• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.11
• /
• pp.77-82
• /
• 1990

The temperature and the composition dependence of the dielectric properties of the solid solution materials in the system $xBa(Zn_{1/3}Nb_{2/3})O_{3}\[BZN]-(1-x)\Sr(Zn_{1/3}Nb{2/3)O_{3}\[SZN]$ at microwave frequency was studied. The dielectric constant and unloaded Q were $40.5{\pm}0.5,5980{\pm}100$ respectively for BZN at 10 GHz and $36.9{\pm}0.5,2700{\pm}100$ for SZN at 10.2GHz. The temperature coefficient of the resonant frequency was $+27.5ppm/{\circ}C$ for BZN and $-39.1ppm/{\circ}C$ for SZN. The results also showed that 0.3 BZN-0.7 SZN is the most temperature-stable composition among xBZN-(1-x) SZN solid solutions. In this case, the dielectric constant, the unloaded Q and $\tau_{f}$ at 9.8GHz were $41.5{\pm}0.2,2920{\pm}100$ and $-3.5ppm/{\circ}C$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1042-1045
• /
• 2001

Microwave dielectric properties of Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_3$-Sr(Zn$_{1}$3/Nb$_{2}$3/) $O_3$(BZN-SZN) system were investigated as a function of sintering temperature and Zr $O_2$content. Density was increased and the temperature coefficient of resonant frequency (TCF, $\tau$$_{f}$) decreased with increasing sintering temperature. However dielectric constant (K) and Q$\times$f value did not change markedly with the sintering temperature. For the samples sintered at the same temperature, density, dielectric constant, and Q$\times$f value were increased and TCF was decreased with increasing Zr $O_2$concentration. Especially, the dielectric constant of the sample increased with x and exhibited the maximum value ($\varepsilon$$_{r}$=41) when x=0.6 at 1575$^{\circ}C$ sintered. TCF decreased with x and exhibited the minimum value ($\tau$$_{f}$=+0.8ppm/$^{\circ}C$) when x=1.0..0.