• Clean Technology
• /
• v.19 no.2
• /
• pp.75-83
• /
• 2013

In the present paper, we review recycling and applications of titanium binary alloy scraps. The recycling techniques are to successfully prepare low oxygen content ingots using hydrogen plasma arc melting (HPAM) and to produce low oxygen content titanium alloy powders by Hydrogenation-dehydrogenation (HDH) and Deoxidation in solid state (DOSS) process. In addition, as applications of the titanium binary alloy scraps, Ti based solid-solution carbide powders, which would be used for producing Ti based solid-solution cermets with high toughness, were prepared using the titanium binary alloy scraps. These results confirmed that the titanium alloy scraps could be recycled and refined using the HPAM. The resulting oxygen content of the titanium alloy powders were below 1,000 ppm after powderizing. Finally, we had confirmed that the refined titanium alloy powders were able to be utilized as raw materials for preparing the toughened cermets.

• Resources Recycling
• /
• v.3 no.1
• /
• pp.25-31
• /
• 1994

This paper was focused to optimize hot extrusion condition of Mg machined chips and scraps as fundamental basic research for the recycle of Mg alloy. We have been performed to extrude at $300~380^{\circ}C$ temperature range under the extrusion ratio of 25:1 after cold-pressing AZ91 Mg machined chips and scraps. AZ91 Mg ingots was used as reference materials. Microstructure observation showed that the extruded machined chips were perfectly bonded and extruded materials became fine grain size($20\mu\textrm{m}$) by recrystallization during hot extrusion. The specimens extruded from the machined chips, scraps and Mg ingot indicated tensile strength of 330MPa and the elongation of 10% at room temperature.

• Resources Recycling
• /
• v.24 no.1
• /
• pp.21-27
• /
• 2015

The present study describes the process of producing low oxygen content alloy powder from Ti-6Al-4V and Ti-8Al-1Mo-1V (AMS 4972) alloy scraps using hydrogenation-dehydrogenation (HDH) and deoxidation in solid state (DOSS) processes. Each prepared powder was deoxidized with Ca contact and non-contact method to compare the deoxidation capability. It is known that the non-contact deoxidation method, using Ca vapor above the melting temperature $T_m$ of Ca, has greater deoxidation capability. However, Oxygen contents in Ti-6Al-4V and Ti-8Al-1Mo-1V powder after non-contact deoxidation method were higher than those after contact deoxidation method. Therefore, we investigate the effect of Al - the richest alloy element in theses Ti based metals - on the deoxidation processes.

• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Resources Recycling
• /
• v.21 no.1
• /
• pp.60-65
• /
• 2012

The Ti-6Al-4V alloys were prepared by recycling of dental Ti pure scraps using vacuum arc melting process, and their physical properties were evaluated the Ti-6Al-4V alloys with different oxygen concentrations. For the preparation of Ti-6Al-4V alloys, Ti pure scraps used for dental implant were utilized as a raw material, and their different oxygen concentrations were ranged from G1 to G4 grade in ASTM standards. It was confirmed that the weight loss of Al in the composition of Ti-6Al-4V alloy could be controlled under the Ar pressure of 875 torr during the melting of alloy. The oxygen concentrations of the Ti-6Al-4V alloys were ranged from 1170 to 3340 ppm. The vickers hardness change of the Ti-6Al-4V alloys showed a similar behavior with that of pure Ti. As a result, we confirmed a possibility of preparation of Ti-6Al-4V alloy by recycling of dental Ti scraps using vacuum arc melting process in this study.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 1993.03a
• /
• pp.7.1-7
• /
• 1993

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2017.05a
• /
• pp.73-74
• /
• 2017

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2017.10a
• /
• pp.95-96
• /
• 2017

• Archives of Metallurgy and Materials
• /
• v.66 no.3
• /
• pp.729-733
• /
• 2021

Ferrotitanium can be produced as a method of recycling Ti scraps. The eutectic composition of ferrotitanium, Fe_29.5Ti_70.5, can be obtained as a nanocrystalline phase due to relatively low melting point. Fe_29.5Ti_70.5 in which FeTi and β-Ti form a lamellar structure have high strength but low strain. To improve this, impurities were removed through hydrogen plasma arc melting (HPAM) and annealed. HPAM can remove substitutional/interstitial solid solutions. As a result, from 6733 ppm to 4573 ppm of initial impurities were removed by HPAM process. In addition, the strain was improved by spheroidizing and coarsening the lamellar structure through annealing. The effect of impurities removed through HPAM on the Young's modulus, yield strength, and strain was observed.

• Journal of Korea Foundry Society
• /
• v.30 no.3
• /
• pp.94-99
• /
• 2010

When the returned scrap of bulk amorphous alloy is remelted, impurities such as oxides and intermetallic compounds increase. Glass forming ability of its scrap is deteriorated remarkably. Melt fluxing technique is introduced to enhance the glass forming ability during melting and freezing of bulk amorphous alloys. Cu and Zr based alloys are chosen. Small pieces of these alloy scraps and $B_2O_3$ flux are put together in a quartz tube. Cyclic heating and cooling are done by induction heating and water quenching or air cooling. Melting fluxing was effective for both Cu-based and Zr-based alloy, and their glass forming abilities were improved with increasing the number of fluxing.