• Journal of Welding and Joining
• /
• 제20권3호
• /
• pp.109-115
• /
• 2002

In this study high power Nd:YAG laser welding of structural steel was investigated. For the test steel blocks of $50{\times}50{\times}200mm$ were cut and machined, and bead-on-plate weld was made on the machined surface. Argon, nitrogen, helium, dry air or mixed gases were used to find the effect of shielding conditions on the bead formation. Results demonstrated that there were Fe I rich region and Fe II rich region in the laser induced plasma column based on the spectral analysis with S-2000 field spectrometer The Fe I region was located at the root of the column near keyhole opening. On the other hand, Fe II region was found at the middle of the plasma column. In the Nd:YAG laser welding, Fe I region emitted continuum which had peak value at wave length of around 710nm, and Fe II region had the peak at 580nm. In the welding of steel by $CO_2$ laser, however, no continuum was observed. There showed two groups of strong spikes in the $CO_2$ laser welding; the first group was displayed at the wave band of 450-560nm. This spike group emitted stronger intensity of light and sharper peaks than those group at 680-800nm.

• Journal of Welding and Joining
• /
• 제11권4호
• /
• pp.57-69
• /
• 1993

In the present study, the microstructure and Charpy V notch toughness of multipass $CO_2$ FCA weldment in three different heat inputs(1-3KJ/mm)were investigated. The weldments using two different domestic FCAW wires(AWS E71T-1 and E71T-5 equivalent) in C-Mn steel were chemically analysed. The following conclusions can be inferred. 1. T-1 wire Showed a stable arc transfer, less spatter and harsh, a better bead spreading and easy slag removal, whereas T-5 wire suffered from the arc stability, which tended to increase spatter and produce a more convex bead. 2.The microsturctures of the top beads of the weldments in three different heat inputs consisted of coarse-grained boundary ferrite and Widmanstatten ferrite side plate with increasing heat inputs. The modest fraction of acicular ferrite in the two wire weldments was observed in the 2KJ/mm heat input. 3.The fine-grained reheated zones of both welds consisted of a duplex microstructure of polygonal ferrite and second phases. 4. The basic flux weldment of T-5wires showed a higher Charpy impact property than that of T-1 wires because of a higher fraction of acicular ferrite in the weld microstructure.

• 한국레이저가공학회지
• /
• 제13권4호
• /
• pp.1-6
• /
• 2010

Recently the use of ultra high strength steels (UHSS) in structural and safety component is rapidly increasing in the automotive industry. For example, 1.5GPa grade hot stamping with die-quenching of boron steel 22MnB5 could apply crash-resistant parts such as bumpers and pillars. The development of laser welding process of hot stamping steels, fundamental bead-on-plate welding and lap joint welding test were carried out using 3kW Nd:YAG laser. Local hardening & HAZ softening occurred in hot stamping steel as a result of metallurgical change caused by the welding heat input in the Nd:YAG laser welding process. The size of soft zones in the hot stamping steel was related to the welding heat input, being smaller at high speeds which generated a smaller heat input. Also in the case of lap joint design structure, same welded characteristics were shown. The HAZ softening degree was controlled to ensure the joint strength.

• 한국생산제조학회지
• /
• 제4권4호
• /
• pp.25-32
• /
• 1995

This study is to inspect the influence of the initial residual stress on fatigue crack growth behavior after the distribution of the initial residual stress is measured when the crack is growing from the compressive residual stress field. Also, the tensile residual stress field. Also, the influence of the variation of residual stress distribution on fatigue crack growth behavior at the crack tip is studied when the initial crack occurs on weld metal, bead interface and HAZ (Heat Affected Zone), respectively. For this purpose, CT-type specimen that crack parallel to the welding bead were manufactured by butt welding on the Al. Alloy 1100-O plate.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.84-86
• /
• 2003

The laser welding and its analysis of thin-sheet carbon steels were carried out with high power CO$_2$1aser. Bead on plate welding of thin sheet was examined to investigate the effect of weld variables of laser welding, and to obtain optimum welding condition. Butt-welding was also carried out to show the effect of gap on the laser weldability of thin sheet. At high welding speed, the partial penetration was obtained by low heat input. Otherwise, porosity was formed in the bead at low weld speed because of too many heat input. The maximum gap tolerance on laser welding was observed to be about 0.2mm. This gap size has good relationship with beam size of laser spot(about 0.3mm). The formability of welded sheet was about 80% value of base metal and the gap size has not affected on the formability, although weld quality is dependent on the gap size.

