• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2007년도 추계학술대회 논문집
• /
• pp.130-131
• /
• 2007

초고경도 박막을 얻기 위해 질화물을 이용한 CrN / CrAlN 초격자 박막을 CFUBM 시스템을 통해 합성하였다. 초격자 박막의 각층의 두께 (${\lambda}$)는 기판의 회전 속도를 이용하여 제어하여 4.4 에서 44.1 nm 까지 합성하였다. 박막의 결정구조 및 미세구조를 분석하기 위하여 고분해능 X선 회절 분석기 (HR-XRD)를 이용하였으며, 박막의 기계적 성질은 나노 인덴터와 ball on disk tester를 통해 분석하였다. CrN / CrAlN 초격자 박막은 각층의 두께 (${\lambda}$)에 따라 28.77 GPa에서 31.97 GPa의 경도 값을 나타내었으며, 미세구조와 기계적 특성이 변화를 관찰할 수 있었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.356-356
• /
• 2010

Tribological behaviors of the hard film on soft substrate system were explored using the hard thin film of diamond-like carbon (DLC) coated the soft polymer of polydimethysiloxane (PDMS). A DLC film with the Young's modulus of 100 GPa was coated on PDMS substrate with Young's modulus of 10 MPa using plasma enhanced chemical vapor deposition (PECVD) technique. The deposition time was varied from 10 sec to 10 min, resulting in nanoscale roughness of wrinkle patterns with the thickness of 20 nm to 510 nm, respectively, at a bias voltage of $400\;V_b$, working pressure 10 mTorr. Nanoscale wrinkle patterns with 20-100 nm in width and 10-30 nm height were formed on DLC coating due to the residual stress in compression and difference in Young's modulus. Nanoscale roughness effect on tribological behaviors was observed by performing a tribo-experiment using the ball-on-disk type tribometer with a steel ball of 6 mm in diameter at the sliding speed of 220 rpm, normal load of 1N and 25% humidity at ambient temperature of $25^{\circ}C$. Friction force were measured with respect to thickness change of coated DLC thin film on PDMS. It was found that with increases the thickness of DLC coating on PDMS, the coefficient of friction decreased by comparison to that of the uncoated PDMS. The wear tracks before and after tribo-test were analyzed using SEM and AFM.

• 공업화학
• /
• 제29권5호
• /
• pp.533-540
• /
• 2018

그래핀은 표면 에너지가 낮고 원자단위의 얇은 물질로서 다양한 소재의 표면에 코팅시키거나 윤활제에 분산시켜 접착력과 마찰을 줄여주는 우수한 윤활유 첨가제로 보고되고 있다. 본 연구에서는 산화 그래핀 나노시트를 세 가지 종류의 염화알킬(butyl chloride, octyl chloride 및 tetradecyl chloride)을 이용하여 액체 윤활제 첨가제용 기능화 산화 그래핀(alkyl functionalized GO, FGO)을 제조하였다. 제조한 기능화 산화 그래핀의 화학적 및 구조적 특성은 Fourier transform infrared (FT-IR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscope (SEM), and transmission electron microscope (TEM)으로 분석하였다. 제조한 기능화 산화 그래핀은 PAO-0W40 오일에 0.02 wt%의 농도로 분산시켰으며, 트라이볼로지적 특성을 high frequency friction/wear tester로 분석한 결과, FGO-14이 첨가된 PAO-0W40 오일은 ball-on-disk의 직선왕복운동 하에서 기유에 비해 ~5.88%의 마찰계수와 ~3.8%의 마모 트랙 폭을 감소시킴으로써 내마모성이 향상됨을 확인하였다. 본 연구에서는 산화 그래핀의 성공적인 기능화와 더불어 다양한 탄화수소사슬 길이에 따른 분산 안정성 및 트라이볼로지적 특성의 향상을 입증하였다.

