• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.412-417
• /
• 2001

본 연구는 습식법으로 수산화 알루미늄과 티타니아를 출발물질로 하여 $Al_2$O$_3$-TiO$_2$복합분체를 제조하였으며, 2 mol의 Al(OH)$_3$분말에 대하여 TiO$_2$분말량을 1, 3, 5, 7, 9, 11 wt%로 첨가하여 $Al_2$O$_3$-TiO$_2$복합분체의 특성을 조사하였다. 제조된 $Al_2$O$_3$-TiO$_2$계 복합분체는 $700^{\circ}C$~140$0^{\circ}C$까지 하소하여 XRD 분석을 한 결과 100$0^{\circ}C$까지는 TiO$_2$(rutile)상과 η-Al$_2$O$_3$상이 공존하다가 110$0^{\circ}C$부터 130$0^{\circ}C$까지는 η-Al$_2$O$_3$에서 $\alpha$-Al$_2$O$_3$로의 상전이가 일어나서 $\alpha$-Al$_2$O$_3$상과 TiO$_2$(rutile)상이 나타났으며 하소온도 140$0^{\circ}C$, TiO$_2$첨가량이 5 wt%일 때부터 $Al_2$TiO$_{5}$가 생성되기 시작하였다. TiO$_2$첨가량에 따른 비표면적값은 첨가량이 7 wt%까지는 감소하였으나 그 이상 첨가시 증가하였다. 입도분석 결과 평균입경은 15.74~23.21$mu extrm{m}$로서 TiO$_2$첨가량이 3 wt%일 때 가장 작은 값을 가졌으며 TiO$_2$첨가량은 5 wt% 이상부터 점차 감소하였다.

• Journal of Korea Foundry Society
• /
• v.22 no.2
• /
• pp.75-81
• /
• 2002

The main objectives were to investigate the suitability of CaO crucible for melting TiAl alloys and to develop investment mold for investment casting of TiAl alloys. TiAl alloy specimen were prepared by plasma arc furnace under argon atmosphere. After melting of TiAl alloy using CaO crucible, the results showed that there is little contamination of oxygen in the TiAl bulk. Conventional vacuum induction furnaces can be readily adaptable to produce cast parts of TiAl without high skilled techniques. The determination of optical metallography and microhardness profiles in investment cast TiAl alloy rods has allowed the gradation of the relative thermal stability of the oxides examined. The molds used for the present study were $ZrO_2$, $Al_2O_3$, CaO stabilized $ZrO_2$ and $ZrSiO_4$. Even although high temperature of mold preheating, $Al_2O_3$ mold is a promising mold material for investment casting of TiAl alloys in terms of thermal stability, cost and handling strength. It is important to take thermal stability and preheating temperature of mold into consideration for investment casting of TiAl alloys.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.225-230
• /
• 2001

저전압용 형광체로 주목받고 있는 SrTiO$_3$:Pr,Al 형광체를 고상반응법으로 제조하였다. 부활성체 Al이 23 mol% 첨가되었을 때 SrTiO$_3$:Pr 형광체는 최대 발광 강도를 보여주었다. 최대 발광 강도를 보인 형광체에 대해 제한시야회절상과 투과전자현미경을 이용하여 SrTiO$_3$:Pr,Al 적색 형광체내 2차상 형성에 대한 연구를 행하였고 또한 에너지 분산 분광 분석을 행하여 SrTiO$_3$:Pr,Al 형광체내 주입된 부활성제 Al의 함량을 결정하였다. 제한시야회절상의 결과에 의하면 SrTiO$_3$:Pr,Al 적색 형광체내에 단사정 SrAl$_2$O$_4$, 삼사정 Ti$_4$O$_{7}$, 육방정 SrAl$_{12}$O$_{19}$가 2차상으로 존재함을 보여 주었다. 에너지 분산 분광 분석 결과 부활성제 Al의 함량 중 일부는 SrTiO$_3$:Pr,Al 적색 형광체 격자에 고용되고 일부 Al은 SrAl$_{12}$O$_{19}$와 SrAl$_2$O$_4$의 2차상을 형성하는데 소모됨을 보여주었다.주었다.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.37-42
• /
• 2000

The comparative study of texture of Al/Ti thin films deposited on low-dielectric polymer and $SiO_2$substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and $SiO_2$by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($\theta$-2$\theta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and $SiO_2$substrates was characterized by cross-sectional transmission electron microscopy (TEM). Both the $\theta$-2$\theta$ method and rocking curve measurement suggest that Al/Ti thin films deposited on $SiO_2$have stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM revealed that grains of Ti films on $SiO_2$substrates had grown perpendicular to the substrate, while the grains of Ti alms on SiLK substrates were formed randomly. The lower degree of (111) texture of Al thin films on low-k polymer was due to Ti underlayer.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.413-419
• /
• 2002

