• Journal of Korean Dental Science
• /
• v.10 no.1
• /
• pp.10-21
• /
• 2017

Purpose: The purpose of this study was to investigate the electrochemical characteristics of nanotubular Ti-25Nb-xZr ternary alloys for dental implant materials. Materials and Methods: Ti-25Nb-xZr alloys with different Zr contents (0, 3, 7, and 15 wt.%) were manufactured using commercially pure titanium (CP-Ti), niobium (Nb), and zirconium (Zr) (99.95 wt.% purity). The alloys were prepared by arc melting in argon (Ar) atmosphere. The Ti-25Nb-xZr alloys were homogenized in Ar atmosphere at $1,000^{\circ}C$ for 12 hours followed by quenching into ice water. The microstructure of the Ti-25Nb-xZr alloys was examined by a field emission scanning electron microscope. The phases in the alloys were identified by an X-ray diffractometer. The chemical composition of the nanotube-formed surfaces was determined by energy-dispersive X-ray spectroscopy. Self-organized $TiO_2$ was prepared by electrochemical oxidation of the samples in a $1.0M\;H_3PO_4+0.8wt.%$ NaF electrolyte. The anodization potential was 30 V and time was 1 hour by DC supplier. Surface wettability was evaluated for both the metallographically polished and nanotube-formed surfaces using a contact-angle goniometer. The corrosion properties of the specimens were investigated using a 0.9 wt.% aqueous solution of NaCl at $36^{\circ}C{\pm}5^{\circ}C$ using a potentiodynamic polarization test. Result: Needle-like structure of Ti-25Nb-xZr alloys was transform to equiaxed structure as Zr content increased. Nanotube formed on Ti-25Nb-xZr alloys show two sizes of nanotube structure. The diameters of the large tubes decreased and small tubes increased as Zr content increased. The lower contact angles for nanotube formed Ti-25NbxZr alloys surfaces showed compare to non-nanotube formed surface. The corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface showed longer the passive regions compared to non-treatment surface. Conclusion: It is confirmed that corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface has longer passive region compared to without treatment surface.

• Transactions of the Korean hydrogen and new energy society
• /
• v.9 no.1
• /
• pp.16-24
• /
• 1998

Recently Zr-based $AB_2$ type hydrogen absorbing alloy has received much attention as a negative electrode material for the Ni-MH batteries because of its high capacity. In this study $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ alloy was chosen and the effects of heat treatment and a partial substitution of the Mo in Mn site on the various electrode properties were investigated. The alloys was prepared by arc melting (as-cast sample). Some of them were heat treated at $1,100^{\circ}C$ for 4 hours. After this they were differentiated by the different cooling rates of slow cooling and quenching. Various electrode characteristics such as activation process, high rate dischargeability and self discharge characteristic were investigated with the three types of electrodes. It was found that heat treated alloys resulted in an increase in plateau flatness of P-C isotherms however both discharge capacity and high rate capability were decreased. And the partial substitution of Mo for Mn in $ZrV_{0.1}Mn_{0.7}Ni_{1.2}$ alloy improved the self-discharge characteristic without the loss of discharge capacity (300mAh/g).