• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.300-304
• /
• 2001

Effect of Cd addition on the fatigue properties of Al-Cu-Mn cast alloy was investigated by low and high cycle fatigue tests. With increasing Cd content, fatigue life and tensile strength were increased. It was found that the fatigue strength was 115MPa and the fatigue ratio was 0.31. Metallographic observation revealed that the fatigue crack initiated at the surface and propagated along the grain boundary. This propagation path was attributed to the presence of PFZ along the grain boundary. The tensile strength increased from 330MPa in the Cd-free Al-Cu- Mn cast alloy to 401MPa in the 0.15%Cd-containing alloy.

• Applied Microscopy
• /
• v.46 no.3
• /
• pp.160-163
• /
• 2016

Effect of dealloying condition on the formation of nanoporous structure in melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy has been investigated in the present study. In as-melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy spinodal decomposition occurs in the undercooled liquid during cooling, leading to amorphous phase separation. By immersing the as-melt-spun $Al_{60}Ge_{30}Mn_{10}$ alloy in 5 wt% HCl solution, Al-rich amorphous region is leached out, resulting in an interconnected nano-porous $GeO_x$ with an amorphous structure. The dealloying temperature strongly affects the whole dealloying process. At higher dealloying temperature, dissolution kinetics and surface diffusion/agglomeration rate become higher, resulting in the accelerated dealloying kinetics, i.e., larger dealloying depth and coarser pore-ligament structure.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.4
• /
• pp.274-282
• /
• 1998

The effect of Al addition on the fatigue properties of austenitic Fe-25Mn-Al-0.5C steels was studied. When Al was not added to the Fe-25Mn 0.5C steel, the strain induced ${\varepsilon}$ martensites, deformation twins and slip bands were formed during fatigue deformation. When 2wt% of Al was added to the steel, the deformation twins and slip bands were formed during fatigue deformation. When 5wt% of Al was added, only slip bands were formed. In low cycle fatigue test, the alloys containing 0wt% and 2wt%Al showed the cyclic hardening due to ${\varepsilon}$ martensites and deformation twins, resulting in shorter fatigue lives than the alloy containing 5wt%Al. In fatigue crack propagation test, the alloy without Al showed the highest crack propagation rate. The fracture surface of the alloy without Al was flat, whereas that of the alloy with 2% or 5%Al was rough. The ${\Delta}K_{th}$, values of the alloys with 0%, 2% and 5%Al were 16, 17.5, and $20.5MPam^{1/2}$, respectively.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.1
• /
• pp.71-77
• /
• 2013

Aluminium powder as reductant in aluminothermy process needs a fine particle size under 200 mesh, but it is not easy economically to make that because of its high ductility and powder production cost. In order to reduce the production cost of fine aluminum powder as reductant of $Mn_3O_4$ waste dust, therefore, the properties of aluminium alloy powder were investigated. Aluminium alloy ingot containing large amount of manganese can be crushed easily because of its intermetallic compounds having brittle properties. The manganese is also main element in ferro-manganese. We can obtain economically Al-15%Mn alloy powder by mechanical comminution process. And the result of thermite reaction using Al-15% Mn alloy powder instead of pure Al powder showed the fact that can be obtained the ferro-manganese which have a high purity in case of using pure aluminium powder as reductant. The recovery of manganese from $Mn_3O_4$ waste dust with Al-15%Mn alloy powder was higher level of about 70% than about 65% in case of using aluminium powder, that is due to lower spatter loss.

• Applied Microscopy
• /
• v.45 no.1
• /
• pp.9-15
• /
• 2015

In the present study, microstructural evolution in CuCrFeNi, CuCrFeNiMn, and CuCrFeNiMnAl alloys has been investigated. The as-cast CuCrFeNi alloy consists of a single fcc phase with the lattice parameter of 0.358 nm, while the as-cast CuCrFeNiMn alloy consists of (bcc+fcc1+fcc2) phases with lattice parameters of 0.287 nm, 0.366 nm, and 0.361 nm. The heat treatment of the cast CuCrFeNiMn alloy results in the different type of microstructure depending on the heat treatment temperature. At $900^{\circ}C$ a new thermodynamically stable phase appears instead of the bcc solid solution phase, while at $1,000^{\circ}C$, the heat treated microstructure is almost same as that in the as-cast state. The addition of Al in CuCrFeNiMn alloy changes the constituent phases from (fcc1+fcc2+bcc) to (bcc1+bcc2).