Particulate composites of $Al_2O_3$/TiC/SiC, $Al_2O_3$/TiC and $Al_2O_3$/SiC have been fabricated by hot pressing and their R-curve behaviors and mechanical properties were investigated. $Al_2O_3$ containing 30 vol% TiC particles showed higher toughness by 8% than that for monolithic alumina and its fracture strength was increased significantly by approximately 30%. On the other hand, the addition of 30 vol% SiC of $3{\mu}m$ in $Al_2O_3$ decreased the fracture strength slightly but induced a rising R-curve behavior owing to the strong crack bridging of SiC particles. In case of $Al_2O_3$/TiC/SiC, arising R-curve behavior was also observed and the fracture toughness reached 6.6 MPa${\cdot}\sqrt{m}$ at the crack length of $1000{\mu}m$, which was lower than that of $Al_2O_3$/SiC, however, while the fracture strength was higher by about 20%. The fracture toughness seemed to be decreased as smaller TiC particles roughened the SiC interface and pullout of the SiC particles for crack bridging became less active.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.319-319
• /
• 1999

From isothermal and cyclic oxidation tests on thermomechanically treated Ti-5%Al, Ti47%Al-4%Cr, and Ti-48%Al-2%Cr-2%Nb alloys at 800, 900, 1000℃ in air, it was found that Ti-48%Al-2%Cr-2%Nb and Ti-47%Al-4%Cr had the best and the worst oxidation resistance, respectively. The oxide scales consisted primarily of TiO₂and Al₂O₃, with and without a small amount of dissolved Cr and 7b ions, depending on the alloy composition. These ions were slightly enriched inside the inner oxide layer, and strongly enriched around the scale-matrix interface. The outer TiO₂-rich layer was formed by the outward diffusion of Ti ions, while the inner (TiO₂+A1₂O₃,) mixed layer was formed by the inward transport of oxygen. The outward movement of Al ions farmed the intermediate Al₂O₃-rich Iayer, above talc prepared alloys.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.135-141
• /
• 2001

Arc-melted Ti-6Al-4V, Ti-4Fe and Ti-(1,2) Si alloys were oxidized at 700, 800, 900 and $1000^{\circ}C$ in air. The oxidation resistance of Ti-4Fe was comparable to that of Ti-6Al-4V, while the oxidation resistance of Ti-(1,2) Si was superior to that of Ti-6Al-4V. Ti-2Si displayed the best oxidation resistance among the four alloys, but failed after oxidation at $1000^{\circ}C$ for 17h. The oxide scale formed on Ti-6Al-4V, Ti-4Fe and Ti-(1,2)Si consisted of ($TiO_2$ and a small amount of $Al_2$$O_3$), ($TiO_2$ and a small amount of dissolved iron), and ($TiO_2$ plus a small concentration of amorphous $SiO_2$), respectively. The oxide grains of the surface scale of the four alloys were generally fine and round.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.287-292
• /
• 1982

Nonohmic properties of ZnO ceramics with various small amounts of additives were studied in relation to experimental methods, additive contant and sintaring temperature. The kinds of additives used to following chemicals were basic additives ($0.5Bi_2O_3$, $0.3BaCO_3$, $0.5MnCO_3$, $0.5Cr_2O_3$, $0.1KNO_3$), $TiO_2$ and $Al(OH)_3$. Expecially, this study has focused on the effectsof $TiO_2$ and $Al(OH)_3$ in ZnO ceramics with the basic additives. SEM studies indicated that the addition of TiO2 promoted grain growth but retarded grain growth with the addition of $Al(OH)_3$. Also, in the case of calcination of ZnO with $TiO_2$ and ZnO with $Al(OH)_3$ previously, grain size of ZnO with $TiO_2$ was larger and that of ZnO with Al(OH)3 was smaller in comparison to the case with out calcination. From the viewpoint of nonohmic exponent and nonohimic resistance, electrical characteristics of ZnO, $TiO_2$ and the basic additives was more effective than that of ZnO, $Al(OH)_3$ and the basic additives. Nonohmic exponent and nonohmic resistance of ZnO, $TiO_2$ and the basic additives was 11-13 and 40-65 respectively.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.153-158
• /
• 2002

$Al_2O_3$ composites powders with 1∼11 wt% $TiO_2$ were prepared by wet method and sintered at 1350$^{\circ}C$, 1450$^{\circ}C$ for 2h. Mechanical properties and microstructural evolution were investigated in this study. $Al_2O_3$-3 wt% $TiO_2$ composite were high bulk density of 2.37 g/$cm^3$ and low apparent porosity of 6.3%. The composites containing of 3 wt% $TiO_2$ showed moderately high bending strength of 68.9 MPa and the young's modulus of 35.5 MPa. The composites with increasing $TiO_2$ contents exhibit reduced thermal expansion coefficient due to the formation of $Al_2TiO_5$ phase.