• Journal of Welding and Joining
• /
• 제5권1호
• /
• pp.57-63
• /
• 1987

A method which can be used for evaluating slag detachability is proposed in this study. The proposed method was intended to get an absolute value for slag detachability, to give consistent value for a given welded joint, and finally to be simple to test. With a test fig made in this study, an impact by dropping a steel ball (13Kg in weight) is applied on the back side of an as-welded plate having a slag layer on the weld bead. Such impact applied forces the slag to drop off from the bead surface. In order to make a quantitative evaluation the amount of slag removed was measured with increasing the number of drops. Using this method six kinds of fluxes were evaluated in terms of the effects of flux type, basicity and weding variables on the slag detachability. As an initial result of this test, it was found that welding heat input affects the detachability significantly. Most importantly the evaluation made using the presently proposed method gives the same order of ranking as that of the actual practice done by a welder.

• Journal of Advanced Marine Engineering and Technology
• /
• 제25권5호
• /
• pp.1122-1129
• /
• 2001

Underwater wet arc welding process was experimentally investigated by using the six types of flux coated electrodes of 3.2 mm diameter and the KR-RA steel plate of 11 mm thickness as base metal. Two types of electrodes were domestic covered arc welding electrode(CR13, CR14) and another two types of wet welding electrodes(UWCS, TN20)were imported goods, and the other two type (UWX1, UWX2) were individually designed flux coated electrodes for experimental welding purpose. Main experimental results are summerized as follows: 1. It is ascertained that individually designed flux coated electrode(UWX1) could be used in practice with KR-RA steel plate for underwater wet arc bead welds. 2. Welding arc can be generated easily and considerably kept in stable using TN20 and UWX1 electrodes. 3. The micro Vickers hardness value and the portion of martensite in the HAZ were increased in all the electrodes by rapid cooling rate, but it is relatively maintain stable for UWCS, TN20 and UWX1 electrodes.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2006년 창립20주년기념 정기학술대회 및 국제워크샵
• /
• pp.201-204
• /
• 2006

A three-dimensional finite element (FEM) model has been developed to simulate the deformation due to bead on plate welding of curved plates with curvature in the weld direction. By using traditional method such as thermal-elastic-plastic FEM, the weld-induced deformation can be predicted accurately. However, this method is not practical approach to analyze the deformation of large and complex structures such as ship hull structures in view of time and cost. This study is classified from the aspect of equivalent load based on inherent strain near the weld line. Therefore, the residual deformation can be simply computed by elastic analysis. Further more, a practical solution is proposed to consider the contact between the plate and the positioning jig by judging the reaction forces of the jig at calculation step and the effect of the longitudinal curvature is closely considered.

• 한국레이저가공학회지
• /
• 제4권2호
• /
• pp.1-12
• /
• 2001

This study has been performed to evaluate basic characteristics of CW-CO$_2$ laser welding process of A5083 and A7N01 Al alloy. The effect of welding parameters, such as shielding gas, gas flow rate, laser power and welding speed on the bead shape and porosity from bead on plate welding tests have been investigated. Welds shielded by He gas had deeper penetration and better bead shape than those shielded by Ar. The penetration depth was augmented with the increase of laser Power and the decrease of welding speed. Welds of A7N01 alloy had deeper penetration than those of A5083 alloy In beads of A5083 alloy which has deeper penetration, the volume fraction of porosities was high due to the number of its was few, but size of its was larger. The case of deeper penetration beads of A7N01 alloy, the porosity reduced under relatively higher power The Volume fraction of porosities in weld of A5083 alloy was significantly higher than that in weld of A7N01 alloy.

• Journal of Welding and Joining
• /
• 제31권6호
• /
• pp.58-64
• /
• 2013

Several joining methods involving resistance welding, laser welding, ultrasonic welding and mechanical joining are currently applied in manufacturing lithium-ion batteries. Cu and Al alloys are used for tab and bus bar materials, and laser welding characteristics for these alloys were investigated with similar and dissimilar material combinations in this study. The base materials used were Al 1050 and oxygen-free Cu 1020P alloys, and a disk laser was used with a continuous wave mode. In bead-on-plate welding of both alloys, the joint strength was higher than the strength of O tempered base material. In overlap welding, the effect of welding parameters on the tensile shear strength and bead shape was evaluated. Tensile shear strength of overlap welded joint was affected by interfacial bead width and weld defect formation. The tensile-shear specimen was fractured at the heat affected zone by selecting proper laser welding parameters.