• 전기학회논문지
• /
• 제56권9호
• /
• pp.1609-1613
• /
• 2007

(Ba,Sr,Ca)$TiO_3$ powders, which were prepared by sol-gel method using a solution of Ba-, Sr- and Ca-acetate and Ti iso-propoxide, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on high purity alumina substrates. The structural and dielectirc properties were investigated for various $Dy_2O_3$ doping contents. As a result of thermal analysis, the exothermic peak was observed at around 670^{\circ}C $ due to the formation of the polycrystalline perovskite phase. All BSCT thick films, sintered at $1420^{\circ}C$ for 2h, showed the typical XRD patterns of perovskite polycrystalline structure and no pyrochlore phase was observed. The average grain size of the specimens decreased with increasing amount of $Dy_2O_3$. The average grain size and thickness of the BSCT specimens doped with 0.1 mol% $Dy_2O_3$ were approximately $1.9{\mu}m$ and $70{\mu}m$, respectively. The relative dielectric constant decreased and dielectric loss increased with increasing amount of $Dy_2O_3$, the values of the BSCT thick films doped with 0.1 mol% $Dy_2O_3$ were 3697 and 0.4% at 1 kHz, respectively. The leakage current densities in all BSCT thick films were less than $10^{-9}A/cm^2$ at the applied electric field range of 0-20 kV/cm.

• 한국전기전자재료학회논문지
• /
• 제20권8호
• /
• pp.680-684
• /
• 2007

In this study, we investigated the effects of structural and electrical properties of $(Ba_{0.6},\;Sr_{0.3},\;Ca_{0.1})TiO_3$ thick films with variation $Dy_2O_3$ contents. $(Ba_{0.6},\;Sr_{0.3},\;Ca_{0.1})TiO_3$ powders, prepared by the sol-gel method, were mixed organic vehicle. The BSCT thick films doped with 0.1, 0.3, 0.5, 0.7 mol% $Dy_2O_3$ were fabricated by the screen-printing techniques on the alumina substrates and the structural and dielectric properties were investigated with variation of $Dy_2O_3$ doping contents. All BSCT thick films were sintered at $1420^{\circ}C$, for 2hr. In the TG-DTA analysis, the formation of the polycrystalline perovskite phase was observed at around $670 ^{\circ}C$. In the XRD analysis, all BSCT thick films showed the cubic perovskite structure. The average thickness of BSCT thick films was approximately $65{\mu}m$. The Curie temperature decreased with increasing $Dy_2O_3$ amount. The relative dielectric constant and dielectric loss of BSCT thick films doped with $Dy_2O_3$ 0.1 mol% were 6267 and 2.6 %, respectively.

• 한국전기전자재료학회논문지
• /
• 제20권7호
• /
• pp.581-586
• /
• 2007

[ $(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$ ] (BSCT) powders, prepared by sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen printing method. The structural and dielectric properties were investigated as a function of the $Yb_2O_3$ doping contents. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films showed the typical XRD patterns of a cubic polycrystalline structure. The average thickness of all BSCT thick films was about $70{\mu}m$. The grain size of the BSCT thick film doped with 0.7 mol% $Yb_2O_3$ was approximately $6.2{\mu}m$. The Curie temperature and relative dielectric constant at room temperature decreased with increasing $Yb_2O_3$ amount. Relative dielectric constant and dielectric loss of the specimen doped with 0.1 mol% $Yb_2O_3$ were 4637 and 19 % at Curie temperature, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.153-156
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$ (x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their dielectric properties were investigated with variation of composition ratio, doped ZrO$_2$ (0.5, 1.0, 1.5, 2.0, 3.0 wt%) and sintered at 145$0^{\circ}C$. The dielectric constant and loss of the x=0.10 specimen applied field were 19.86 and 0.302 % at 0 V/cm, and 25.937 and 0.339 % at 300 V/cm, respectively. Dielectric constant were increased with increased applied field and decreased with increased frequency, and dielectric loss were within 0.1% at applied 800 MHz, respectively. all specimens showed fairly good applied field. Although, dielectric constant and loss of all specimen showed to tend of nearly the same. same.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.685-688
• /
• 2003

