$Al/SiC/Al_{2}O_{3}$ hybrid composites are fabricated by squeeze infiltration method. From the misconstructive of $Al/SiC/Al_{2}O_{3}$ hybrid composites fabricated by squeeze infiltration method, uniform distribution of reinforcements and good bondings are found. Hardness value of $Al/SiC/Al_{2}O_{3}$ hybrid composites increases linearly with the volume fraction of reinforcement because SiC whisker and $Al_{2}$O$_{3}$ fiber have an outstanding hardness. Optimal aging conditions are obtained by examining the hardness of $Al/SiC/Al_{2}O_{3}$ hybrid composites with different aging time. Tensile properties such as Young's modulus and ultimate tensile strength are improved up to 30% and 40% by the addition of reinforcements, respectively. Failure mode of $Al/SiC/Al_{2}O_{3}$ hybrid composites is ductile on microstructural level. Through the abrasive wear test and wear surface analysis, wear behaviour and mechanism of 6061 aluminum and $Al/SiC/Al_{2}O_{3}$ hybrid composites are characterized under various testing conditions. The addition of SiC whisker to $Al/SiC/Al_{2}O_{3}$ composites gives rise to improvement of the wear resistance. The wear resistance of $Al/SiC/Al_{2}O_{3}$ hybrid composites is superior to that of Al/SiC composites. The wear mechanism of aluminum alloy is mainly abrasive wear at low speed range and adhesive and melt wear at high speed range. In contrast, that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is abrasive wear at all speed range, but severe wear when counter material is stainless steel. As the testing temperature increases, wear loss of aluminum alloy decreases because the matrix is getting more ductile, but that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is hardly varied. Oil lubricant is more effective to reduce the wear loss of aluminum alloy and $Al/SiC/Al_{2}O_{3}$ hybrid composites at high speed range.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.130-130
• /
• 2018

산업 발전으로 특수합금들이 발달함에 따라 가공할 수 있는 새로운 절삭공구소재들이 개발되어지고 있다. 또한 공구소재보다 코팅개발이 상대적으로 더욱 효과적이기 때문에 코팅 기술 개발이 활발히 진행되고 있다. 일본에서는 새로운 코팅층 물질 개발보다는 기존의 코팅물질을 조합하거나 개량하여 성능을 향상시키는 추세이다. TiAlSiN 박막은 스퍼터링과 음극 아크 소스를 이용한 hybrid 공정을 이용하여 코팅 후 특성을 평가하였다. Ti-50at.%Al의 조성을 갖는 TiAl 합금 타겟은 음극 아크 소스를 이용하여 코팅하였다. 공정 가스는 Ar과 N2의 혼합 가스를 사용하였으며 공정 압력은 $1.0{\times}10^{-2}Torr$이었다. 음극 아크 소스에 인가된 전류는 70 A이었다. TiAlSiN 박막의 Si 함량을 조절하기 위해서 Si은 스퍼터링으로 코팅하였으며 스퍼터링 소스에 인가되는 전력의 세기를 0.29 kW ~ 1.05 kW까지 변화시켰다. 코팅 공정에 사용된 Si 타겟의 순도는 4N이다. TiAlSiN 박막의 Si 함량은 스퍼터링 전력에 따라 3.4 ~ 14.4at%까지 변화하는 것을 확인하였다. TiAlSiN 코팅층의 경도는 초미소 경도계를 이용하여 측정하였으며, Si 함량이 증가하면 TiAlSiN 박막의 경도도 증가하는 것을 확인할 수 있다. TiAlSiN 박막의 Si 함량이 9.2at.%일 때 3000 Hv 이상의 경도를 보였다. TiAlSiN 코팅층의 Si 함량이 14.4at%로 높아지면 경도가 낮아지는 현상을 보였다. TiAlSiN 박막의 Si 함량이 증가하면 내산화성이 향상되는 현상을 확인할 수 있었다.

