• Korean Journal of Materials Research
• /
• v.19 no.5
• /
• pp.265-269
• /
• 2009

The through-thickness variations of strain and microstructure during high-speed hot rolled 5052 aluminum alloy sheet were investigated. The specimens were rolled at temperature ranges from 410 to $560^{\circ}C$ at a rolling speed of 15 m/s without lubrication and quenched into water at an interval of 30 ms after rolling. The redundant shear strain induced by high friction between rolls and the aluminum sheet was increased largely beneath the surface at a rolling reduction above 50%. Dynamic recrystallization occurred in the surface regions of the specimen rolled under conditions of high temperatures or high rolling reductions.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.84-86
• /
• 2007

Aluminum sheets were asymmetrically cold rolled without lubrication by using different roll velocities of upper and lower rolls in order to intensify the shear deformation. During asymmetrical cold rolling of aluminum sheets, a reduction per a rolling pass, initial sheet thickness, roll diameter, roll velocity ratio were varied to investigate the effect of rolling parameters. The formation of through thickness shear texture was related to the ratio of the contact length between the roll and sample($l_c$) to the sheet thickness(d). The strain states associated with asymmetrical rolling were investigated by the finite element method (FEM) simulation. FEM results indicated that the evolution of deformation texture in a thickness layer is strongly governed by integrated values of strain rates $\dot{\varepsilon}_{13}$ and $\dot{\varepsilon}_{11}$ along the streamline in the roll gap.

• Transactions of Materials Processing
• /
• v.30 no.5
• /
• pp.242-246
• /
• 2021

Aluminum alloy sheet is being applied to automobiles continuously for the purpose of reducing car body weight. However, due to low formability, there's a limit to application of products with a deep forming depth such as door inner parts. Therefore, the difficult-to-form parts are mainly segmented formed then joined together, which is also disadvantageous as it increases the cost of manufacturing. This study proposes a hybrid cold-hot stamping method for the 1-piece door inner part to reduce cost. To design the stamping process, numerical simulation method is established by using the temperature-dependent mechanical properties of AA6016. The formability according to the hybrid cold-hot stamping method is evaluated using numerical analysis. The suitability of the proposed stamping method is then verified through the stamping tryout.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.3
• /
• pp.1585-1593
• /
• 2015

3D-structured (embossed) aluminum sheets have been used in the heat insulation purpose for automative exhaust parts because of increasing their surface areas and stiffness reinforcement imposed in making the embossing pattern. However, there are many restrictions in press forming of the embossed sheet compared with the flat sheet (non-embossed one) because of its difference in the mechanical properties and the geometrical 3-dimensional shape. In this paper we investigated the deformation characteristic of embossed aluminum sheet in the incremental sheet forming process which has frequently used in the design verification and the trial manufacturing of sheet products. The single point incremental forming (SPIF) experiments for the rectangular cone forming using the CNC machine with a chemical wood-machined die and a circular tool shape showed that the formability of the embossed sheet are better than that of the flat sheet in view of the maximum angle of cone forming. This comes from the fact that the embossed sheet between the tool and the elastic die wall is plastically compressed and the flatted area contributes to increase the plastic deformation. Also the tool path along the outward movement from the center showed a better formability than that of the inward movement from the edge. However the surface quality for the tool path along the outward movement evaluated from the surface deflection is inferior than that of the tool path along the inward movement.

• Transactions of Materials Processing
• /
• v.20 no.7
• /
• pp.512-517
• /
• 2011

TRB(Tailor Rolled Blank) is an emerging manufacturing technology by which engineers are able to change blank thickness continuously within a sheet metal. TRB door inner panels with required larger thicknesses can be used to support localized high loads. In this study, the aluminum alloy 5J32 TRB sheet is used for a door inner panel application. The TRB material properties were varied by using three heat treatment conditions. In order to predict the failure of the aluminum TRB during simulation, the forming limit diagram, which is used in sheet metal forming analysis to determine the criterion for failure, was investigated. Full-field photogrammetric measurement of the TRB deformation was performed with an ARAMIS 3D system. A FE model of the door inner panel was created using Autoform software. The material properties obtained from the tensile tests were used in the numerical model to simulate the door inner of AA 5J32 for each heat treatment condition. After finite element analysis for the evaluation of formability, a prototype front door panel was manufactured using a hydraulic press.

