_{c}\;^{zero}$ of the sample with the 50 wt% Ag additive at the surface showed 94 K.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1990년도 추계학술대회 논문집
• /
• pp.31-35
• /
• 1990

In the ($Bi_{1-x}Pb_{x}$)$_2$$Sr_2$$Ca_2$$Cu_{3.6}$$O_{y}$ (x=0∼0.5) superconductors, DTA and XRD-pattern analyses were performed to obviousely define optimal calcining and sintering temperature. And, understanding behaviors of High-Tc phase with preparation condition of superconductors, that is, calcining and sintering temperature, sintering time, and variation of Pb contents, in order to make single phase of superconductor, microstructure and its composition were analyzed with SEM, XRD, and EDAX. continuously, the cause of phase transition was define with synthetically studying mutural relation between measured electrical resistivity and current density. Also, in order to design enhancement of critical current density, Jc required for realization, samples varied with pressing condition were made, and measured its, Jc.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1007-1013
• /
• 1998

The samples of Bi2Sr2Ca1-xNaxCu2O8+y with various carrier concentration were synthesized by substituting Na for Ca ion. The superconducting properties hall coefficients and X-ray powder diffraction were measur-ed the sampled. Single phase samples were obtained for 0$\leq$x<0.3 of Bi2Sr2Ca1-xNaxCu2O8+y In the single phase the critical temperature. {{{{ { T}_{c } }} and carrier concentration increase with the increase of Na concentration pass through a maximum and then decreases. In the range of x$\geq$0.7 to the Na doped samples however we observed the metal-semiconductor transition. The c-axis seemed to decrease and a and b-axes increase with increasing Na concentration in the single phase. Decreasing of c-axis while increasing x is due to the smaller size of {{{{ {Na}^{+1 } }} ions to the {{{{ { Ca}^{+2 } }} ions. In the range of x>0.3 however the trend becomes ambiguous due to the inclusion of the 10K phase and impurity phase.

• 한국전기전자재료학회논문지
• /
• 제15권4호
• /
• pp.308-313
• /
• 2002

Samples with the norminal composition, $Bi_{2-x}Au_xSr_2CaCu_2O_{8+\delta}$ (x = 0, 0.05. 0.1, 0.15) were prepared by the solid-state reaction method. The superconducting properties, x-ray powder diffraction patterns, critical temperature and microstructure of surface were measured the samples. x-ray patterns show the single phase(2212) nature of the samples. But, the peaks of 2201 at $2\theta=30^{\circ}$ and Au peak at $2\theta=38.31^{\circ}$ are observed in the Au additive samples. The grain sire are enlarged with the increase of x. As the result of enlargement the grain size, the onset and offset critical temperature($T_c^{on}$,$T_c^{zero}$) increased with increase of x.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1989년도 추계학술대회 논문집 학회본부
• /
• pp.119-121
• /
• 1989

The properties of Pb-doped Bi-Sr-Ca-Cu-O Super-conductors prepared by solidstate reaction have been studied. Zero resistance was attained at l03K for the sample sintered 845[$^{\circ}C$]for 264hours and it was depended upon sintering conditions. From XRD data low Tc phase and high Tc phase were observed and the volume fraction of high Tc phase increased with increase in sintering period. The grain size increased with increase in sintering temperature and time.