• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.135-135
• /
• 2003

This paper presents the preparation of SnO$_2$ films by Sol-Gel process and using spin coating method, and their sensing properties in CO gas. Experimental procedure consisted of following steps: (1) Tin chloride(SnCl$_4$) and Ammonium hydrogen carbonate (NH$_4$HCO$_3$) were used as precursors; (2) the Sol solution with concentration of about 10wt% SnO$_2$ was prepared from washed Gel-precipitate for spin coating step; (3) thereafter, the coating solution was dropped onto the alumina (Al$_2$O$_3$) substrate that was then spun, the spin coating was carried out with total 10 times; (4) finally, the films were calcined for 3 hours at 50$0^{\circ}C$ or higher temperature (600, 700, 800 or 90$0^{\circ}C$) in order to obtain various gram sizes. The average grain size was calculated by Scherrer's equation using main peaks in XRD spectra; meanwhile the thickness, microstructure and surface morphology of the films were observed by FE-SEM.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.9
• /
• pp.429-433
• /
• 2006

PZT(80/0) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precusor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5mol/L and the number of coating was varied from 0 to 6. The porosity decreased and the grain size increased with increasing the number of coatings. The thickness of the PZT-6(6: number of coatings) films was about $60{\mu}m$. The relative dielectric constant increased and the dielectric loss decreased with increasing the number of PZT(20/80) sol coatings. The relative dielectric constant and dielectric loss of the PZT-6 thick film were 275 and 3.5%, respectively. The remanent polarization, coercive field and breakdown strength of the PZT-6 film were $19.8{\mu}C/cm^2$, 13.7kV/cm and 130kV/cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.66-78
• /
• 1998

the microstructure and mechanical properties of seeded and ball-milled dry gels prepared by boehmite sol-gel method were discussed. The densification of seeded gels was improved with increasing seed content namely the number of seed The number of seed was 1.09, 3.35, 5.72${\times}$1012/cm3 boehmite when seeded with 1, 3, 5wt% respectively The ball milled gel contained about 0.5wt% seed and the number of seed was 4.72${\times}$1012/cm3 boehmite. The sintered density of 5wt% seeded gel was below 80% when sintered at 1300$^{\circ}C$ for 1h. On the other hand that of ball milled gel was very improved and reached to 97% In the case of 3wt% seeded gels the density over 97% was attained when sintered at 1500$^{\circ}C$for 1h. and the grain of the sintered body was several micrometers in size. However the sintered body of ball milled gel showed grain size of submicrometer when sintered at 1300$^{\circ}C$ for 1h. And this specimen showed highest harness value of 1900kg/mm2 The fracture toughness increased with increasing sintering temperature. The sintered body of ball milled gel showed the largest grain size and the highest fracture toughness without regard to sint-ering temperature.

• Advances in nano research
• /
• v.14 no.4
• /
• pp.355-362
• /
• 2023

Physical exercise, especially intense exercise and high intensity interval training (HIIT) by trampoline, can lead to muscle injuries. These effects can be reduced with intelligent products made of nanocomposite materials. Most of these nanocomposites are polymers reinforced with silicon dioxide, alumina, and titanium dioxide nanoparticles. This study presents a polymer nanocomposite reinforced with silica. As a result of the rapid reaction between tetraethyl orthosilicate and ammonia in the presence of citric acid and other agents, silica nanostructures were synthesized. By substituting bis (4-amino phenoxy) phenyl-triptycene in N, N-dimethylformamide with potassium carbonate, followed by catalytic reduction with hydrazine and Pd/C, the diamine monomer bis (4-amino phenoxy) phenyl-triptycene is prepared. We synthesized a new polyaromatic (imide) with triptycene unit by sol-gel method from aromatic diamines and dianhydride using pyridine as a condensation reagent in NMP. PI readily dissolves in solvents and forms robust and tough polymer films in situ. The FTIR and NMR techniques were used to determine the effects of SiO₂ on the sol-gel process and the structure of the synthesized nanocomposites. By using a simultaneous thermal analysis (DTA-TG) method, the appropriate thermal operation temperature was also determined. Through SEM analysis, the structure, shape, size, and specific surface area of pores were determined. Analysis of XRD results is used to determine how SiO₂ affects the crystallization of phases and the activation energy of crystallization.

• Membrane Journal
• /
• v.18 no.2
• /
• pp.176-184
• /
• 2008

Nano-porous ceramic membranes was synthesized by the sol-gel method. Gas permeation of hydrogen and nitrogen was determined by single composition gas. Pore size $0.1{\mu}m$ and porosity 32% of flat type ${\alpha}-Al_2O_3$ substrate was manufactured. An intermediate ${\gamma}-Al_2O_3$ layer with pore size of 4 nm was formed by dip-coating. Polymeric silica sol was synthesized by acid catalyzed hydrolysis and condensation of tetra-ethyl-ortho-silicate. Supported membranes on alumina were prepared by dipping and calcining. He, $N_2$ permeation experiments with nanoporous sol-gel modified supported ceramic membranes were peformed to determine the gas transport characteristics. $He/N_2$ permselectivity around $100{\sim}160$ and helium permeation in the order of $10^{-7}mol/m^2{\cdot}s{\cdot}Pa$ were measured in the temperature range of $303{\sim}363K$.

• Membrane Journal
• /
• v.15 no.2
• /
• pp.105-113
• /
• 2005

Silica membranes were prepared on a porous metal sheet by ultrasonic spray pyrolysis method for gas separation at high temperatures. In order to improve the permselectivity, silica was deposited in the sol-gel derived $silica/\gamma-alumina$ intermediate layer by pyrolysis of tetraethyl orthosilicate (TEOS) at 873 K. The pyrolysis with forced cross flow through the porous wall of the support was very effective in plugging mesopores, Knudsen diffusion regime, that were left unplugged in the membranes. At permeation temperature of 523 K, the silica/alumina composite membrane showed $H_2/N_2$ and water/methanol selectivity as high as 17 and 16, respectively, by molecular sieve effect.

