• 대한기계학회논문집
• /
• 제10권6호
• /
• pp.898-905
• /
• 1986

본 논문에서는 강의 피로균열진전거동과 미시조직과의 관계를 밝히기 위한 연 구의 일환으로 제이상 마르텐사이트 중에 모상 페라이트가 존재하는 복합조직강을 준 비하여 이들 강의 제이상 경도변화에 따른 피로균열진전저항을 균열휨과 균열닫힘을 통하여 검토하였다.

• 한국생산제조학회지
• /
• 제18권4호
• /
• pp.395-400
• /
• 2009

As the variables affecting the fatigue behavior have uncertainty, the fatigue crack propagation is stochastic in nature. Therefore, the fatigue life prediction is critical for the design and the maintenance of many structural components. In this study, fatigue experiments are conducted on the specimens of magnesium alloy under the different thicknesses of specimen. The effects of specimen thickness on the probability distribution of the fatigue crack propagation life and the crack size are estimated experimentally. The probability distribution of the crack size and the fatigue life for different specimen thicknesses are investigated by Anderson-Darling test and the best fit for those probability distributions are also presented.

• 대한기계학회논문집
• /
• 제11권2호
• /
• pp.243-252
• /
• 1987

본 논문에서는 작은 인공결함을 가진 표면균열의 진전거동을 밝히기 위하여 용접성이 좋고 강도도 적당하며 내식성이 좋아 해양구호무재 및 용접구호물재로서 널 리 사용되는 5083-H113 알루미늄합금을 준비하고 이재료의 피로표면균열 진전거동에 미치는 응력비의 영향을 균열닫힘과 함께 검토하였다.

• 한국해양공학회지
• /
• 제11권3호
• /
• pp.29-38
• /
• 1997

Crack penetration behavior by fatigue crack propagation and measurements of AE before-and-after crack penetration were examined using SS41 steel plate. Experimental crack shape of SU type was in good agreement with calculated shape rather than S type. Crack propagation behavior on the front surface appears not to change markedly after penetration. However, crack growth on the back surface appears to accelerate as reported by author. As a crack propagates, AE occurred heavily just before penetration. Then, it decreases and crack is penetrating. A transition from plane strain to plane stress was observed by fractographic study. At this time, separation of fracture surface was shown which affects AE occurrence.

• 한국자동차공학회논문집
• /
• 제9권3호
• /
• pp.181-189
• /
• 2001

For the Tailor Welded Blank sheet used fur automobile body panel, the characteristics of fatigue crack propagation behavior were studied. The thickness of specimen was machined to be same (0.9+0.9mm) and different (0.9+2.0mm). As a base test, mechanical properties around welding zone were examined. The results indicated that there were no significant decreases in mechanical properties, but hardness around welding bead is 2.3 times greater than base material. The crack propagation rate was noticeably decreased around welding line and rapidly increased as it passed by welding line. Reviewing the shape of the crack propagation, crack width around welding line was wide around the welding zone due to retardation of crack growth, but it became narrow passing welding line due to decreased toughness. Elasto-Plastic analysis was performed by finite element analysis fur explaining the test results.

• 대한기계학회논문집
• /
• 제13권5호
• /
• pp.938-946
• /
• 1989

본 연구에서는 CT시험편을 이용하여 소규모 항복조건하에서 하한계(near threshold)영역과 안전균열성장(제II)영역의 균열진전거동을 파악하고 피로균열 진전속도와 음향방출거동, 파단면 특성을 각각 비교, 고찰하여 각 파라미터간의 상관 관계 및 유용성을 검토하고자 한다.

• 대한기계학회논문집A
• /
• 제21권7호
• /
• pp.1097-1105
• /
• 1997

Because of the existence of stress interaction field made by other defects and propagating cracks, the structure may be weakened. Therefore in this study, the crack behavior in the interaction field made by two different cracks is studied experimentally. In the experiment, vertical distance between two cracks and applied stress are varied to make different stress interacted field. In addition, the effect of plastic zone is used to examine crack propagation path and rate. Three types of crack propagation in the interacted field were found, and crack propagating path and rate of two cracks were significantly changed according to different applied stress as each crack propagates. And the results are attributed to the effect of the size and shape of the plastic zone.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.333-337
• /
• 2008

This study investigates crack propagation behavior of Sn-3.0Ag-0.5Cu solder under pull-push loading conditions. Fatigue Crack Growth (FCG) tests were conducted on Center Cracked Plate (CCP) specimens in fast-fast (pp) strain waveform. The fast-slow (pc), slow-fast (cp) and slow-slow (cc) strain waveforms were also used to study the effect of strain rates. The crack propagation rates for the four strain waveforms were correlated with J-integral range and a scatter band of factor 4 was found. The crack growth rates for the pc waveform was highest, followed by cp, cc and then pp waveforms.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2005년도 춘계학술대회 논문집
• /
• pp.264-271
• /
• 2005

This study investigates the behavior of fatigue crack propagating between holes or holes filled with another materials. When holes or the holes bonded with another materials exist near center crack symmetrically, crack propagation rate is influenced by the bonding force of brazing part and the elastic modulus ratio of another material to matrix. It is experimentally and analytically confirmed that the center crack stops when its tip reaches near the center line of the holes and a small crack is initiated from the boundaries of holes or the holes filled with another materials and it propagates to final fracture. The mechanical behaviors of center crack near another materials are also investigated.

• 한국공작기계학회논문집
• /
• 제14권6호
• /
• pp.74-82
• /
• 2005

This study investigates the behavior of fatigue crack propagating between holes or holes filled with another materials. When holes or the holes bonded with another materials exist near center crack symmetrically, crack propagation rate is influenced by the bonding force of brazing part and the elastic modulus ratio of another material to matrix. It is experimentally and analytically confirmed that the center crack stops when its tip reaches near the center line of the holes and a small crack is initiated from the boundaries of holes or the holes filled with another materials and it propagates to final fracture. The mechanical behaviors of center crack near another materials are also investigated.