• Tribology and Lubricants
• /
• 제36권1호
• /
• pp.47-54
• /
• 2020

In this study, the effects of ultrasonic nanocrystal surface modification (UNSM) treatment at room and high temperatures (RT and HT of 400℃) on friction and wear behavior of Ti-6Al-4V alloy prepared by selective laser melting (SLM) were investigated. The objective of this study is to improve the mechanical properties and frictional behavior of Ti-6Al-4V alloy by UNSM treatment. Dry friction and wear tests were conducted using a ball-on-disk method at RT with a bearing steel as the counter ball. Due to the high HT and UNSM treatment, the surface hardness tended to increase and surface roughness tended to reduce. X-ray diffraction (XRD) analysis showed that nanocrystallization structure and compressive residual stress were formed at the surface layer after UNSM treatment at both RT and HT. After UNSM treatment, it was observed that the wear rate was reduced by about 6% for the specimen treated at RT and a 28% reduction for the specimen treated at HT in comparison with the untreated one. Based on scanning electron microscope (SEM) images showed that the damage caused by fatigue wear occurred in the wear track of the heat-treated specimen, and it is believed to be the cause of the highest wear rate. Mechanical properties and wear resistance of Ti-6Al-4V alloy were improved and prospect of industrial application was confirmed. Further research is still required to improve the characteristics of SLM Ti-6Al-4V alloy to the level of wrought Ti-6Al-4V alloy.

• 소성∙가공
• /
• 제23권6호
• /
• pp.345-350
• /
• 2014

The current study elucidates the effects of cementite spheroidization and pro-eutectoid ferrite on the sliding wear resistance in medium carbon (0.45wt%C) and high carbon (1wt%C) steels. Both steels were initially heat treated to obtain a fully pearlite or ferrite + pearlite microstructure. Spheroidizing heat treatments were performed on both steels to spheroidize the pearlitic cementite. Sliding wear tests were conducted using a pin-on-disk wear tester with the steel specimens as the disk and an alumina ($Al_2O_3$) ball as the pin. The sliding wear tests were carried out at room temperature in air with humidity of $40{\pm}2%$. Adapted sliding distance and applied load was 300m and 100N, respectively. Sliding speed was 0.1m/s and the wear-track radius was 9 mm. Worn surfaces and cross-sections of the wear track were examined using an SEM. Micro Vickers hardness of the wear-track subsurface was measured as a function of depth from the worn surface. Hardness and sliding-wear resistance of both steel decreased with increased spheroidization of the cementite. The decrease was more significant in the fully pearlitic steel (1wt%C steel). The steel with the pro-eutectoid ferrite showed relatively higher wear resistance compared to the spheroidized pearlitic steel.

• 한국표면공학회지
• /
• 제54권5호
• /
• pp.267-277
• /
• 2021

Nitriding layers developed during gaseous nitriding of AISI4115 steels for the application of steel bushing part were investigated. The compound layer thickness of about 10㎛, 0.3mm of case depth under the same conditions, and conventional nitriding, nitrocarburizing, and controlled nitriding were performed in three methods. In the controlled nitriding, K_N was controlled by measuring the hydrogen partial pressure. The nitrided samples were analyzed by micro Vickers hardness test, optical microscopy and scanning electron microscopy. The phases of compound layer were identified by X-ray diffraction and electron backscatter diffraction. The controlled nitriding specimen indicated the highest surface hardness of about 860 HV_0.1. The compound layer of the conventional nitriding and nitrocarburizing specimen was formed with about 46% porous layer and 𝜺 + 𝜸' phase, and about 13% porous layer and about 80% 𝜸' phase were formed on the controlled nitriding specimen. As a result of the Ball-on-disk wear test, the worn mass loss of ball performed on the surface of the controlled nitriding specimen was the largest. The controlled nitriding specimen had the highest surface hardness due to the lowest porous percentage of compound layer, which improved the wear resistance.

• 한국표면공학회지
• /
• 제47권5호
• /
• pp.263-268
• /
• 2014

Nanocrystalline diamond(NCD) coated SiC balls were applied in a ball-on-disk tribometer. After seeding in an ultrasonic bath containing nanometer diamond powders, $2.2{\mu}m$ thick NCD films were deposited on sintered 3 mm diameter SiC balls at $600^{\circ}C$ in a 2.45 GHz microwave plasma CVD system. Bare $ZrO_2$ and SiC balls were prepared for comparison as test balls. Tribology tests were performed in air with pairs of three different balls and mirror polished steel(SKH51) disk. The wear tracks on balls and disks were examined by optical microscope and alpha step profiler. Under the load of 3 N, the friction coefficients of steel against $ZrO_2$, SiC and NCD-coated balls were between 0.4 and 0.8. After a few thousands sliding laps, the friction coefficient of NCD-coated balls dropped from 0.45 to below 0.1 and maintained thereafter. Under a higher load of 10 N or 20 N with a long sliding distance of 2 km, $ZrO_2$ and SiC balls exhibited the similar friction coefficients as above. The friction coefficient of NCD-coated balls was less than 0.1 from the beginning and increased to above 0.1 steadily or with some fluctuations as sliding distance increased. NCD coating layers were found worn out after long duration and/or high load sliding test, which resulted in the friction coefficient higher than 0.1.

