This study was done to evaluate whether vital bleaching agents could influence on the translucency of the bovine enamel. The anterior bovine teeth that were extracted one day before and without any gross discoloration were obtained and then were preserved in physiologic saline. 6 mm cylindrical tooth specimens were fabricated with diamond puncher perpendicularly on labial surface of bovine tooth. After embedded in transparent acrylic resin with labial surface being exposed, they were cut to a thickness of 1.2 mm with low speed diamond saw (Isomat, Buehler Co., Lake Bluff, IL, USA). They were smoothly ground to 1 mm thickness of enamel with sandpaper. 24 specimens were randomly divided into 3 groups and control group respectively. Opalescence (10% carbamide peroxide, Ultradent, South Jordan, USA), Rembrandt (10% carbamide peroxide, DenMat, USA) and Opalescence F (15% carbamide peroxide with fluoride, Ultradent, USA) were applied on labial sides of the bovine enamel for 7 days (bleaching agents were reapplied every 24 hours) and the opposite surface was contacted to cotton that soaked in distilled water. The control group was soaked in distilled water. Three stimulus value X, Y and Z were evaluated with colorimeter (Color ' Color Differencerneter, Model TC-6FX, Tokyo Denshoku Co., Japan) on the labial surface of all specimen three times on white and black background plate before the bleaching agents were applied and on 3rd, 5th and 7th day after applied. The degree of translucency was normally assessed by measuring the inverse property, opacity (contrast ratio). 10% Opalescence, 15% Opalescence-F, and control group showed no significant variation in the translucency of bovine enamel, However Rembrandt decreased the translucency of it (p < 0.01).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.2
• /
• pp.293-299
• /
• 2005

It is important to reduce chair time and procedure in restorative treatment for children. Composite resin is not only used in esthetic restoration of anterior teeth but also posterior teeth by its improved physical property. The 7th generation dentin bonding system was recently developed in order to simplify three steps which is needed to bond composite resin to tooth surface-etchant, primer, adhesive. We compared shear bond strengths of 4, 5, 6, 7th generations dentin bonding systems. The primary dentin was pretreated with 4, 5, 6, 7th generation dentin bonding systems. Then composite resin was cured to the specimen using molds 2.5mm in diameter and 2mm in height. Thermocycling was performed and shear bond strength was finally measured. The results were as follow; 1. The mean values of shear bond strengths in 5th generation dentin bonding system(group 2) were greater than those of 4, 6, 7th generation dentin bonding system(group 1, 3, 4). The differences were statistically significant. 2. The mean values of shear bond strengths in 4th generation dentin bonding system(group 2) were greater than those of 6, 7th generation dentin bonding system(group 1, 3, 4). But, the differences were not statistically significant. 3. Between the mean values of shear bond strengths in 6, 7th generation dentin bonding system(group 3, 4) were similar.

• Restorative Dentistry and Endodontics
• /
• v.31 no.4
• /
• pp.269-281
• /
• 2006

This study evaluated the effectiveness and safety of an experimental bleaching strip (Medison dental whitening strip. Samsung medical Co., Anyang, Korea) containing 2.9% hydrogen peroxide. Twenty-three volunteers used the bleaching strips for one and a half hour daily for 2 weeks. As control group. the same strips in which hydrogen peroxide was not included were used by 24 volunteers with the same protocol. The shade change (${\Delta}E^{*}$, color difference) of twelve anterior teeth was measured using Shade Vision (X-Rite Inc., S.W. Grandville, MI, USA). Chroma Meter (Minolta Co., Ltd. Osaka. Japan) and Vitapan classical shade guide (Vita Zahnfabrik, Germany). The shade change of overall teeth in the experimental group was significantly greater than that in the control group (p < 0.05) and was easily perceivable. The change resulted from the increase of lightness (CIE $L^{*}$ value) and the decrease of redness (CIE $a^{*}$ value) and yellowness (CIE $b^{*}$ value). The shade change of individual tooth was greatest in canine. and smallest in central incisor. The safety of the bleaching strip was also confirmed.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.3
• /
• pp.263-270
• /
• 2019

Current trends in restorative dentistry focus on improving the esthetics and keeping the sound dental tissues as long as possible. The aims of this case report were to describe the successful outcome of cubic-phase zirconia laminate veneers for a patient with isolated microdontia by using a digital workflow, and to describe their clinical implications. A 15-year-old female who had isolated microdontia in combination with spacing visited Ajou University Dental Hospital for esthetic treatment. In this case, 6 maxillary anterior teeth were restored with cubic-phase zirconia laminate veneers without tooth structure removal by using a digital impression, computer-aided design (CAD) software, and computer-aided manufacturing (CAM) procedures. At 6-month follow-up, no distinct mechanical and biological complications were detected and the prostheses exhibited satisfactory esthetics and functions. Due to its favorable tissue responses and enhanced translucency, cubic-phase zirconia can be a suitable strategy for a noninvasive esthetic approach.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.26 no.2
• /
• pp.284-295
• /
• 1999