• Journal of the Korean Ceramic Society
• /
• 제51권3호
• /
• pp.197-200
• /
• 2014

We investigated the influence of blistering on $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks passivation layers. $Al_2O_3$ film provides outstanding Si surface passivation quality. $Al_2O_3$ film as the rear passivation layer of a p-type Si solar cell is usually stacked with a capping layer, such as $SiO_2$, SiNx, and SiON films. These capping layers protect the thin $Al_2O_3$ layer from an Al electrode during the annealing process. We compared $Al_2O_3$/SiON stacks and $Al_2O_3$/SiNx:H stacks through surface morphology and minority carrier lifetime after annealing processes at $450^{\circ}C$ and $850^{\circ}C$. As a result, the $Al_2O_3$/SiON stacks were observed to produce less blister phenomenon than $Al_2O_3$/SiNx:H stacks. This can be explained by the differences in the H species content. In the process of depositing SiNx film, the rich H species in $NH_3$ source are diffused to the $Al_2O_3$ film. On the other hand, less hydrogen diffusion occurs in SiON film as it contains less H species than SiNx film. This blister phenomenon leads to an increase insurface defect density. Consequently, the $Al_2O_3$/SiON stacks had a higher minority carrier lifetime than the $Al_2O_3$/SiNx:H stacks.

• Journal of the Korean Chemical Society
• /
• 제38권1호
• /
• pp.1-7
• /
• 1994

Semiempirical MNDO calculations are employed to study ionicity of OH groups and stability in $T_1-OH-T_2bridges(T_1$ = Al, B and $T_2$ = P, Si) such as found in aluminophosphate family($AlPO_4-5$, BAPO-5, and SAPO-5) molecular sieves. Dimeric model clusters of Al-OH-P, B-OH-P and Al-OH-Si bridges were considered. It is shown that the elongation of the T-O bond, upon replacement of Al by B, occurs preferentially by a local deformation of the Al-O-P bridge. But the elongation of the T-O bond occurs preferentially by a rotation of Al-O-Si bridge upon substitution P for Si. Also, the ionicity of OH groups and stability increase in order to B-OH-P < Al-OH-P < Al-OH-Si bridge.

• Journal of Korea Foundry Society
• /
• 제33권3호
• /
• pp.103-112
• /
• 2013

Effect of Fe and Mn contents on the tensile properties of Al-4 wt%Mg-0.9 wt%Si alloy system has been studied. Common phases of Al-4 wt%Mg-0.9 wt%Si alloy system were ${\alpha}$-Al, $Mg_2Si$, ${\alpha}-Al_{12}(Fe,Mn)_3Si$ and ${\beta}-Al_5FeSi$. As Fe content of Al-4 wt%Mg-0.9 wt%Si alloy system increased from 0.15 wt% to above 0.3 wt%, ${\beta}-Al_5FeSi$ compound appeared. When Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, morphology of plate shaped ${\beta}-Al_5FeSi$ compound changed to chinese script ${\alpha}-Al_{12}(Fe,Mn)_3Si$. As Fe content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Mn alloy increased from 0.15 wt% to 0.4 wt%, tensile strength of the as-cast alloy decreased from 191 MPa to 183 MPa and, elongation of the alloy also decreased from 8.0% to 6.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with low Mn/Fe ratio of the alloy. However, when Mn content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Fe alloy increased from 0.3 wt% to 0.5 wt%, tensile strength of as-cast alloy increased from 181 MPa to 194 MPa and, elongation of the alloy increased from 6.8% to 7.0%. These improvements attribute to the morphology change from ${\beta}-Al_5FeSi$ phase to chinese script, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ phase shape-modified from with high Mn/Fe ratio of the alloy.

• Journal of Korea Foundry Society
• /
• 제13권4호
• /
• pp.350-358
• /
• 1993

Aluminum base composites reinforced with various amount of SiC particles and Mg contents have been investigated by different fabrication method for twenty-years. In this paper, how the decomposition and dissolution behaviors of $SiCp(20{\mu}m)$ in the melt of Al composites arised was studied. As the results, the decomposition and dissolution of SiCp into the melt of Al composites increased with increase of the temperature above $720^{\circ}C$, and holding time at a given melting temperature. Because SiC is thermodynamically unstable in this Al-SiCp composite at temperature above the liquidus, SiCp dissolves and reacts with Al in matrix to form $Al_4C_3$ according to following chemical equation $4Al+3SiC{\rightarrow}Al_4C_3+3Si$, Si decomposed and dissolved from SiCp increases Si content of matrix, while liquidus temperature of matrix decrease with increase of SiC content in matrix. The hardness of SiCp decreased with increase of the melting temperature, the hardness of the matrix /particle interface increased with increase of the melting temperature due to increase of the $Mg_2Si$ and $Al_4C_3$ intermetallic compounds, etc.