• Tribology and Lubricants
• /
• 제35권6호
• /
• pp.356-361
• /
• 2019

The friction and wear between machine components directly influence the energy loss and failure in various machines. Therefore, there is always a demand for finding methods to reduce friction and wear. Of the possible methods, lubrication is a widely used method for reducing friction and wear. In the case of lubrication, it is important to analyze the tribological behavior in the boundary lubrication because most of friction and wear occurs in the boundary lubrication regime. Cast iron has been regarded as a good material for industrial applications due to the excellent mechanical properties and high productivity. Especially, nodular cast iron is a material that shows better mechanical properties and wear-resistance compared with cast iron due to inclusion of spheroidal graphite. In this work, we investigated the tribological characteristics of nodular cast iron with respect to different counter parts in boundary lubrication regime. Sliding tests were conducted with SUJ2, ZrO₂, Si₃N₄ balls as counter parts using a pin-on-disk type tribotester. The results showed different friction and wear behaviors with different counter parts. The case of ZrO₂ showed the lowest wear rate in specimen and no significant ball wear. In case of SUJ2, it showed similar wear rate with ZrO₂ case in specimen and the highest friction coefficient. The case of Si₃N₄ showed the lowest friction coefficient, 33% lower than the case of SUJ2. It showed 16.9 times larger wear rate in specimen and 43% larger wear rate in ball compared to that of the SUJ2 case.

• 한국세라믹학회지
• /
• 제52권6호
• /
• pp.429-434
• /
• 2015

This study investigates the macroscopic wear behaviors of C/C and C/C-SiC composites coated with hafnium carbide (HfC). To improve the wear resistance of C/C composites, low-pressure chemical vapor deposition (LPCVD) was used to obtain HfC coating. The CVD coatings were deposited at various deposition temperatures of 1300, 1400, and $1500^{\circ}C$. The effect of the substrate material (the C/C substrate, the C/C-CVR substrate, or the C/C-SiC substrate deposited by LSI) was also studied to improve the wear resistance. The experiment used the ball-on-disk method, with a tungsten carbide (WC) ball utilized as an indenter to evaluate the wear behavior. The HfC coatings were found to effectively improve the wear resistance of C/C and C/C-SiC composites, compared with the case of a non-coated C/C composite. The former showed lower friction coefficients and almost no wear loss during the wear test because of the presence of hard coatings. The wear scar width was relatively narrower for the C/C and C/C-SiC composites with hafnium coatings. Wear behavior was found to critically depend on the deposition temperature and the material. Thus, the HfC-coated C/C-SiC composites fabricated at deposition temperatures of $1500^{\circ}C$ showed the best wear resistance, a lower friction coefficient, and almost no loss during the wear test.

• Tribology and Lubricants
• /
• 제30권2호
• /
• pp.108-115
• /
• 2014

The friction behaviors of bulk amorphous thermal spray coating (BAC) and second phase-reinforced composite coatings using a high velocity oxy-fuel spraying process were investigated using a ball-on-disk test rig that slides against a ceramic ball in an atmospheric environment. The surface temperatures were measured using an infrared thermometer installed 50 mm from the contact surface. The crystallinities of the coating layers were determined using X-ray diffraction. The morphologies of the coating layers and worn surfaces were observed using a scanning electron microscope and energy-dispersive spectroscopy. The results show that the friction behavior of the monolithic amorphous coating was sensitive to the testing conditions. Under lower than normal loads, a low and stable friction coefficient of about 0.1 was observed, whereas under a higher relative load, a high and unstable friction coefficient of greater than 0.3 was obtained with an instant temperature increase. For the composite coatings, a sudden increase in friction coefficient did not occur, i.e., the transition region did not exist and during the friction test, a gradual increase occurred only after a significant delay. The BAC morphology observations indicate that viscous plastic flow was generated with low loads, but severe surface damage (i.e., tearing) occurred at high loads. For composite coatings, a relatively smooth surface was observed on the worn surface for all applied loads.