• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 반도체재료
• /
• pp.42-45
• /
• 2001

The high permittivity are applied to DRAM and FRAM. (Ba,Sr)$TiO_3$ (EST) thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on $Pt/SiO_2/Si$ substrate at 4000 [rpm] for 10 seconds in a time coating. Coated specimens were dried at $90[^{\circ}C]$ for 5 minutes. Coating process was repeated from 3 times to 5 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about 2600-2800[$\AA$] in 3 times. Dielectric constant of thin films was little decreased at 1[KHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current was stable When the applied voltage was 0~3[V] Leakage current was $10^{9}\sim10^{11}$[A] at 0~3[V].

• 한국진공학회지
• /
• 제11권1호
• /
• pp.1-7
• /
• 2002

RF Magnetron Sputtering 방법으로 $Ba_{0.5}Sr_{0.5}TiO_3$ 박막을 Pt/Ti/$SiO_2$/Si 기판위에 증착하였다. $Ba_{0.5}Sr_{0.5}TiO_3$ 박막 증착시 기판온도는 실온으로 고정시켜주었고, 작업 가스 유량(Ar:$O_2$)과 RF Power는 각각 90:10에서 60:40까지 그리고 50 W와 75 W로 하였다. 또한 박막 증착 후 RTA(Rapid Thermal Annealing)를 이용하여 산소분위기에서 $600^{\circ}C$로 고온 순간 열처리를 하였다. 커패시터 제작을 위해 UHV System의 E-beam evaporator를 이용하여 Pt를 증착하였다. XRD 측정을 통한 구조적 특성에서는 작업 가스 유량과 RF Power에 비해 고온 순간 열처리가 결정화에 기여도가 큼을 확인할 수 있었다. 전기적 특성에서는 RF Power가 50 W이고 열처리를 한 샘플에서 비교적 우수한 특성을 보여주었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.455-458
• /
• 2001

The thin films of high pemitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)$TiO_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/$SiO_2/Si$ substrate at 4,000 [rpm] for 10 seconds. The devices of BST thin films to composite $(Ba_{0.7},Sr_{0.3})TiO_3$ were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_2/Si$ substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$, $3800[\AA]$. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency l[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.455-458
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/SiO$_2$/Si substrate at 4,700 [rpm] for 10 seconds. The devices of BST thin films to composite (Ba$\_$0.7/Sr$\_$0.3/)TiO$_3$ were fabricated by changing of the depositing layer number on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was 2500[${\AA}$], 3500[${\AA}$], 3800[${\AA}$]. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency 1[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.258-261
• /
• 2000

Highly (h00)-oriented (Ba, Sr)TiO$_3$(BST) thin films were grown by pulsed laser deposition on the perovskite LaNiO$_3$(LNO) metallic oxide layer as a bottom electrode. The LNO films were deposited on SiO$_2$/Si substrates by rf-magnetron sputtering method. The crystalline phases of the BST film were characterized by x-ray $\theta$-2$\theta$, $\omega$-rocking curve and $\psi$-scan diffraction measurements. The surface microsturcture observed by scanning electron microscopy was very dense and smooth. The low-frequency dielectric responses of the BST films grown at various substrate temperatures were measured as a function of frequency in the frequency range from 0.1 Hz to 10 MHz. The BST films have the dielectric constant of 265 at 1 kHz and showed multiple dielectric relaxation at the low frequency region. The origin of these low-frequency dielectric relaxation are attributed to the ionized space charge carriers such as the oxygen vacancies and defects in BST film, the interfacial polarization in the grain boundary region and the electrode polarization. We studied also on the capacitance-voltage characteristics of BST films.

• 한국전자파학회:학술대회논문집
• /
• 한국전자파학회 2002년도 종합학술발표회 논문집 Vol.12 No.1
• /
• pp.370-374
• /
• 2002

This paper describes the design and fabrication of distributed analog phase shifter circuit. The phase shifter consist of coplanar waveguide(CPW) lines that are periodically loaded with voltage tunable (Ba,Sr)TiO$_3$ thin film interdigital(IDT) capacitors deposited by the pulsed laser deposition(PLD) on (001) MgO single crystals. The phase velocity on these IDT loaded CPW lines is a function of applied bias voltage, thus resulting in analog phase shifting circuits. The measured differential phase shift is 48$^{\circ}$ and the insertion loss decreases from -5㏈ to -3㏈ with increasing bias voltage from 0 to 40 V at 100㎐.

