• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.1079-1082
• /
• 2004

Dense $BaMgAl_{10}O_{17}:Eu^{2+}$ phosphor particles with a spherical shape have been synthesized through spray pyrolysis method using basic aluminum nitrate precursor as a spray solution. Also, a thin layer of silica on the surface of $BaMgAl_{10}O_{17}:Eu^{2+}$ particles were coated by hydrolysis reaction of alkoxide sources with the particles. The correlation between PL intensity and surface treatment by coating for the dense $BaMgAl_{10}O_{17}:Eu^{2+}$ particles have been investigated.

• 한국세라믹학회지
• /
• 제26권5호
• /
• pp.593-600
• /
• 1989

Fine spinel powder was prepared from the Mg-Al double alkoxide synthesized using magnesium powder, aluminum foil and sec-butyl alcohol. This powder was compared with powder prepared by mixing two commercial alkoxides. The spinelization was started at 50$0^{\circ}C$ and was almost completed at 100$0^{\circ}C$ with a good crystallinity in the double alkoxide system. In mixed alkoxide system, homogeneous spinel powder was not obtained and MgO existed as a second phase because of solubility and hydrolysis rate differences of two alkoxides. The relative density of specimen prepared by double alkoxide was 99% and specimen prepared by mixed alkoxide was 95%. The modulus of rupture of specimens prepared by double alkoxide and mixed alkoxide was 49.9kg/$\textrm{mm}^2$ and 41.6kg/$\textrm{mm}^2$, respectively.

• 한국세라믹학회지
• /
• 제26권4호
• /
• pp.453-458
• /
• 1989

Aluminum nitride powder prepared from the hydroxides, AlOOH and Al(OH)3 which were obtained by hydrolysis of Al-isopropoxide, was densified at 1750 and 180$0^{\circ}C$ for 60 min by hot-pressing under the pressure of 25kg/$\textrm{cm}^2$. Theoretical density could be obtained at 175$0^{\circ}C$. Their flexural strengths were 450MPa and 395MPa for the specimens obtained from Al(OH)3 and AlOOH, respectively. There was no remarkable change in flexural strength up to 100$0^{\circ}C$. Fracture toughness values were 3.50MN/m3/2 for Al(OH)3 and 3.11MN/m3/2 for AlOOH. It is assumed that these differences in mechanical properties are due to the abnormal grain growth for the AlN ceramics obtained from AlOOH.

• 한국세라믹학회지
• /
• 제31권3호
• /
• pp.291-297
• /
• 1994

Cordierite powders were prepared by controlled hydrolysis of metal alkoxides with catalysts in water medium without using organic solvents. Water was adjusted to a certain pH by HC1 and NH4OH. $\alpha$-Cordierite powder was prepared from aluminum isopropoxide, tetraethyl orthosilicate and magnesium ethoxide mixed with water adjusted to pH of 3. At water pH of 11, $\alpha$-cordierite, mullite and $\beta$-quartz phases were coexisted. The powders were freeze dried, calcined and then fired at different temperatures. The characteristics of powders were examined by means of DTA, X-ray diffraction, FT-IR, and electron microscopy. It was found that $\alpha$-cordierite could be synthesized at temperature of 120$0^{\circ}C$ from the powders prepared by alkoxides with water medium without organic solvents.

• 한국세라믹학회지
• /
• 제20권1호
• /
• pp.3-12
• /
• 1983

In the present study an attempt was made to synthesize the $Al_2O_3$.$2SiO_2$ glass in which atomic ratio is Al:Si=1:1 by sol-gel process. And at such a low temperature as 55$0^{\circ}C$ clear amorphous gel derived glass with Si-O-Al bonding was obtained. $Si(OC_2H_5)_4$ and $Al(NO_3)_3$.$9H_2O$ were used as the precursor and among the mutual solvents only n-butanol gave good results for the synthesis of the gel derived glass. Partial hydrolysis of TEOS with one-fold mol of $H_2O$ prior to the reaction with aluminum nitrate gave the better results., Total oxide content to the total reactants by weight was affective to the results.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.217-224
• /
• 1988

Alkoxide 법으로 합성한 알루미나의 동공 구조를 BET 법으로 구한 흡 탈착 등온선의 hysteresis loop와 동공 분포로부터 고찰하였다. 알루미나는 aluminum isopropoxide를 화학량의 물로 가수분해하여 제조하였고, 가수분해 온도는 3$^{\circ}C$와 8$0^{\circ}C$에서 수행하였다. 이어 20$0^{\circ}C$부터 50$0^{\circ}C$까지 단계적으로 승온시키며 일정시간 열처리하였다. 3$^{\circ}C$ 가수분해 시료의 동공부피는 열처리 온도에 비례하여 증가하였으며, 동공크기는 쌍입분포(twin peaked pore size distribution)형으로 나타났다. 그러나 8$0^{\circ}C$ 가수분해 시료는 열처리에 의하여 동공부피가 감소하고, 동공크기는 단입분포(single peaked pore size distribution)로 나타났다. 이러한 관찰 결과로부터 전자의 동공형태는 slit형, 후자는 ink-bottle형을 하고 있는 것으로 추정되었다. 이와 같이 가수분해 온도는 동공 형태를 결정하는 중요한 인자일 뿐만 아니라, 층상 알루미나의 구조수 일탈 거동을 결정하는데 중요하다. 열처리 효과는 단지 최종 제품의 동공 분포를 결정하는데 영향을 주고 있는 것으로 해석되었다.

