• 한국주조공학회지
• /
• 제30권4호
• /
• pp.137-141
• /
• 2010

The effects of Zn amounts on the castability and tensile properties of Al-Zn-Mg-Cu alloys were investigated for development of high strength die casting aluminium alloys. Al-Zn-Mg-Cu alloys with 3.5% Zn showed high cast cracking tendency and poor mold filling behaviour. Al-Zn-Mg-Cu alloys with 5wt% Zn and 7wt% Zn had the tensile strengths of 300~400MPa and the elongations of 2~18%. The effect of Zn on the tensile strength of Al-Zn-Mg-Cu alloys was insignificant, but Al-Zn-Mg-Cu alloy with high Zn amount had lower elongation.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.78-78
• /
• 2002

• 열처리공학회지
• /
• 제20권5호
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• 한국기계기술학회지
• /
• 제20권6호
• /
• pp.818-823
• /
• 2018

In this study, the effect of pre-aging treatment for inhibition of natural aging of Al-4.8Zn-1.3Mg alloy by extrusion process was investigated. Firstly, the as-cast microstructure of Al-4.8Zn-1.3Mg alloy billet and its evolution during homogenization($460^{\circ}C$, $4h+510^{\circ}C$, 5h) were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), hardness analysis. The as-cast microstructures of Al-4.8Zn-1.3Mg alloy reveal $Mg_2Zn$, $Al_5Cu$, $Al_{13}Cu$ formed between dendrities. After homogenization, MgZn, $Al_4Cu$, $Al_{13}Cu$ phases precipitated into the matrix. In addition, standard deviation of homogenized billet was improved than as-cast billet from 2.62 to 0.99. According to pre-aging($100^{\circ}C$, 1h) Al-4.8Zn-1.3Mg alloy by extrusion process, yield strength and tensile strength deviation improved more than condition by natural aging.

• 한국재료학회지
• /
• 제7권8호
• /
• pp.660-667
• /
• 1997

AI-Mg-합금의 용융산화에 의해 생성되는 AlO$_{2}$O$_{3}$-복합재료의 미세구조에 미치는 합금원소의 영향을 연구하였다. AI-1Mg 합금과 AI-3Mg 합금을 기본으로하여 Si, Zn, Sn, Cu, Ni, Ca, Ce를 1, 3, 5 %를 무게비로 첨가하였다. 각 합금을 1473K에서 20시간 유지하여 산화시킨 후 산화층의 거시적 형상과 미세구조를 광학현미경으로 관찰하였다. 각 미세구조의 상분율을 상분석기로 측정하였다. 산화층의 최첨단면은 SEM과 EDX로 관찰하고 분석하였다. Cu나 Ni를 첨가한 합금으로부터 성장한 산화층의 미세구조가 가장 치밀하였다. Zn이 포함된 합금으로부터 성장한 산화층 최첨단 성장면에는 ZnO가 관찰되었다. Zn이 포함되지 않은 다른 합금의 성장 전면에는 항상 MgAi$_{2}$O$_{4}$상이 관찰되었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.86-86
• /
• 2002

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 춘계 학술발표강연 및 논문개요집
• /
• pp.85-85
• /
• 2002

• 열처리공학회지
• /
• 제19권5호
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• 한국주조공학회지
• /
• 제29권6호
• /
• pp.265-269
• /
• 2009

The optimum RRA heat treating conditions and SCC (stress corrosion cracking) resistance of semi-solid Al-Zn-Mg-Cu alloy fabricated by inclined cooling plate were compared with those of conventional mould cast alloys. The non-stirring method characterized by using a cooling plate can effectively eliminate dendritic structure and form a fine globular semisolid microstructure in as-cast Al-Zn-Mg-Cu alloy and the SCC resistance of semi-solid Al-Zn-Mg-Cu alloy was higher than that of conventional mold cast alloy. Also, after retrogressed treatment at RRA heat treatment of semi-solid Al-Zn-Mg-Cu alloy, retrogressed treatment time has increased more than 10 minutes at $180^{\circ}C$ to recovery the T6 heat treatment strength.

• 한국주조공학회지
• /
• 제41권3호
• /
• pp.241-251
• /
• 2021

7000계 알루미늄 합금은 다른 Al 합금에 비해 강도가 우수하여 주목을 받고있으며, 7000계 알루미늄 빌렛은 일반적으로 Direct-Chill (DC) 주조 공정을 통해 제조된다. DC 주조 공정으로 제조된 알루미늄 빌렛의 표면 결함은 주로 Exudation과 Meniscus freezing 현상과 관련이 있으며, 이는 합금 성분, 주조 속도 및 주조 온도의 영향을 받는다. 특히, 7000계 알루미늄 합금은 응고 과정에서 응고 온도 범위가 넓어 주조 결함이 발생하기 쉽다. 본 연구에서는 DC 주조 공정에 의해 제조된 Al-8Zn-2Mg-2Cu 합금 빌렛에 대한 표면 결함 변화에 대하여 조사하였다. 빌렛의 표면은 "Wavy" 또는 "Dot" 표면으로 관찰되었다. Wavy 표면은 낮은 주조 속도(200mm/min)와 온도(655℃)에서 Meniscus freezing 현상에 의해 형성되었으며, Concave 영역에서 Meniscus freezing 현상으로 인한 조성작 과냉으로 인해 미세한 수지상 조직이 관찰되었다. 반면에, 주조 온도가 높은 조건(675℃)에서는 Dot 표면이 기공 형성에 의해 형성되었으며, 높은 주조 속도(230mm/min)에서 제조된 Dot 표면을 갖는 빌렛에서는 높은 금속 수두압에 의해 Exudation 층이 형성되었다. Exudation 층의 Dot 영역과 Smooth 영역은 각각 미세한 수지상 형태와 주상정 형태의 조직이 관찰되었으며 이는 Dot 영역에서 가스 기공의 형성에 의한 결과이다.