• 한국재료학회지
• /
• 제21권10호
• /
• pp.546-549
• /
• 2011

Nano-sized $SnO_2$ thick films were prepared by a screen-printing method onto $Al_2O_3$ substrates. The sensing characteristics were investigated by measuring the electrical resistance of each sensor in a test box as a function of the detection gas. The nano-sized $SnO_2$ thick film sensors were treated in a $N_2$ atmosphere. The structural properties of the nano $SnO_2$with a rutile structure according to XRD showed a (110) dominant $SnO_2$ peak. The particle size of $SnO_2$:Ni nano powders at Ni 8 wt% was about 45 nm, and the $SnO_2$ particles were found to contain many pores according to the SEM analysis. The sensitivity of the nano $SnO_2$-based sensors was measured for 5 ppm $CH_4$ gas and $CH_3CH_2CH_3$ gas at room temperature by comparing the resistance in air with that in the target gases. The results showed that the best sensitivity of $SnO_2$:Ni and $SnO_2$:Co sensors for $CH_4$ gas and $CH_3CH_2CH_3$ gas at room temperature was observed in $SnO_2$:Ni sensors doped with 8 wt% Ni. The response time of the $SnO_2$:Ni gas sensors was 10 seconds and recovery time was 15 seconds for the $CH_4$ and $CH_3CH_2CH_3$ gases.

• 자원리싸이클링
• /
• 제28권6호
• /
• pp.79-86
• /
• 2019

최근, 전기차 증가에 따른 리튬 전지의 사용량 증가로 리튬 가격 증가 및 폐리튬전지 발생량이 증가하고 있다. 이러한 이유로 폐리튬전지 내 리튬 회수에 대한 연구가 진행되고있다. 본 연구에서는 폐전기차 셀분말의 열처리 조건에 따른 선택적 리튬 침출에 관한 연구를 진행하였다. 셀 분말(LiNi_xCo_yMn_zO₂, LiCoO₂)로부터 선택적 리튬 침출을 위해서는 환원을 통한 상변화 및 분리가 필요하다. 폐전기차 셀분말 내 탄소는 고온에서 산소와 반응하여 환원제 역할을 한다. 적정 온도를 알고자 대기/질소 분위기에서 TG-DSC 분석 및 550 ~ 850 ℃ 열처리 후, XRD 분석을 하였다. 열처리 된 분말은 ICP 분석을 위해 D.I water에서 1:10 비율로 침출 후 분석하였다. XRD 분석결과, 700 ℃에서 Li₂CO₃ 피크가 확인되었다. 850 ℃ 열처리 시 Li₂O의 피크가 확인되었는데, 이는 Li₂CO₃가 723 ℃ 이상의 온도에서 Li₂O와 CO₂로 분해되었기 때문이다. 또한 Li₂O와 Al₂O₃와 반응으로 LiAlO₂가 확인되었다. 850 ℃에서 열처리 시 Li 침출율이 낮아졌는데 이는 LiAlO₂가 D.I water에서 침출하지 않기 때문으로 판단된다. 리튬 침출율의 경우 열처리의 조건에 따라 달라지며, 질소 분위기 중 700 ℃로 열처리 시 약 45 %의 리튬침출이 확인되었다. 침출 용액을 고-액분리 후증발농축하여 XRD 분석을 실시한 결과, Li₂CO₃의 피크를 확인하였다.