• 한국세라믹학회지
• /
• 제37권2호
• /
• pp.122-127
• /
• 2000

The thermal expansion, thermal stability, mechanical strength and infrared radiative property of Al2TiO5-clay composites, prepared from synthesized Al2TiO5 and clay, were investigated to develop a material for far infrared radiators. The emittance of composites containing 10~50 wt% clay, heated at 1,20$0^{\circ}C$ for 3 h, increased with increasing clay content and emittance was about 0.3 and 0.92 in the ranges of 3,400~2,500 cm-1 and 2,500~400cm-1, respectively. The bulk density and bending strength of the Al2TiO5-clay composites increased with increasing clay content. 50 wt% Al2TiO5-50 wt% clay composite, heat-treated at 1,20$0^{\circ}C$, had an adequate strength for infrared radiators; 80 MPa. The degree of thermal expansion hysteresis decreased with increasing clay content and the mean thermal expansion coefficient increased with increasing clay content. The thermal expansion coefficient of 50 wt% Al2TiO5-50 wt% clay composite heated at 1,20$0^{\circ}C$ was 5.78$\times$10-6/$^{\circ}C$.

• 산업기술연구
• /
• 제20권A호
• /
• pp.239-245
• /
• 2000

Sintered $Al_2TiO_5$ has a very low thermal expansion and an infrared radiative selectively emitting large amounts of far infrared rays. However, it is week in mechanical strength. Spectral infrared emittance, thermal expansion coefficient, and mechanical strength of $Al_2TiO_5$-clay composites were studied to develop a material for far infrared radiators. The composites containing 10~50 mass% Jungsan clay had high emittance in the range of 2,000~500cm-1. The bending strength of the $Al_2TiO_5$-clay composites increased with increasing clay content. The $Al_2TiO_5$-clay composites with a clay content of 50mass% and heat-treated at $1,200^{\circ}C$ had a large strength for infrared radiators ; 86MPa. The average linear thermal expansion coefficient from $200{\sim}1,000^{\circ}C$ of the 50mass% jungsan clay containing compo sited heat-treated at $1,200^{\circ}C$ was lower than $3.87{\times}10-6/^{\circ}C$.

• 헤리티지:역사와 과학
• /
• 제46권4호
• /
• pp.108-125
• /
• 2013

경주 동천동 출토 토제범(土製范)에 대한 실측복원도, 조성광물 분석, 입도 및 물성시험, 미세조직관찰, 색도차 및 주성분 분석결과를 알아보았다. 연구대상 내범과 외범의 단면은 내측(제1층위)과 외측(제2층위)으로 구분되고 외측에는 유기물이 혼합되어 있다. 단면에는 열적 경험과 탈형제로 인한 변화 양상이 확인되며, X-선 촬영에서는 내측인 제1층위가 투과율이 높은 광물로 구성되었고 편광현미경에서 석영만이 관찰되었다. SEM 관찰에서 단면의 내측은 공극이 확대된 양상을 나타내고 중앙은 균열이 발달하였으며 외측에서는 변화를 관찰할 수 없었다. 구성입자의 입도는 내범과 외범이 거의 유사하며 미사질식양토로 구분되고, 미사질과 점토의 구성비는 약 2.7 : 1과 약 2.9 : 1이었다. 물성시험에서 내범과 외범의 밀도와 흡수율은 유사하고 공극률만이 내범이 27.36%와 외범은 31.09%로 다소 차이가 있었다. 단면의 색도차는 제1층위의 표면에 탈형을 위해 그을음을 입히거나 제1층위를 먹물로 수비하였을 가능성이 있다. 조성광물 분석에서는 내범과 외범의 조성광물이 동일하나 내범에서만 자철석이 동정되었다. 주성분 분석에서는 $SiO_2$의 평균함량이 71.64%, $Al_2O_3$는 14.59%이고, 부성분 중 $Fe_2O_3$는 4.51%, $K_2O$는 3.06%이며, $Na_2O$, MgO, CaO, $TiO_2$, $P_2O_5$, MnO는 2% 이하를 나타내었다.