The purpose of this study was to measure and analyze the bond strength of bonded amalgam using dental adhesives and to compare this with light-curing composite resin. Sections 8mm in diameter were punched out from the labial surface of bovine anterior teeth. These were embedded in clear acrylic resin blocks with labial surface facing out. 55 specimens were made for enamel and dentin each. After dividing these into 5 groups, group 1: Superbond C&B, group 2: Panavia 21, group 3: All-Bond 2, group 4: Fuji I Glass Ionomer Luting Cement, group 5: Scotchbond Multi-Purpose(Restorative Z-100), molds with holes of 6.3mm in diameter and 1.5mm in depth were placed over the specimens. The exposed tooth surfaces were treated with adhesives and the molds were filled with amalgam. In group 5, the mold was filled with composite resin and light-cured for 40 seconds. The author measured all specimens for bond strength 24 hours after amalgam filing and analyzed fracture surfaces. The following results were obtained: 1. Among the dentin groups, groups 1, 2 and 4 showed significantly lower bond strength compared with group 5(P<0.05). 2. Among the enamel groups, group 4 showed significantly lower bond strength compared with group 5(P<0.05). 3. In group 2, 2D showed significantly lower bond strength compared with group 2E(P<0.05). Other adhesives showed no such differences in bond strength between dentin and enamel(P>0.05). 4. Cohesive failure was observed in groups 1E and 5D, while mixed failure was seen in groups 1 and 5. Only adhesive failures were noted in groups 2, 3, 4.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.560-569
• /
• 1999

Blood supply rather than nerve supply implies pulp vitality. To evaluate pulp vitality clinically, electric pulp test and thermal test which are based on sensory nerve response have been used in addition to many auxiliary data such as past dental history, visual inspection, radiographic examination, percussion, palpation and transillumination test. However, reactivity of the nerves to the stimulation is not synonymous with normalcy. Therefore measurement of pulpal blood flow using a laser Doppler flowmeter became a new trial to test the pulp vitality. The purpose of the present study was to evaluate normal pulpal blood flow level of maxillary teeth in adult to provide a guideline in determining the vitality of dental pulp. Pulpal blood flow was measured in maxillary central and lateral incisors, canines, first and second premolars and first molars of seventy nine adults of 22 - 30 years old using a laser Doppler flowmeter (PeriFlux 4001, Perimed Co., Stockholm, Sweden, 780 nm infrared laser, 1mW). For directly-made splints, silicone rubber impressions were taken directly from the mouth. For indirectly-made splints, alginate impressions were taken from the mouth and stone cast were made. After making depressions on the buccal surfaces of the cast teeth to indicate the hole positions, second impressions with vinyl polysyloxane putty were taken from the cast. Holes for the laser probes were made at the putty impressions 4mm above the gingival level. Laser probe (PF416 dental probe, 1.5mm) was inserted in the prepared hole and the splint was set in the mouth. After 10 minutes of patient relaxing, pulpal blood flow was recorded for 5 minutes on each tooth. The recorded flow was saved in the computer and calculated with a software 'Perisoft' version 5.1. Pulpal blood flow was also recorded in six teeth of five individuals with no response to electric pulp test and cold test, with periapical radiolucency, or with history of root canal treatment to compare with nonvital teeth. The difference between the mean flow values of each group of teeth were analyzed using one-way ANOVA and Duncan's Multiple Range test. The results were as follows: 1. The average pulpal blood flow values of all the tested teeth of each location were between 9 - 16 Perfusion Unit. Pulpal blood flow value was highest in maxillary lateral incisors, followed by first premolars, second premolars, canines, central incisors, and then first molars (p<0.01). 2. In six anterior teeth, indirectly-made splint group showed higher pulpal blood flow values than directly-made splint group (p<0.01). In posterior teeth, however, there was no significant flow value difference between directly-made splint group and indirectly-made splint one (p>0.05). 3. Teeth with vital pulps showed higher signal values than teeth with nonvital pulps (p<0.01), and the flow photographs showed heartbeat-synchronous fluctuations and vasomotions, while those were absent in non vital tooth.

• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.463-471
• /
• 2008

This study investigated the clinical effectiveness and safety of sealed bleaching compared to conventional in-office bleaching using a randomized clinical trial of split arch design. Ten participants received a chairside bleaching treatment on the upper anterior teeth, and each side was randomly designated as sealed or control side. A mixture of Brite powder (PacDent, Walnut, USA), 3% hydrogen peroxide and carbamide peroxide (KoolWhite, PacDent, Walnut, USA) were used as bleaching agent. The control side was unwrapped and the experimental side was covered with a linear low density polyethylene (LLDPE) wrap for sealed bleaching. The bleaching gel was light activated for 1 hour. The tooth shades were evaluated before treatment, after treatment, and at one week check up by means of a visual shade (VS) assessment using a value oriented shade guide and a computer assisted shade assessment using a spectrophotometer (SP). The data were analyzed by paired t-test. In the control and sealed groups, the visual shade scores after bleaching treatment and at check up showed statistically significant difference from the preoperative shade scores (p<.05). The shade scores of the sealed group were significantly lighter than the control immediately after bleaching and at the check-up appointment (p<0.05). Compared to prebleaching status, the ${\Delta}E$ values at post bleaching condition were $4.35{\pm}1.38\;and\;5.08{\pm}1.34$ for the control and sealed groups, respectively. The ${\Delta}E$ values at check up were $3.73{\pm}1.95\;and\;4.38{\pm}2.08$ for the control and sealed groups. ${\Delta}E$ values were greater for the sealed group both after bleaching (p<.05) and at check up (p<.05). In conclusion, both ${\Delta}E$ and shade score changes were greater for the sealed bleaching group than the conventional bleaching group, effectively demonstrating the improvement of effectiveness through sealing.