• 대한치과기공학회지
• /
• 제24권1호
• /
• pp.65-71
• /
• 2002

This study was performed to observe the microhardness change of the surface and the bonding strength between the porcelain and alloy specimens in order to investigate the effects of appended indium, tin and copper on interfacial properties of Au-Pd-Ag alloys. The hardness of castings was measured with a micro-Vicker's hardness tester. The interfacial shear bonding strength between alloy specimen and fused porcelain was measured with a mechanical testing system(MTS 858.20). The microhardness of Au-Pd-Ag alloy was increased by adding indium and tin, but not increased by adding copper. The shear bonding strength of Au-Pd-Ag-Sn alloy and Au-Pd-Ag-Cu alloy showed 87MPa, 57MPa. The higher concentration of adding elements showed the higher shear bonding strength.

• 대한치과기공학회지
• /
• 제21권1호
• /
• pp.27-41
• /
• 1999

치과용 Ag기 합금에서 30wt%Pd 및 10wt%Cu의 용질농도의 구성비가 3이 되는 3원 합금과 여기에 2wt% Au의 첨가에 미치는 석출상의 영향을 조사 분석하여 아래와 같은 결론을 얻었다. Ag-Pd-Cu 3원 합금은 $\alpha$ 단일상에서 Ag-rich ${\alpha}_2 $ 및 PdCu 규칙상에 의해서 경화반응이 진행되며 연속승온시효곡선에 의하면 100-$300^{\circ}C$의 저항증가와 300-$500^{\circ}C$의 저항감소라고 하는 2단계 변화에 의해서 경화곡선이 얻어졌다. 또한 본 합금의 시효과정에서는 ${\alpha}{\to}{\alpha}_2+PdCu{\to}$의 2상 분리반응에 의하여 경화원인이 되었다. 석출과정은 ${\alpha}{\to}{\alpha}_1+PdCu{\to}{\alpha}_2+PdCu$ 이고 Cu-rich인 ${\alpha}_2$상은 거의 나타나지 않으며 최고 경도값은 ${\alpha}_2$ 및 PdCu의 2상공존 구역에서 나타났다. 미량의 Au첨가에 의해서 경화는 다소 증가하지만 경화성보다는 내식성에 보다 크게 기여하였고 Pd/Cu=3인 합금은 Pd/Cu=1 또는 1.7의 합금보다도 전반적으로 경도값은 가장 낮게 나타나며 이것은 치과용 Ag기 합금의 시효경화성에는 Cu농도가 크게 기여하였다. 불연속석출물인 nodule 생성물은 입계에 우선 형성되어 $\alpha$ matrix로 진행되어 nodule 석출물은 부드러운 경계면을 가지고 $\alpha$ matrix주위에 strain matrix를 나타내므로 nodule 형성이 본 합금의 시효경화를 야기하였다. 내식성은 Pd 함량이 가장 높은 본 합금에서 매우 양호하게 나타났으며 Pd 함량이 증가가 내식성의 향상에 크게 기여하여 미량의 Au 첨가에 의해서 보다 현저히 효과를 얻었다. 본 합금의 시효열처리 조건은 $450^{\circ}C$ 적절하며 1-120min 시효시간에 걸쳐서 소정의 경도 값을 얻을 수 있고 시효경화성 및 내식성의 결과로부터 Ag-30wt%Pd-10wt%Cu합금 및 미량 Au 합금은 치과용 금속재료로 적합하였다.

• 대한치과기공학회지
• /
• 제19권1호
• /
• pp.21-35
• /
• 1997

Au 함량이 20% 미만인 Au-Ag-Pd합금의 기초합금인 Ag-Pd-Cu 3원계 합금의 시효경화 특성을 규명할 목적으로 20wt% Pd 및 20wt% Cu의 용질농도구성비가 1이 되는 3원 합금과 여기에 2wt% Au의 첨가합금에 미치는 석출상의 영향을 분석, 조사하여 아래와 같은 결론을 얻었다. Ag-20wt% Pd-20wt% Cu 3원 함금은 ${\alpha}$의 단일상에서 Ag-rich의 ${\alpha}2$상 및 PdCu규칙상에 의하여 경화반응이 진행되며 연속승온과정에서 $100{\sim}300^{\circ}C$의 경도증가와 $300{\sim}500^{\circ}C$의 경도감소의 2단계 경화특성이 얻어졌다. 연속승온시효과정은 Au첨가에 관계없이 2단계의 석출반응이 저온영역에서는 stage I, stage II로 나타나고 stage I은 고온에서의 소입에 의해 도입된 과잉공공의 이동 및 소멸에 의한 반응이고 stage II는 평형농도의 공공확산에 의한 반응에 대응하였다. 또한 본 합금의 시효석출과정은 ${\alpha}\to{\alpha}+{\alpha}2+PdCu\to{\alpha}_1+{\alpha}_2+PdCu$이고 최대 경화는 ${\alpha}_1,\;{\alpha}_2$, PdCu의 3상공존구역에서 나타났다. 이들 석출반응은 입계반응이고 반응의 진행과 함께 경도값은 상승하며 경화능에 직접적으로 기여하였다. 또한 석출상은 미세한 lamella조직의 nodule을 나타내고 이들 ${\alpha}_1,\;{\alpha}_2$ 및 PdCu상과의 미세한 혼합상의 형성이 시효경화능에 기여하는 주된 원인이 되었다. 과시효는 lamella의 조대화와 PdCu상의 ${\alpha}_2$상으로의 용해에 따른 정량적 감소에 대응하였다. 본 합금의 시효열처리 온도는 $450^{\circ}C$가 적절하며 $1{\sim}120min$ 시효시간에 걸쳐서 소정의 경화특성을 얻을 수 있었다.

