• 한국가스학회지
• /
• 제6권1호
• /
• pp.32-37
• /
• 2002

천연가스는 청정 무공해 에너지라는 장점으로 소비량이 매년 크게 증가하고 있는 주요 에너지원이다 천연가스 수요의 증가에 따른 LNG 저장 시설의 확충이 요구되고 있어, 한국가스공사에서는 LNG 저장탱크 설계 기술을 개발하고 있다. 본 논문에서는 유한요소법을 이용하여 LNG 저장탱크의 Roof를 설계에 대하여 연구하였으며, 설계 및 평가에 적용된 하중 조건과 안전 코드는 BS7777 코드에 따라 연구하였다.

• 한국주조공학회지
• /
• 제38권6호
• /
• pp.121-131
• /
• 2018

The effect of additives on the castability of the AC2BS aluminum alloy, which contains 35% recycled scrap, was investigated. For the wide utilization of the recycled scrap AC2BS aluminum alloy, the research results were compared to those with the AC2B virgin alloy, which is typical Al-Si-Cu alloy system. It was confirmed that the addition of Al-5%Ti-1%B increased the ${\alpha}$-Al nucleation temperature during solidification and decreased the grain size through cooling curve and microstructural observations of the recycled alloy. It was also found that an addition of Al-10%Sr decreased the eutectic Si growth temperature during the solidification process and modified the shape of the eutectic Si of the recycled alloy. The characteristics of fluidity, shrinkage and solidification crack strength were evaluated. For the AC2BS aluminum alloy containing 35% recycled scrap, both ${\alpha}$-Al grain refinement due to Ti-B and eutectic Si modifications due to Sr contributed to the improvement of the fluidity. The macro- shrinkage ratio increased with additions of both Al-10%Sr and Al-5%Ti-1%B and the micro-shrinkage ratio increased with the addition of Al-10%Sr but decreased with the addition of Al-5%Ti-1%B. The casting characteristics of TiB and Sr-treated AC2BS aluminum alloy containing 35% recycled scrap are similar to those of AC2B virgin alloy. The improvement of the solidification crack strength of the AC2BS aluminum alloy was possible by the reduction of the grain boundary the stress concentration through the enhancement by both ${\bullet}{\cdot}$-Al refinement and eutectic Si modification. More extensive use of the AC2BS aluminum alloy containing 35% recycled scrap can be expected in the future.

• 한국가스학회지
• /
• 제5권4호
• /
• pp.85-91
• /
• 2001

내부탱크의 파손에 따른 외부탱크의 누설 안전성을 검토하기 위해서 PC 구조물의 누설 저지효과에 대해 고찰하고자 한다. 이러한 누설 안전성 해석은 완전 방호식의 PC 구조물로 제작된 외부탱크가 내부탱크로부터 유입된 $-162^{\circ}C$의 초저온 액체에 의해 파손될 것이라는 가정을 하고, BS 7777에서 규정한 잔류압축구간의 개념을 도입하여 누설 안전성을 예측하였다. 계산된 결과에 의하면 PC 구조물로 제작된 외부탱크가 $10\%$ 잔류압축구간이 설치될 경우 $-162^{\circ}C$ 초저온 액체에 의해 누설된 총시간은 215시간(약 9일) 걸리는 것으로 해석되었고, 내부탱크에 설치된 주펌프 3대($330m^3/hr$ 송출용량)를 가동하면 $140,000m^3$ 규모의 LNG를 이웃 저장탱크에 이송하는데는 6일정도 걸리기 때문에 최소한 수치적으로는 안전하다는 결과이다.

• 한국주조공학회지
• /
• 제36권2호
• /
• pp.67-74
• /
• 2016

The effects of scrap content on the hot tearing property and tensile property were investigated in AC2BS alloy. The hot tearing strengths were $16.4kgf/cm^2$, $15.2kgf/cm^2$, $14.9kgf/cm^2$ and $13.3kgf/cm^2$, respectively, under the constant solid fraction of 29.3% when the scrap contents of the specimens were 0%, 20%, 35% and 50%. In the same way, tensile strengths of the as-cast condition were $24.5kgf/mm^2$, $23.7kgf/mm^2$, $17.3kgf/mm^2$ and $16.0kgf/mm^2$, respectively, and the corresponding tensile strengths of the T6 heat treatment condition were $27.2kgf/mm^2$, $26.7kgf/mm^2$, $24.2kgf/mm^2$ and $23.9kgf/mm^2$. Hot tearing strength and tensile strength decreased as scrap content of the specimen increased. According to the evaluation of the quantitative hot tearing and tensile test results, the decrease of these strengths is due to the presence of oxide films which act as crack initiation site of the specimens. Therefore, elimination of oxide films of aluminum melt to maintain melt cleanliness is required.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 추계학술대회논문집A
• /
• pp.448-452
• /
• 2001

Natural gas became one of the major sources of energy in Korea. As the consumption of natural gas increase, the more capacity of the LNG storage tanks is required. Recently, Korea Gas Corp.(KOGAS) has developed the technology of designing the LNG storage tanks. In this study, some of the finite element analysis has been made for designing of the roof structure of LNG storage tanks. The load case and safety code used in this study were followed by BS7777.

• 한국전산구조공학회논문집
• /
• 제30권6호
• /
• pp.485-493
• /
• 2017

본 연구에서는 LNG 저장시설의 외조를 구성하는 SCP(sandwich concrete panel)에 대한 충돌해석을 수행하고 그 거동을 분석하였다. 설계기준 중 하나인 BS7777에서 제시하는 충돌에너지와 동일한 값을 갖도록 두 종류의 충돌체와 다양한 충돌속도를 이용하여 충돌조건을 구성하고 이에 대한 비선형동적 해석모델을 구성하여 설정된 충돌조건에 대하여 수치해석을 수행하였다. 또한 1차 충돌 후에 동일한 지점에 같은 충돌에너지를 가진 2차 충돌이 일어나는 것을 가정하여 충돌거동을 분석하였다. 해석결과 동일한 충돌에너지를 갖는 충돌에서 충돌체의 크기가 작고, 충돌속도가 작을수록 큰 변형이 발생하는 것으로 나타났다. 충돌에너지는 외측강판과 내부 충진콘트리트가 6:4정도의 비율로 소산시키는 것으로 나타났다. 중복충돌해석에서는 2차 충돌체의 크기에 따라 최종충돌변형이 지배되는 것으로 나타났고 2차 충돌에 의한 변형량은 1차 충돌에 비하여 적은 값을 나타냈는데 이는 강판의 막거동 때문인 것으로 분석되었다. 이격된 중복충돌에서는 이격위치와 관계없이 2차 충돌점에서 가장 큰 변형이 발생하는 것으로 나타났다.