• Journal of the Korean Ceramic Society
• /
• 제51권5호
• /
• pp.392-398
• /
• 2014

$Al_2O_3$-SiC composites reinforced with SiC whisker ($SiC_w$) were fabricated using three different methods. In the first, $Al_2O_3-SiC_w$ starting materials were used. In the second, $Al_2O_3-SiC_w$-SiC particles ($SiC_p$) were used, which was intended to enhance the mechanical properties by $SiC_p$ reinforcement. In the third method, reaction-sintering was used with mullite-Al-C-$SiC_w$ starting materials. After hot-pressing at $1750^{\circ}C$ and 30 MPa for 1 h, the composites fabricated using $Al_2O_3-SiC_w$ and $Al_2O_3-SiC_w-SiC_p$ showed strong mechanical properties, by which the effects of reinforcement by $SiC_w$ and $SiC_p$ were confirmed. On the other hand, the mechanical properties of the composite fabricated by reaction-sintering were found to be inferior to those of the other $Al_2O_3$-SiC composites owing to its relatively lower density and the presence of ${\gamma}-Al_2O_3$ and ${\gamma}-Al_{2.67}O_4$. The greatest hardness and $K_{1C}$ were 20.37 GPa for the composite fabricated using $Al_2O_3-SiC_w$, and $4.9MPa{\cdot}m^{1/2}$ using $Al_2O_3-SiC_w-SiC_p$, respectively, which were much improved over those from the monolithic $Al_2O_3$.

• Journal of Power System Engineering
• /
• 제5권4호
• /
• pp.74-81
• /
• 2001

The infiltration behavior of molten Al-alloy, microstructures, hardness, and the interfacial reactions of $SiC_p/Al$ composites fabricated by the pressureless infiltration technique were investigated. It was made clear that both the weight fraction of SiC reinforcement and additive Mg content considerably influenced on the infiltration behavior of the molten Al-alloy matrix. Complete infiltration of molten Al-alloy achieved under the conditions that weight fraction of SiC content is more than 30wt%, and additive Mg content is more than 9wt%. Interfacial region of Al-alloy matrix and SiC reinforcement phase, $Mg_2Si$ was formed by the reaction between Mg and SiC. Another reaction product AlN was also formed by the reaction between Al-alloy matrix and gas atmosphere nitrogen.

• Korean Journal of Materials Research
• /
• 제27권11호
• /
• pp.603-608
• /
• 2017

$Si_3N_4$ is a ceramic material attracting attention in many fields because of its excellent abrasion resistance. In addition, Ti and TiAl alloys are metals used in a variety of high temperature environments, and have attracted much attention because of their high strength and high melting points. Therefore, study of the interface reaction between $Si_3N_4/Ti$ and $Si_3N_4/TiAl$ can be a useful practice to identify phase selection and diffusion control. In this study, $Si_3N_4/Ti_5Si_3+TiN/TiN/Ti$ diffusing pairs were formed in the $Si_3N_4/Ti$ interfacial reaction and $Si_3N_4/TiN(Al)/Ti_3Al/TiAl$ diffusion pathway was identified in the $Si_3N_4/TiAl$ interfacial reaction. The diffusion layers of the interface reactions were identified and, to investigate the kinetics of the diffusion layer, the integrated diffusion coefficients were estimated.

• Journal of the Korean Ceramic Society
• /
• 제39권4호
• /
• pp.413-419
• /
• 2002

Particulate composites of $Al_2O_3$/TiC/SiC, $Al_2O_3$/TiC and $Al_2O_3$/SiC have been fabricated by hot pressing and their R-curve behaviors and mechanical properties were investigated. $Al_2O_3$ containing 30 vol% TiC particles showed higher toughness by 8% than that for monolithic alumina and its fracture strength was increased significantly by approximately 30%. On the other hand, the addition of 30 vol% SiC of $3{\mu}m$ in $Al_2O_3$ decreased the fracture strength slightly but induced a rising R-curve behavior owing to the strong crack bridging of SiC particles. In case of $Al_2O_3$/TiC/SiC, arising R-curve behavior was also observed and the fracture toughness reached 6.6 MPa${\cdot}\sqrt{m}$ at the crack length of $1000{\mu}m$, which was lower than that of $Al_2O_3$/SiC, however, while the fracture strength was higher by about 20%. The fracture toughness seemed to be decreased as smaller TiC particles roughened the SiC interface and pullout of the SiC particles for crack bridging became less active.