• 대한치과기공학회지
• /
• 제20권1호
• /
• pp.37-49
• /
• 1998

실용치과재료로 사용되고 있는 Ag-Pd-Cu 3 원계 합금의 시효석출과정을 Pd 및 Cu의 용질 농도의 조성비가 약 1.7인 합금과 이 합금에서 2wt%Au의 첨가합금에 미치는 영향을 조사 분석하여 아래와 같은 결론을 얻었다. Ag-25Pd-15Cu 3원 합금은 ${\alpha}$의 단일상에서 ${\alpha}_1$ (Cu-rich), ${\alpha}_2$(Ag-rich) 및 PdCu 규칙상에 의해서 경화반응이 진행되며 연속승온시효에 의하면 $100{\sim}300^{\circ}C$의 저항증가와 $300{\sim}500^{\circ}C$의 저항감소라고 하는 2단계 변화에 의해서 경화곡선이 얻어졌다. 또한 본 합금의 시효과정은 ${\alpha}{\to}{\alpha}+{\alpha}_2+PdCu{\to}{\alpha}_1+{\alpha}_2+PdCu$이고 2상분리 반응에 경화되며 최고경화는 ${\alpha}_1,\;{\alpha}_2$ 및 PdCu 규칙상의 혼합영역에서 나타났다. 이들 석출반응은 입계반응이고 반응의 진행과 함께 경도값은 상승하고 경화촉진에 기여하였다. 또한 Nodule은 미세한 lamella조직을 나타내고 이들 ${\alpha}_2$와 PdCu상과의 미세한 혼합상의형성이 시효경화에 기여하는 주된 원인이 되었다. 과시효는 lamella의 조대화와 PdCu상의 ${\alpha}2$상으로의 용해에 따른 정량적 감소에 대응하였다. 석출상은 thin lamella구조의 잘 방위된 미세한 판상석출물로서 이들 미세 판상석출물은 AuCu($L1_0$)type의 face-centered tetragonal(fct)의 초격자구조였다. 규칙화된 미세한 판상석출물은 stair-step mode로서 twinning에 의해 형성되며 이것은 시효에 의해 $L1_0$ type의 PdCu 규칙상과 같은 초격자 형성시 정방비틀림 때문이라고 생각된다. 이들 twinning lamella는 귀금속원소에 의해 형성된 $L1_0$ type의 PdCu 규칙상과 같기 때문에 이들 합금의 부식저항에도 기여하였다. Ag-25Pd-15Cu합금은 전반적으로 양호한 내식성을 나타내며 Pd.Cu=1인 합금에서보다도 Pd함량이 높은 Pd/Cu=1.7에서 내식성이 보다 우수한 것은 Pd 함량이 내식성에 기여하였고 2%Au의 첨가에 의해서 부식성을 개선할 수 있었다.

• 대한의용생체공학회:의공학회지
• /
• 제15권4호
• /
• pp.389-394
• /
• 1994

The age-hardening behavior and the structural changes in a commercial dental Au-Ag-Cu-Pd alloy were investigated by means of hardness test, optical and scanning electron microscopic observation, energy dispersive spectroscopy and X-ray diffraction study. The drastic reduction in hardness by prolonged aging occurred after a rapid increase in hardness at the initial stage by the isothermal aging at $350^{\circ}C$. This softening was due to the broad precipitates formation of the lamellar structure which was composed of the f.c.t. AuCu I ordered f.c.t. phase containing Pd and the f.c.c. Ag-rich $\alpha$1 solid solution f.c.c.phase containing Au.

