We have fabricated $Bi_{3.25}La_{0.75}Ti_3O_12$ (BLT) thin films on the Pt/Ti/$SiO_2$/Si substrates using a metalorganic decomposition (MOD) method with annealing temperature from $550^{\circ}C$ to $750^{\circ}C$. The structural properties of BLT films examined by x-ray diffraction (XRD). From XRD analysis. BLT thin films show polycrystalline structure. The layered-perovskite phase was obtained by spin-on films at above $600^{\circ}C$ for 1h. Scanning electron microscopy (SEM) showed uniform surface composed of rodlike grains. The grain size of BLT films increased with increasing annealing temperature. The BLT film annealed at $650^{\circ}C$ was measured to have a dielectric constant of 279, dielectric loss of 1.85(%), remanent polarization of $25.66\mu C/\textrm{cm}^2$, and coercive field of 84.75 kV/cm. The BLT thin films showed little polarization fatigue test up to $3.5{\times}10^9$ bipolar cycling at 5 V and 100 kHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.851-856
• /
• 2003

We have investigated the material and electrical properties of $Bi_{4-x}La_xTi_3O_{12}$ (BLT) ferroelectric thin film for ferroelectric nonvolatile memory applications of capacitor type and single transistor type. The 120nm thick BLT films were deposited on $Pt/Ti/SiO_2/Si$ and $SiO_2/Nitride/SiO_2$ (ONO) substrates by the sol-gel spin coating method and were annealed at $700^{\circ}C$. It was observed that the crystallographic orientation of BLT thin films were strongly affected by the excess Bi content and the intermediate rapid thermal annealing (RTA) treatment conditions regardeless of two type substrates. However, the surface microstructure and roughness of BLT films showed dependence of two different type substrates with orientation of (111) plane and amorphous phase. As increase excess Bi content, the crystallographic orientation of the BLT films varied drastically in BLT films and exhibited well-crystallized phase. Also, the conversion of crystallographic orientation at intermediate RTA temperature of above $450^{\circ}C$ started to be observed in BLT thin films with above excess 6.5% Bi content and the rms roughness of films is decreased. We found that the electrical properties of BLT films such as the P-V hysteresis loop and leakage current were effectively modulated by the crystallographic orientations change of thin films.