[ $(Ba,Sr,Ca)TiO_3$ ] powders, prepared by the sol-gel method, were mixed with an organic vehicle and the BSCT thick films were fabricated by the screen printing techniques on alumina substrates. The grain size decreased with increasing amounts of $MnO_2$, and the BSCT(50/40/10) thick film doped with 1wt% $MnO_2$ showed a value of 6.5mm. The thickness of thick films by four-cycle on printing/drying was approximately 100mm. The relative dielectric constant, dielectric loss and tunability of the BSCT(S0/40/10) thick films doped with 1.0wt% $MnO_2$ were 1296, 0.61% and 11.18%, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.42-45
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$+yZrO$_2$wt% (x=1.10, 0.15, 0.20, y=0.5~3.0) specimens were fabricated by the mixed and ZrO$_2$ contents were studied. All BSCT specimens contents were studied. All BSCT specimens showed dense and homogeneous structure without the presence of the seconds phase. The Curie temperature and the dielectric constant at room temperature decreased with increasing the Ca/Ba composition ratio and ZrO$_2$ content. The BSCT(50/40/10) specimens showed the excellent tunability property. And the tunability were increased with increasing the contents of ZrO$_2$./TEX>.

• 한국전기전자재료학회논문지
• /
• 제14권6호
• /
• pp.460-465
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$(x=1.10,0.15,0.20) specimens were fabricated by the solid state reaction method and then the structural and dielectric properties as a function of he composition ratio and sintering temperature were studied. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around 102$0^{\circ}C$ due to the formation of the polycrystalline perovskite phase. The BSCT(50/40/10) specimen sintered at 150$0^{\circ}C$ showed the highest average grain size(18.25${\mu}{\textrm}{m}$). The Curie temperature and dielectric constant at room temperature decreased with increasing Ca content. The dielectric constant and dielectric loss of the BSCT(50/40/10) specimen, sintered at 145$0^{\circ}C$, were about 4324 and 0.972% at 1KHz, respectively.ively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.402-405
• /
• 2001

$(Ba_{0.6-x}Sr_{0.4}Ca_{x})TiO_{3}$ (x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their stuctural and dielectric properties were investigated with variation of composition ratio and an amount of $Al_{2}O_{3}$ (0.5, 1.0, 1.5. 2.0, 3.0 wt%) doping content. As a result of the X-ray diffraction BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with increase an $Al_{2}O_{3}$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing an amount of $Al_{2}O_{3}$ doping content. The dielectric loss is minimum for BSCT doped with 1.5wt% $Al_{2}O_{3}$ content. The tunability was decreased with increasing an Ca content and is about 4.2% for BSCT(50/40/10) doped with 2.0wt% $Al_{2}O_{3}$ content.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 춘계학술대회 논문집 유기절연재료 전자세라믹 방전플라즈마 일렉트렛트 및 응용기술
• /
• pp.79-82
• /
• 2002

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ + ywt% MgO (x=0.10, 0.15, 0.20, y=0.0~3.0) ceramics were fabricated by the conventional solid-state reaction, and their structural and dielectric properties were investigated with variation of composition ratio and MgO doping content. A second phase, representative of MgO, appears in 3wt% MgO-doped BSCT specimens. Average grain sizes decreased with increasing amounts of MgO, and the BSCT(40/40/20) specimens doped with 3wt% MgO showed a value of $9.3{\mu}m$. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing MgO doping content and Ca composition ratio. The relative dielectric constant was non-linearly decreased as the field strength is increased. The tunability was increased with decreasing a Ca content and the BSCT(50/40/10) specimen doped with 1.0wt% MgO content showed the highest value of 6.4% at 5kV/cm.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권11호
• /
• pp.550-554
• /
• 2001

$(Ba_{0.6}Sr_{0.4}Ca_x)TiO_3 + yAl_2O_3$ wt% (x=0.10, 0.15, 0.20, y=0~3.0) ceramics were fabricated by the mixed-oxide method, and their structural and dielectric properties were investigated with variation of composition ratio and $Al_2O_3$ doping content. As results of the X-ray diffraction and microstructure analysis, all BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with an increase of $Al_2O_3$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing $Al_2O_3$doping content. The dielectric loss is minimum at BSCT doped with 1.5wt% $Al_2O_3$content. The tunability was decreased with increasing an Ca content and the BSCT(50/40/10) specimen doped with 2.0wt% $Al_2O_3$content showed the maximum value of 4.2%.