• 대한의용생체공학회:의공학회지
• /
• 제17권2호
• /
• pp.247-254
• /
• 1996

The relationship between the isothermal age-hardening behavior and the phase transformation in the commercial dental Au-Ag-Cu-Pd alloy was investigated Age-hardening was mostly attributed to the lattice distortions of the supersaturated w phase resulting from the transformation to the metastable phasel which were more distinct at lower aging temperature. The lattice distortions resulting from the transformation of the metastable phases to the equilibrium phases also made a contribution to the age-hardening.

• 대한치과보철학회지
• /
• 제27권1호
• /
• pp.123-141
• /
• 1989

The purpose of this study was to investigate the tendency of color change of ceramic, and its mechanism un der the influence of Pd-Ag alloy. The specimens were made by firing porcelain on tile metal plates cast with Au-Pt alloy, Pd-Cu alloy and Pd-Ag alloy. In the case of Pd-Ag alloy, specimens were fired under three different conditions as follows, 1) without protection, 2) protection with ceramic metal conditioner, 3) protection with carbon block. For the specimens of element analysis, a barrier was constructed with platinum foil between metal plate and ceramic. Color change was measured with colorimeter and elemental changes in ceramic were calculated with DC argon plasma emission spectrophotometer. The results were as follows : 1. Color change of ceramic by Pd-Ag alloy was negligible in hue, but decreased in value and increased in chroma (yellow discoloration). 2. Color change of ceramic by Pd-Ag alloy was appeared through vapor transport mechanism. 3. As the protection method for the color change of ceramic by Pd-Ag alloy, application of ceramic metal conditioner was superior to utilization of carbon block.

• 대한치과보철학회지
• /
• 제27권1호
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.

• Corrosion Science and Technology
• /
• 제4권1호
• /
• pp.19-22
• /
• 2005

Two Au-Ag-Cu-Pd dental casting alloys (Au:12% and 20%) used. The test solutions used 0.9 % NaCl solution (isotonic sodium chloride solution), 0.9 % NaCl solution containing 1 % lactic acid, and 0.9 % NaCl solution containing 1 % lactic acid and 0.1 mol $dm^{-3}$ $Na_2S$. The surface of two samples in three sample solutions was not natural discoloration during one year. The alloy containing 12 % gold was easily alloyed and the composition was uniform comparing with the alloy containing 20 % gold. The rest potentials have not a little effect after three months. The kinds of metals could not definitely from the oxidation and reduction waves of metal on the cyclic voltammograms. The dissolutions of gold and palladium were 12 % Au sample in the 0.9 % NaCl solution containing 1 % lactic acid and 0.1 mol $dm^{-3}$ $Na_{2}S$. The pH of solution had an affect on dissolution of copper, and sulfur ion had an affect on dissolution of silver. The copper dissolved amount from 20 % gold sample was about 26 times comparing with that of 12 % gold sample in the 0.9 % solution containing 1 % lactic acid. Corrosion products were silver chloride and copper chloride in NaCl solution, and silver sulfide and copper sulfide in NaCl solution containing $Na_{2}S$.

• 대한치과보철학회지
• /
• 제32권3호
• /
• pp.378-395
• /
• 1994

The purpose of this study was to investigate the effect of various metal surface treatments and adhesive systems on the flexural bond strength of composite resin to Au-Ag-Cu-Pd alloy. The specimens were divided into nine groups by the combinations of surface treatment methods and adhesive systems. The types of surface treatment in this study were alumina blasting only, alumina blasting-Sn plating, alumina blasting-heating and three kinds of adhesive system used in this study were Silicoater system(Heraeus Kulzer GmbH,Germany), Superbond C & B(Sun Medical Co.,Ltd.,Japan) and Cesead opaque primer(Kurary Co.,Ltd.,Japan). After surface treatments and adhesive systems were applied, each specimen was built up with Dentacolor composite resin (Heraeus Kulzer GmbH,Germany). Four-point flexural bond strength was measured by Instron universal testing machine (Model 4301,U.S.A.) and modes of failure were observed by SEM(JEOL,SSM-840A,Japan). The obtained results were as follows: 1. The group that was bonded with Superbond C & B after alumina blasting-heating shelved the highest bond strength with significant difference among the groups, except the group with Cesead opaque primer after alumina blasting-Sn plating(P<0.05). 2. In the groups bonded with Cesead opaque primer, there was significant difference only in the bond strength between the alumina blasting-Sn plating group and alumina blasting group, where the former showed a higher bond strength(P<0.05). 3. In the groups bonded with Silicoater system, there were no significant differences in bond strength regardless of the surface treatment method(P<0.05). 4. In SEM evaluation, the groups of high bond strength, especially bonded with Superbond C & B after alumina blasting-heating and Cesead opaque primer after alumina blasting-Sn plating, revealed mainly cohesive-adhesive failure, whereas the others showed the tendency of adhesive failure.