• 열처리공학회지
• /
• 제6권2호
• /
• pp.49-58
• /
• 1993

Isothermal transformation behavior during patenting and variations of microstructure and tensile strength of patented wires were investigated in Si-added high carbon steel. The TTT curves of the steels were made for two different austenitizing temperature. As the salt bath temperature was increased, the observed microstructures were bainite at $450^{\circ}C$, the mixture of bainite and pearlite at $500^{\circ}C$, and to pearlite at $600^{\circ}C$, The tensile strength of patented wire exhibited the highest value when the structure was pearlite. while the bainitic structure showed the lowest.

• 소성∙가공
• /
• 제27권5호
• /
• pp.296-300
• /
• 2018

T-type and H-type section steels were generally used in shipbuilding and offshore plants and were produced by welding technology. These section steels were produced by handwork, and the supplying amounts can't satisfy the demand amounts of the fabrication companies. In case of fillet welding, there are some gaps in weld-joint region due to no groove preparation processing and it can occur crack initiation in the welded region. It is important to evaluate the microstructural and mechanical properties of welded zone to solve these problems. To satisfy the demand amounts of T-bar parts, automatic welding technology was introduced and several conditions as a function of welding speeds were carried out to improve the manufacturing speed. Heat-affected zone may be affected by variation of heat input and cooling rate through automatic welding speed and welding speed is necessary to be optimized. In this study, fusion zone and heat-affected zone were investigated by microstructural and mechanical analysis and were evaluated whether the welded parts were sound or not.

• 열처리공학회지
• /
• 제12권3호
• /
• pp.231-239
• /
• 1999

Volume fraction and morphology of retained austenite, tensile properties of TRIP type high strength steel sheet with Fe-C-Si-Mn-Cu chemical composition have been investigated. The retained austenite of granular, bar and film type existing in specimen was obtained after intercritical annealing and austempering. The granular type retained austenite increased with increase of intercritical annealing and austempering temperature. With increase of intercritical annealing temperature, retained austenite and carbon contents increased. Maximum contents of retained austenite was obtained by austempering at $400^{\circ}C$. The maximum tensile strength was obtained by austempering at $450^{\circ}C$ and maximum elongation was obtained at $400^{\circ}C$. T.S${\times}$E.L value increased with increase of retained austenite contents due to the elongation strongly controlled by contents of retained austenite, but tensile strength was affected with various factors such as bainitic structure etc.

• 한국주조공학회지
• /
• 제32권2호
• /
• pp.104-108
• /
• 2012

The effect of heat treatment on mechanical properties of 0.4C-2.3Si(wt%) steel with bainitic ferrite matrix were investigated. This steel has been synthesized intergrating concepts from TRIP(Transformation Induced Plasticity) steel & Austempered Ductile Cast Iron(ADI) technology. The low alloy medium carbon (0.4 %C) steel with high silicon (2.3 %Si) was initially annealed for 60 min at $800^{\circ}C$, $820^{\circ}C$ and $840^{\circ}C$ respectively in the intercritical region and then subsequently austempered at various temperatures at $260^{\circ}C$, $320^{\circ}C$ and $380^{\circ}C$ for 30 min in a salt bath. The mechanical properties were measured by using a tensile test. A detailed study of the microstructure of this steel after heat treatment was carried out by means of electron back scattering diffraction (EBSD) technic. In this study, a new low alloy steel with high strength (780~1,050MPa) and exceptionally high ductility (20~40%) was obtained.