• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.551-554
• /
• 2004

Bi-2223 HTS tapes are used widely for application of superconducting power systems. However there are need the properties of high strength and low AC loss. Two kinds of Bi-2223 HTS tapes with different Ag sheath were used to know the effect of sheath alloying for the strength and the resistivity. The workability and reaction degree of superconducting phase at Bi-2223 HTS tapes were investigated. We designed conventional type-Ag/alloy and double sheathed mono filament type-Ag/alloy/alloy in order to increase the strength and resistivity of matrix in Bi-2223 HTS tapes. The effect of axial strain and thermal cycling on the critical current was investigated for the Bi-2223 HTS tapes. Because the workability of double sheath Bi-2223 HTS tape was lower than one sheath Bi-2223 HTS tape, it was need additional softening treatment. Bi-2223 formation reaction was decreased by Ag alloy matrix during sintering process. Two kinds of Bi-2223/Ag tapes with different Ag sheath were used to know the effect of sheath alloying for the tensile strain. Critical current is drastically decreased for Ag/alloy and Ag/alloy/alloy sheathed tapes at tensile strain above 0.24 % and 0.34 %, respectively. This result showed that mechanical strength was increased over than 40 % by introduce double sheath at mono filament stage.

• Progress in Superconductivity and Cryogenics
• /
• v.4 no.1
• /
• pp.40-44
• /
• 2002

Influences of bending strain on the critical current (Ic) were investigated in Bi-2223 superconducting tapes at 77K. The effect of bending mode on the Ic degradation behavior was discussed in viewpoints of test procedure, n-value and damage morphology Especially, in this paper, we reported the Ic behavior in Ag alloy/Bi-2223 multifilamentary superconducting tapes under bending occurred within a width plane of the tape which was called as a hard bending. The Ic degradation under hard bending appeared significantly as compared with that under easy bending. The n-value decreased slightly with the increase in bending strain under the hard bending.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.8
• /
• pp.718-723
• /
• 2000

The critical characteristics of Bi-2223 HTS tapes made by PIT method are influenced by the heat treatment and the mechanical processing. In this study firstly we investigated the influence o rolling reduction rate in mechanical process for improving Jc of HTS tapes. As a result the optimized rolling reduction rate that we obtained was 10%-50% and 30%-30% (1st-2nd). And then we fabricated the stacking type HTS tapes that made of the multi-filamentary tapes with various length(3, 5, 10cm) and with various number of stacking (1, 5, 10 layer). Measuring the critical current and observing the structure of grain we concluded that the stacking type tapes will be able to operate more stably by adding the number of stacking tapes. And we could expect that by minimizing the gap between Ag-sheath of tapes mechanical strength of stacking HTS tapes is enhanced and current in tapes will flow more stably.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1339-1341
• /
• 1997

The various type Ag sheathed Bi-2223 tapes have been were fabricated by Powder-in-tube(PIT) process. The critical current density could be improved with the value of $23,000\;A/cm^2$(77 K, zero field) in the single concentric Bi-2223 tape. The bending property dependence of $I_c$ was improved in the double concentric Bi-2223 tape compared with single filamentary and single concentric one.

• The Transactions of the Korean Institute of Electrical Engineers B
• /
• v.49 no.4
• /
• pp.240-245
• /
• 2000

The self-field losses in a long multifilamentary Bi-2223/AgMgNi tape with varying transport current, voltage tap configurations, frequency and tape arrangements were investigated. Experimental results show that the measured losses are strongly dependent on voltage gap configurations but independent on tape arrangements. All voltage taps except the center tap are found to agree well with those predicted by Norris for an elliptical conductor. The self-field losses are purely hysteretic in nature in the range of applied frequencies for the transport currents below the critical current.