• 한국응용과학기술학회지
• /
• 제22권2호
• /
• pp.168-174
• /
• 2005

Aluminum tri-butoxide was mixed with the water/ethanol solution and then chloroplatinic acid was added to the solution. The solution was dried at $100^{\circ}C$ for 15hrs to remove the solvent and water then it was calcined at $500^{\circ}C$. The catalyst was activated with a gas mixture. During the activation, the temperature was increased from $150^{\circ}C$ to $500^{\circ}C$. The necessary amount of urea was dissolved in 50mL water and injected. Aqueous urea solution was then mixed with the feed gas stream. At low temperatures, nitrogen containing compounds of urea decomposition are used as reductants in the reducton of $NO_X$. However at high temperatures the nitrogen containing compounds are oxidized to NO and $NO_2$ by oxygen instead of being used in the reduction. The activity of the catalyst was dependent on urea concentration in the feed stream when there was not adequate water vapor in the feed. The maximum conversion was shifted from $250^{\circ}C$ to $150^{\circ}C$ when water concentration was increased from 2 to 17%. It seems that the maximum temperature shifts to lower temperatures because the hydrolysis rate of HNCO increases with water, resulting in higher amounts of $NH_3$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.II
• /
• pp.1499-1502
• /
• 2005

Dense $BaMgAl_{10}O_{17}:Eu^{2+}$ phosphor particles with a spherical shape have been synthesized through spray pyrolysis method using basic aluminum nitrate precursor as a spray solution. This $BaMgAl_{10}O_{17}:Eu^{2+}$ particles prepared by the spray pyrolysis have shown the stronger emission intensity compared to the commercially-available $BaMgAl_{10}O_{17}:Eu^{2+}$. However, thermal stability of the BAM:Eu b lue phosphor is very poor due to changing from $Eu^{2+}$ to $Eu^{3+}$ at the thermal process, so brightness of the phosphor decreases. To improve the thermal stability of the dense BAM:Eu phosphor, the spherical BAM:Eu particles were coated with pure $BaMgAl_{10}O_{17}$ layer using the hydrolysis reaction in a solution system. The synthesized powders were characterized by XRD, SEM and PL. On the other hand, the emission properties of the BAM:Eu phosphors coated with $BaMgAl_{10}O_{17}$ layer before and after thermal treatment at $500^{\circ}C$ for 30 min were estimated under VUV excitation. The brightness of the coated phosphor was higher than that of the uncoated phosphor. Also, the coating thickness of BAM layer in the BAM:Eu particles was optimized.

• 한국재료학회지
• /
• 제17권11호
• /
• pp.593-600
• /
• 2007

Aluminum was anodized in a $H_2SO_4$ solution, and titanium (IV) oxide ($TiO_2$) was electrodeposited into nanopores of anodic porous alumina in a mixed solution of $TiOSO_4$ and $(COOH)_2$. The photocatalytic activity of the prepared film was analyzed for photodegradation of methylene blue aqueous solution. Consequently, we found it was possible to electrodeposit $TiO_2$ onto anodic porous alumina, and synthesized it into the nanopores by hydrolysis of a titanium complex ion under AC 8-9 V when film thickness was about $15-20{\mu}m$. The photocatalytic activity of $TiO_2$-loaded anodic porous alumina ($TiO_2/Al_2O_3$) at an impressed voltage of 9 V was the highest in every condition, being about 12 times as high as sol-gel $TiO_2$ on anodic porous alumina. The results revealed that anodic porous alumina is effective as a substrate for photocatalytic film and that high-activity $TiO_2$ film can be prepared at low cost.

• Bulletin of the Korean Chemical Society
• /
• 제31권12호
• /
• pp.3723-3729
• /
• 2010

We investigated the high-excitation voltage cathodoluminescence (CL) performance of blue light-emitting (ZnS:Ag,Al,Cl) and green light-emitting (ZnS:Cu,Al) phosphors coated with metal oxides ($SiO_2$, $Al_2O_3$, and MgO). Hydrolysis of the metal oxide precursors tetraethoxysilane, aluminum isopropoxide, and magnesium nitrate, with subsequent heat annealing at $400^{\circ}C$, produced $SiO_2$ nanoparticles, an $Al_2O_3$ thin film, and MgO scale-type film, respectively, on the surface of the phosphors. Effects of the phosphor surface coatings on CL intensities and aging behavior of the phosphors were assessed using an accelerating voltage of 12 kV. The MgO thick film coverage exhibited less reduction in initial CL intensity and was most effective in improving aging degradation. Phosphors treated with a low concentration of magnesium nitrate maintained their initial CL intensities without aging degradation for 2000 s. In contrast, the $SiO_2$ and the $Al_2O_3$ coverages were ineffective in improving aging degradation.