• Journal of Sensor Science and Technology
• /
• v.7 no.3
• /
• pp.188-196
• /
• 1998

The sensing and electrical characteristics of $WO_{3}$-based n-type semiconductor gas sensors are investigated. In normal air condition, $TiO_{2}$(4 wt. %)-doped $WO_{3}$-based sensor fabricated without any binder shows the grain boundary ( GB ) potential barrier height of 0.26 V. Sensors fabricated with alumina, PVA and silica sol binders show 0.17, 0.22 and 0.26 V of GB potential barrier height, respectively. In the ambience of 120 ppm $NO_{x}$ concentration, the GB potential barrier height of the sensor fablicated without binder is increased to 0.59 V. The sensors were fabricated with alumina, PVA, silica sol binders show 0.43, 0.66 and 0.52 V of potential barrier, respectively. Thus the variation of the potential barrier at GB is largest in the sensor fabricated with the PVA binder. This is found to be the main reason why the sensor fabricated with the PVA binder shows the best sensitivity. It is also found that the decrease of sensitivity at a temperature higher than the optimum operation temperature is due to the temperature dependence of the sensor resistance in normal air condition rather than the desorption of the adsorbed $NO_{x}$ gas particles. In the ambience of 250 ppm CO concentration, the GB potential barrier heights of the sensors fabricated without binder and with PVA binder are about 0.2 V showing negligible change compared to the case of normal air ambience. This fact indicates that these sensors are good candidates for the selective detection of $NO_{x}$ gas in the mixture of CO and $NO_{x}$ gases.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.1076-1086
• /
• 1994

This study covers synthetic effect of the various hydrothermal treatments on formation of artificially made kaolinite mineral. The hydrothermal treatment includes the temperature treatment with time duration, addition of seeds, particle size of the starting material used, pH variation and the different types of organic acids. A colloidal silica and alumina sol which are commercially available are used for this study. A colloidal silica and alumina sol are mixed by the atomic ratio of Al/Si = 1, based on the theoretical kaolinite composition and calcined at $600^{\circ}C$ for 8 hours duration. It was found that the kaolinitic clay mineral was well developed; thereby, the different patterns of crystalline mineral are appeared. Spherical type as a crystal form was distinctively formed at the temperature of 20$0^{\circ}C$ to 25$0^{\circ}C$ with short duration time, while platy type as a crystal was highly yielded at 300~35$0^{\circ}C$. Moreover, by adding more than 20 wt% of seed as the natural kaolinitic clay to the starting material is widely distributed and developed when 2 ${\mu}{\textrm}{m}$ or less particle size of the starting material is used; also, when they are heat-treated at the temperature of 25$0^{\circ}C$ with 5 hours duration. With respect of the effect of pH variation on formation of the synthetic kaolinite minerals, the crystalline minerals are highly yielded at less than pH 2 and gradually diminished at more than pH9. Regarding to the effect of different acids on development of the kaolinite mineral, the organic acids with high chelating capacity produces good formation of crystalline minerals; whereas, amine radical-(NH2) is not an effective agent to generate the crystalline minerals.

• Polymer(Korea)
• /
• v.30 no.6
• /
• pp.550-555
• /
• 2006

The coating material for the ink-jet printing paper tends to be waterbase as the waterbase ink-jet ink is used more widely. Waterbase coating material consists of alumina sol as a pigment, poly(vinyl alcohol) as a main binder and polymeric additive for improving properties. In this study, polymeric auditive was synthesized by combining one or toto monomers among methacrylic acid, acrylic acid and acrylamide to the basic monomers, styrene and n-butylacrylate. The properties of printability such as ink absorption, ink spreading, and optical density, glossiness and water resistance were investigated by changing the kinds of surfactants, the composition of monomers and the structure of polymer particles. Results showed that materials containing anionic surfactant and/or acrylic acid had problems in com-patibility with alumina sol. Also, coating materials containing acrylamide had good printability and lout glossiness while those containing methacrylic acid did not have good printability and high glossiness.

• Membrane Journal
• /
• v.25 no.1
• /
• pp.15-26
• /
• 2015

In this study, porous metal (O.D. = 10 mm, length = 10 mm, 316 L SUS, Mott Corp.) and ${\alpha}$-alumina tube (O.D. = 10 mm, length = 50 mm, Pall, German) support was modified with suspension sols, which were consisted of $3{\sim}4{\mu}m$ and 150 nm size of ${\alpha}$-alumina particle in the water or silica-zirconia colloidal sol. The porous support was fabricated by dip coating method for 5 seconds with suspension of alumina particles. After drying at $100^{\circ}C$ for 1 h, it was calcined at $550^{\circ}C$ for 30 min. It was repeated several times in order to decrease big pore on support. The surface roughness and largest pore size on the porous support was decreased by increasing coating times with $3{\sim}4{\mu}m$ size of ${\alpha}$-alumina particle and alumina coating with 150 nm size of ${\alpha}$-alumina particle served as further smoothening the surface and decreasing the pore size of the substrate. And the silica-zirconia membranes were successfully prepared on the modified porous metal and ${\alpha}$-alumina supports, and showed hydrogen permeance in the range of $1.8-8.4{\times}10^{-4}mol{\cdot}m^{-2}{\cdot}s^{-1}{\cdot}Pa^{-1}$ and $3.3-5.0{\times}10^{-5}mol{\cdot}m^{-2}{\cdot}s^{-1}{\cdot}Pa^{-1}$, respectively.