• 대한치과기공학회지
• /
• 제25권1호
• /
• pp.63-70
• /
• 2003

The microstructure and hardness of a porcelain fused Au-Pt-Cu-In alloy was investigated using optical microscopy, secondary electron microscopy, electron probe microanalyzer, transmission electron microscope, and vickers hardness. The hardness of the heat-treated Au-Pt-Cu-In quartenary alloy reached a maximum value in 30 min at 550$^{\circ}C$ in the range of 150 to 950$^{\circ}C$. In the aged Au-Pt-Cu-0.5In alloy at 550$^{\circ}C$, the hardness of the alloy rapidly increased until 30min with increasing aging time and after that it was remained nearly constant value. Based on above results, glazing and final aging of the porcelain fused Au-Pt-Cu-0.5In alloy were performed at 920 and 550$^{\circ}C$, respectively. The hardness of Au-Pt-Cu-0.5In alloy glazed at 920$^{\circ}C$ was 90 Hv and that of the alloy aged for 30 min at 550$^{\circ}C$ increased to 160 Hv. This indicates that a ceramic-metal crown with high strength can be manufactured using the glazing at 920$^{\circ}C$ and followed final aging at 550$^{\circ}C$ for 30 min.

• 대한의용생체공학회:의공학회지
• /
• 제24권3호
• /
• pp.203-208
• /
• 2003

인듐함량에 따른 Au-Pt-Cu 삼원계합금의 미세조직 및 기계적 특성을 광학현미경, 시차주사열분석기, SEM, XRD, EPMA 그리고 미소경도계를 이용하여 조사하였다. 인듐함량이 0.5 wt% 인 Au-Pt-Cu-0.5In 사원계 합금을 온도범위 150~95$0^{\circ}C$에서 열처리한 결과 55$0^{\circ}C$/3O분 열처리한 시료의 경도 값이 가장 높게 나타났고, 55$0^{\circ}C$에서 시효시간을 증가시킴에 따라 30분에서 최고 경도치에 도달된 후 거의 일정하게 유지되었다 또한, 55$0^{\circ}C$에서 30분 동안 시효 처리한 Au-Pt-Cu 삼원계합금의 미세조직은 인듐 함량이 증가함에 따라 결정립이 미세화 되었다. XRD, EPMA을 이용하여 Au-Pt-Cu-In 사원계 합금에 존재하는 석출상을 분석한 결과 모상은 fcc구조를 갖는 Au-Pt-Cu 고용체, 석출상은 Ll$_2$구조를 갖는InPt$_3$ 석출물로 판명되었다. 이러한 연구결과로부터 인듐 함량에 따른 Au-Pt-Cu-In 합금의 경도증가는 결정립 미세화에 의한 강화 효과와 InPt$_3$ 형태의 석출물에 의한 석출강화 효과에 기인하는 것으로 해석된다.