• 한국세라믹학회지
• /
• 제43권7호
• /
• pp.421-426
• /
• 2006

[ $(BaSr)TiO_3$ ] thick films were prepared by tape casting method, using $BaTiO_3\;and\;SrTiO_3$ powder slurry in order to investigate dielectric properties i.e. dielectric constant, ${\varepsilon}_r$, Curie temperature, $T_c$. Grain growth within $(BaSr)TiO_3$ thick films was observed with increasing weight ratio of $BaTiO_3$. This observation can be explained by phenomena of substitution of $Sr^{2+}$ ion for $Bi^{2+}$ ion in the $BaTiO_3$ system. Also, the Curie temperature in $(BaSr)TiO_3$ thick films was shifted to lower temperature range with increasing $ SrTiO_3$. Furthermore, Curie temperature having maximum dielectric constant was in the range of $-40^{\circ}C\;to\;30^{\circ}C$, and hence sharper phase transformation occurred at Curie temperature. There occurred decrease in tunability and k-factor of $(Ba_{0.6}Sr_{0.4})TiO_3$ calculated from the dielectric constant, ${\varepsilon}_r$ above Curie temperature. In addition, above the $60^{\circ}C$, phase fixation was observed. This means that internal stress relief occurred with increasing $90^{\circ}$ domains.

• 한국재료학회지
• /
• 제17권7호
• /
• pp.386-389
• /
• 2007

The dielectric properties of $(Ba_{0.5}Sr_{0.5})TiO_3$ ferroelectric thin films have been investigated according to the substrates in order to optimize the their properties. MgO, r-plane sapphire, and poly-crystalline sapphire (Alumina) substrates have been used to deposite $(Ba_{0.5}Sr_{0.5})TiO_3$ ferroelectric thin films by RF magnetron sputtering. The BST thin films deposited on the single crystal (100)MgO substrates have high tunability and low dielectric loss. These results are caused by a low misfit between the lattice parameters of the BST films and the substrate. The BST films deposited on r-plane sapphire have relatively high misfit, and the tunability of 17% and dielectric loss of 0.0007. To improve the dielectric properties of the BST films, the post-annealing methods has been introduced. The BST films deposited on (100)MgO, (1102)r-plane sapphire, and poly-crystalline sapphire substrates have best properties in post-annealing conditions of $1050^{\circ}C$, $1100^{\circ}C$, and $1150^{\circ}C$, respectively. The different optimal post-annealing conditions have been found according to the different misfits between the films and substrates, and thermal expansion coefficients. Moreover, the films deposited on alumina substrate which is relatively cheap have a good tunability properties of 23% by the post-annealing.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1998년도 추계학술대회 논문집 학회본부 C
• /
• pp.798-800
• /
• 1998

(Ba,Sr)$TiO_3$ thin films were etched with $Cl_2$/Ar gas mixing ratio in an inductively coupled plasma (ICP) by varying the etching parameter such as f power, do bias voltage, and chamber pressure. The etch rate was $560{\AA}/min$ under Cl_2/(Cl_2+Ar)$ gas mixing ratio of 0.2, rf power of 600 W, do bias voltage of 250 V, and chamber pressure of 5 mTorr, At this time, the selectivity of BST to Pt, $SiO_2$ was respectively 0.52, 0.43. The surface reaction of the etched (Ba,Sr)$TiO_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.196-196
• /
• 2008

We have investigated that the effect of post annealing on the structural and electrical properties of $Ba_{0.5}Sr_{0.5}TiO_3$ thin films. The BST thin films were deposited on n-type 4H-silicon carbide(SiC) using pulsed laser deposition (PLD). The deposition was carried out in oxygen ambient 100mTorr for 5 minutes, which results in about 300nm-thick BST films. For the BST/4H-SiC, 200nm thick silver was deposited on the BST films bye-beam evaporation. The X-ray diffraction patterns of the BST films revealed that the crystalline structure of BST thin films has been improved after post-annealing at $850^{\circ}C$ for 1 hour. The root mean square (RMS) surface roughness of the BST film measured by using a AFM was increased after post-annealing from 5.69nm to 11.49nm. The electrical properties of BST thin film were investigated by measuring the capacitance-voltage characteristics of a silver/BST/4H-SiC structure. After the post-annealing, dielectric constant of the film was increased from 159.67 to 355.33, which can be ascribed to the enhancement of the crystallinity of BST thin films.