• Progress in Superconductivity and Cryogenics
• /
• v.6 no.1
• /
• pp.6-11
• /
• 2004

The influences of mixed strain mode of bending-tension on the critical current. Ic in externally reinforced Bi-2223 tapes and their interaction were investigated in this study. A test fixture which providing a mixed deformation mode of bending-tension to HTS tapes has been newly devised. When the total strain induced in the tape in the mixed strain mode was expressed by the superposition of the bending and tensile strains the irreversible strain for the critical current degradation of Bi-2223 tapes increased, as compared with the simple bending mode case. The $I_c$ degradation at the region exceeding the irreversible strain showed a medium between the simple bending case and the simple tension case. As the initial bending strain imparted increased , namely as the diameter of mandrel adopted decreased. the apparent irreversible strain in Bi-2223 tapes increased . but the increment became smaller As a result. it can be found that the tension to be applied to bent Bi-2223 tapes during cabling should be smaller. as the mandrel diameter becomes smaller.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2001.02a
• /
• pp.193-196
• /
• 2001

This paper deals with the fabrication and characteristic experiment of a high-Tc superconducting(HTSC) power supply using by Bl-2223 tape. The purpose of this research is to apply real HTSC load. This system consists of two heaters, an electromagnet, a Bi-2223 solenoid and a Bi-2223 pancake load. In the experiment. 17sec and 8.5sec were used for pumping period. Mechanism of the superconducting switch is used for heater-trigger. In experiment, the pumping-current has reached about 1.2A.

• Progress in Superconductivity and Cryogenics
• /
• v.7 no.4
• /
• pp.4-9
• /
• 2005

The degradation behavior of the critical current $(I_c)$ of Bi-2223 superconducting tapes under pressurized liquid nitrogen were investigated using a newly developed p-shaped sample holder which gives a series of bending strains to a sample. Three kinds of commercially available multi-filamentary Bi-2223 superconducting tapes were used. At atmospheric pressure, the Ie degradation behavior depended on the manufacturing process undergone by each tape. The tapes externally reinforced or densified by over pressure showed better bending strain tolerance than the Ag alloy-sheathed Bi-2223 tape. But these tapes showed a significant $I_c$ degradation when pressurized to 1 MPa in liquid nitrogen. For all samples, after depressurization to atmospheric pressure from 1 MPa, the Ie was completely recovered to its initial values at atmospheric pressure. When the samples were subjected to a thermal cycle wherein the tape was warmed up to room temperature after being depressurized from 1 MPa, it was found that the larger degradation of $I_c$ occurred at the regions where significant ballooning occurred, such as $0\%\;and\;0.2\%$. However, an improved ballooning damage tolerance was observed in the highly-densified tape.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.11
• /
• pp.589-595
• /
• 2000

In this papre, AC losses of Bi-2223 tapes with different twist pitch of superconducting core were fabricated, measured and analyzed. These samples produced by a powder-in-tube method are multi-filamentary tape with Ag matrix. Also, it's produced by non-twist and different twist pitch(8, 10, 13, 30, 50, 70 mn). The critical current measurement was carried out under the environment in Liquid nitrogen and in zero field by 4-probe method. And the AC loss measurement was carried out under the environment of applied time-varying transport current by transport method. From experiment, the critical current is larger non-twist than twisted filament. And, the AC loss by Norris equation is higher non-twisted tape than 13mm twisted tape. Also, it is confirmed that of AC loss of tape having non-twist pitch larger than those having differnet twist pitch.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1554-1556
• /
• 2000

Normal zone propagation(NZP) characteristics were investigated on Ag sheathed multi filamentary Bi-2223 tape and cylindrical stacking conductor. The critical current($I_c$) of Ag sheathed Bi-2223 tape and cylindrical stacking conductor were 12 A, 63 A at 77 K, 0 T. Normal zone propagation(NZP) experiments with tape were conducted with refrigerator in temperature from 45 K to 77 K, 0 T. Cylindrical stacking conductor was molding with epoxy and experiments were conducted with adiabatic condition in $LN_2$. NZP velocities of tape with two condition of DC and AC were almost same at each temperature. Temperature ($T_1$) of tape with distance of 0.5 cm from heater was strongly climbed up to 95K and slowly decreased. NZP velocities of cylindrical stacking conductor were 1.9-2.4 cm/sec in $LN_2$.