• Transactions of Materials Processing
• /
• v.12 no.8
• /
• pp.710-717
• /
• 2003

The implicit, finite element analysis program for analyzing the springback in the warm forming process of aluminum alloy sheets was developed. For the description of planar anisotropy in warm forming temperatures, Barlat's yield function is employed, and the power law type constitutive equation is used in terms of working temperatures for the depiction of work hardening in high temperatures. Also, Jetture's 4-node shell elements are introduced for reflecting the mechanical behavior of aluminum alloy sheet and the non-steady heat balance equations are solved for considering heat gain and loss during the forming process. For the springback evaluation, Newton-Raphson iteration method is introduced for overcoming the geometric nonlinearlity problem. In order to verify the validity of the FEM program developed, the stretching bending and springback processes are simulated. Though springback analysis results are slightly bigger than experimental ones, they have the same trend of the decreasing springback as the forming temperature increases.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.08a
• /
• pp.13-20
• /
• 2003

The implicit, finite element analysis program for analyzing the springback in the warm forming process of aluminum alloy sheets was developed. For the description of planar anisotropy in warm forming temperatures, Barlat's yield function is employed, and the power law type constitutive equation is used in terms of working temperatures fur the depiction of work hardening in high temperatures. Also, Jetture's 4-node shell elements are introduced for reflecting the mechanical behavior of aluminum alloy sheet and the non-steady heat balance equations are solved for considering heat gain and loss during the forming process. For the springback evaluation, Newton-Raphson iteration method is introduced for overcoming the geometric nonlinearlity problem. In order to verify the validity of the FEM program developed, the stretching bending and springback processes are simulated. Though springback analysis results are slightly bigger than experimental ones, they have the same trend of the decreasing springback as the forming temperature increases.

• Journal of Welding and Joining
• /
• v.16 no.2
• /
• pp.84-92
• /
• 1998

On this study, the variations of hardness and microstructure were observed at he spot-welded part of 5182 alminum alloy sheets with thickness of 1.2 mm. The hardness of spot-welded part of aluminum alloy indicated the lowest value at nugget center. Also, the position where fatigue crack exists was investigated by surveying microstructure of the spot-welded sections. Mean load-deformation diagrams were obtained from static tensile test. Fracture was occurred completely within 5 mm after transforming elastic into plastic area. Fatigue test was stopped when the specimens of fatigue test had the final displacement of 0.2mm and measured fatigue bending angle and crack length. This study utilized them, investigated the relations between fatigue bending angle and fatigue crack length and made a estimation of the fatigue fracture life of resistance spot welded part of 5182 aluminum alloy sheet. The relative equation o fatigue crack length and fatigue failure life can be represented by {TEX}$L_{C}${/TEX}=α{TEX}$N_{f}^ {β}${/TEX}.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.74-80
• /
• 1998

An extensive corrosion study was initiated by galvalume steel sheet manufacturing company to clarify the corrosion behavior of zinc and zinc-alloy coated automotive sheet steel in out panel and electrical application. Since the early 1980's the use of zinc and aluminum alloy coated steel for vehicular corrosion protection has increased drastically. This paper describes the evaluation of formability, weldability and painted corrosion performance of galvalume steel sheet. This paper presents an overview of the program and some initial test results on the weldability, lifetime of the electrode tip shape of the spot welding and corrosion protection. Galvalume steel sheet improved corrosion performance and spot weldability of galvalume steel sheet has no problem for the variation of welding current. And tip lifetime was changed according to the influence of shape.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.159-164
• /
• 2000

The fracture behaviors of aluminum foils and sheet papers were analyzed on the basis of linear elastic fracture mechanics(LEFM). The fracture loads of the similarly shaped specimens were calculated by dimensional analysis. The actual fracture loads were measured using the simple tension equipment. The predicted fracture loads were compared with the experimental results.