• Journal of Powder Materials
• /
• v.4 no.2
• /
• pp.100-105
• /
• 1997

In this study the changes of the hardness and microstructures during aging at 120$^{\cire}C$ of an RS-P/M Al-5.6wt%Zn-2.0wt%Mg-1.3wt%Zr-1.0wt%Mn-0.25wt%Cu alloy were studied using a transmission electron microscopy. The hardness increased rapidly at early stage of aging and reached the maximun when the specimen was aged for 24 hr. The many irregular-shaped $Al_4Mn$ and rod-shaped $Al_6Mn$ dispersoids with 0.1-0.4 $\mu$m in length were observed in the as-extruded alloy. The dark particles with 2-3 nm in size were observed in aged specimen for 5hr and those are thought to be G.P.zones or precursor of $\eta'$ precipitates. In aged specimen for 24 hr, the $\eta'$ phases were distributed homogeneously within the matrix and the PFZ with 30-40 nm in width was observed along the grain boundary. With further aging, the width of PFZ increased and $\eta$ phases were also detected within the matrix.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.227-227
• /
• 1999

The effects of intermediate annealing (IA) and the final cold rolling (CR) condition on the microstructure and sagging resistance during brazing were investigated using three layer clad sheets composed of the Al-7.5 wt.%Si alloy (filler, thickness: 10 ㎛)/Al-1.3 wt.%Mn based alloy (core, 80㎛)/Al-7.5 wt.%Si alloy (filler, 10㎛). Also, the effect of 1.2∼2 wt.% Zn addition into the core on the sagging resistance of the clad sheets was determined. It was revealed that all the clad sheets fabricated by the optimum condition (IA at 690 K and CR to 20∼45%) show excellent sagging resistance with a limited erosion due to the formation of a coarsely recrystallized grain structure in the core during brazing. It was also revealed that the recrystallization behavior of the Al-1.3 wt.%Mn based alloy is hardly affected by the addition of 1.2-2 wt.%Zn during the brazing cycle. Therefore, the sagging resistance of the clad sheets is found to be governed not by the Zn content added in the A1-1.3wt.%Mn based core, but by the intermediate annealing and final cold rolling condition.

• Journal of Korea Foundry Society
• /
• v.29 no.4
• /
• pp.169-175
• /
• 2009

Effect of iron and manganese contents on die soldering reaction has been studied in Al-9wt.%Si-0.3wt.%Mg alloy. Ternary ${\alpha}_{hcp}-Al_8Fe_2Si$ and ${\alpha}_{bcc}-Al_8Fe_2Si$ intermetallic compounds formed by interaction diffusion between Al-Si-Mg system alloy melt and SKD61 die steel surface. Thickness of soldering reaction layer in die steel surface decreased as Fe and Mn contents of the melts increased : When Fe content of Al-9wt.%Si-0.3wt.%Mg melts at constant 0.5wt%Mn content was 0.15wt.%, 0.45wt.% and 0.6wt.%, thickness of soldered layer of each alloy was $64.5{\mu}m,\;57.3{\mu}m$ and $46.9{\mu}m$ respectively. For Mn content of the alloy melts at constant 0.45wt.%Fe content was 0.30wt.%, 0.50wt.% and 0.70wt.%, thickness of soldered layer of each alloy was $66.1{\mu}m,\;57.3{\mu}m$ and $48.3{\mu}m$ respectively.

• Journal of Powder Materials
• /
• v.4 no.4
• /
• pp.243-251
• /
• 1997

Engine valve-shaped TiAl-Mn intermetallics containing 43.5 to 47.5at%Al (Mn/Al=0.036) are successively fabricated by reactive sintering the elemental powder mixtures near-net shaped by extrusion and die forging. A duplex structure consisted of lamellar grains and equiaxed $\gamma$ grains is developed for all compositions, and the areal fraction of the lamellar grains(or equiaxed $\gamma$ grains) decreases (or increases) with increasing Al content. As Al content increased, the elongation increases with accompanying decrease in yield strength and ultimate tensile strength at both room temperature and 80$0^{\circ}C$. This indicates that the suitable composition is Ti-45at%Al-1.6at%Mn in considering the balance of ambient and elevated tensile properties. The reactive-sintered Ti-45Al-1.6Mn alloy shows superior oxidation resistance not only to the plasma arc melted one but also to the heat resistance steel STR35(representative exhaust valve head material for automotive engine). The reactive-sintered Ti-45Al-1.6Mn alloy coated with an oxidizing scale exhibits a better wear resistance than induction hardened martensitic steel STR11(representative exhaust valve tip material for automotive engine).

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.595-599
• /
• 2004

We investigated the structural, electrical and magnetic properties of Mn-doped $CuAlO_2$ delafossite ceramics ($CuAl_{1-x}Mn_{x}O_2,\;0\le\;x\;\le0.05$), synthesized by solid-state reaction method in an air atmosphere at a sintering temperature of $1150^{\circ}C$. The solubility limit of Mn ions in delafossite $CuAlO_2$ was found to be as low as about 3 $mol\%$. Positive Hall coefficient and the temperature dependence of conductivity established that non-doped $CuAlO_2$ ceramic is a variable-range hopping p-type semiconductor. It was found that the Mn-doping in $CuAlO_2$ rapidly reduced the hole concentration and conductivity, indicating compensation of free holes. The analysis of the magnetization data provided an evidence that antiferromagnetic superexchange interaction is the dominant mechanism of the exchange coupling between Mn ions in $CuAl_{1-x}Mn_{x}O$ alloy, leading to an almost paramagnetic behavior in this alloy.