Park, Jae-Sung;Ryou, Min;Yoon, Eui-Pak;Yoon, Woo-Young;Kim, Kwon-Hee;Kim, Myung-Ho
- Journal of Korea Foundry Society
- /
- v.26 no.3
- /
- pp.123-128
- /
- 2006
Mechanical and thermal properties of spray-cast hypereutectic Al-20wt.%Si-xwt.%Fe alloys (x=0, 1, 3, 5) were investigated. After the spray-casting, hot extrusion was performed at $400^{\circ}C$. Intermetallic compound (${\beta}-Al_5FeSi$) and primary Si are observed in the spray-cast aluminum alloys. The size of primary Si and intermetallic compound of the spray-aluminum alloys became finer and more uniformly distributed than that of the permanent mold cast ones. Ultimate tensile strength of the spray-cast aluminum alloys increased by increasing Fe contents, but that of the permanent mold cast aluminum alloys decreased by increasing Fe contents possibly due to increased amount of coarse intermatallic compound. The coefficient of thermal expansion (CTEs) of the aluminum alloys became lower with finer primary Si and intermetallic compound, and this is attributed to the increased amount of interfacial area between the aluminum matrix and the phases of finer Si and intermetallic compound.
PDF KSCI

Kim, Dong-Hyuk
- Journal of Korea Foundry Society
- /
- v.40 no.6
- /
- pp.135-145
- /
- 2020
Aluminum cast iron has excellent oxidation resistance, sulfurization resistance, and corrosion resistance. However, the ductility at room temperature is insufficient, and at temperatures above 600?, the strength drops sharply and practicality is limited. In the case of heat-resistant cast iron, high-temperature materials containing Cr and Ni account for 30 to 50% or more. However, these high-temperature materials are expensive. Aluminum heat-resistant cast iron is considered as a substitute for expensive heat-resistant materials. Oxidation due to the aging temperature and holding time conditions increases more in 0 wt.% Al-cast iron than in 2 and 4 wt.% Al-cast iron according to oxidized weight and gravimetric oxide layer thickness measurements. As a result of observing the cross-section of the oxide layer, it was found to contain 0 wt.% of Al-cast iron silicon oxide-containing SiO₂ or Fe₂SiO₄ oxide film. In cast iron containing aluminum, the thickness of the internal oxide layer due to aluminum increases as the aging temperature and retention time increase, and the amount of the iron oxide layer generated on the surface decreases.
https://doi.org/10.7777/jkfs.2020.40.6.135 인용 PDF KSCI

Lee, Sung-Mo;Kim, Deok-Su;Park, Tae-Dong;Yoon, Young-Cheol
- Journal of Korea Foundry Society
- /
- v.36 no.1
- /
- pp.10-17
- /
- 2016
Numerical analysis has been performed to evaluate effect of the shape variables such as core length, slot width and slot length on misrun in aluminum die casting process for motor rotor. The predictive method for misrun in diecasting process was established by comparing the result of numerical analysis and an actual motor rotor. Solidification modulus was introduced to predict quantitatively the castability of aluminum diecasting process for motor rotor. It was found that there are minimum critical solidification modulus and slot width to prevent misrun according to core length through diecasting limit diagram proposed using the predictive method. The critical solidification modulus and slot width increase as core length increases to prevent misrun of aluminum motor rotor in diecasting process. Based on the results, the design criteria of slot shape to prevent misrun of aluminum motor rotor with various core length were established.
https://doi.org/10.7777/jkfs.2016.36.1.10 인용 PDF KSCI