• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1023-1024
• /
• 2006

Al-8Fe-2Mo-2V-1Zr alloys were prepared by the gas atomization/hot extrusion and the melt spinning/hot extrusion. For the gas atomized and extruded alloy, equiaxed grains with the average size of 400 nm and finely distributed dispersoids with their particle sizes ranging from 50nm to 200nm were observed. For the melt spun and hot extrusion processed alloy, refined microstructural feature consisting of equiaxed grains with the average size of 200nm and fine dispersoids with their particle sizes under 50nm appeared to exhibit a difference in microstructure. Strength of the latter alloy was higher than that for the former alloy up to elevated temperatures.

• 한국안전학회지
• /
• 제14권1호
• /
• pp.208-215
• /
• 1999

급냉응고 강화된 Al-9.45wt%Fe-4.45wt%Cr 합금의 크 거동을 40~115Mpa 응력범위와, 300~$441^{\circ}C$(0.53~0.66Tm) 온도 범위에서 조사하였다. 이 계열의 합금은 비행기 및 자동차의 구조용재료 혹은 엔진용 부품에 많이 사용되고 있으며, 재료의 사용이 주로 고온에서 이루어지므로 안전성을 확보하기 위해서는 크 실험이 특히 중요하다. 이 합금의 크 실험 결과 응력지수와 크 활성화에너지가 높았으며 실험 응력과 온도에 크게 좌우되었다. 크 응력이 조대화에 강하게 영향미치는 것으로 보이기 때문에 모든 크 시편의 분산입자의 조대화율은 등온 소둔시편 보다도 더 빠르게 나타났다. 분산상과 연결된 전위는 고응력, 저온의 크 시편에서 더욱 자주 관찰되었다. Power law creep에서의 크 변형 속도는 문턱응력과 전위분리기구를 포함하는 Sherby와 Rosler/Arzt식으로 예견되는 것과 일치함을 발견하였다. 이 합금에서 분산상은 void생성원으로 작용하였으며 소위 입계파괴인 입자내의 연성파괴의 원인이 되었다. 생성된 void는 성장하여 Al기지내의 분산상과 분리되고, 슬립에 의해 결정립계에 집적되어 결국 입계파괴가 일어났다. 그러므로 이들 분산상이 $Al_{13}Fe_4$, $Al_{13}Cr_2$ and $Al_2O_3$의 형성에 의해 파괴 기구의 중요한 역할을 함이 입증되었다.nd $Al_2O_3$의 형성에 의해 파괴 기구의 중요한 역할을 함이 입증되었다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.29-29
• /
• 1999

The synthesis of layered structures on the nanometer scale has become essential for continued improvements in the operation of various electronic and magnetic devices. Abrupt metal-metal interfaces are desired for applications ranging from metallization in semiconductor devices to fabrication of magnetoresistive tunnel junctions for read heads on magnetic disk drives. In particular, characterizing the interface structure between various transition metals (TM) and aluminum is desirable. We have used the techniques of MeV ion backscattering and channeling (HEIS), x-ray photoemission (ZPS), x-ray photoelectron diffraction(XPD), low-energy ion scattering (LEIS), and low-energy electron diffraction(LEED), together with computer simulations using embedded atom potentials, to study solid-solid interface structure for thin films of Ni, Fe, Co, Pd, Ti, and Ag on Al(001), Al(110) and Al(111) surfaces. Considerations of lattice matching, surface energies, or compound formation energies alone do not adequately predict our result, We find that those metals with metallic radii smaller than Al(e.g. Ni, Fe, Co, Pd) tend to form alloys at the TM-Al interface, while those atoms with larger atomic radii(e.g. Ti, Ag) form epitaxial overlayers. Thus we are led to consider models in which the strain energy associated with alloy formation becomes a kinetic barrier to alloying. Furthermore, we observe the formation of metastable fcc Ti up to a critical thickness of 5 monolayers on Al(001) and Al(110). For Ag films we observe arbitrarily thick epitaxial growth exceeding 30 monolayers with some Al alloying at the interface, possible driven by interface strain relief. Typical examples of these interface structures will be discussed.

• 한국분말재료학회지
• /
• 제11권3호
• /
• pp.193-201
• /
• 2004

1960년 Au-Si계 합금에서 처음으로 비정질상이 급속 응고법에 의해 보고된 이래/sup 1)/ 지난 40년 간 많은 합금계에서 비정질상이 보고되어졌다. 대표적으로 Fe-, Ni-, Co기 합금 등 많은 합금계에서 비정질상이 보고되었으나, 비정질상의 형성을 위해서는 약 105 K/s이상의 높은 냉각속도를 필요로 하였다. 1980년대 수백 K/s의 낮은 냉각속도 하에서도 비정질상이 형성될 수 있는 다원계 합금(multi-component alloy)이 Mg-Ln-(Ni, Cu, Zn), Ln-Al-TM 합금에서 보고되어 졌으나 많은 관심을 받지 못하다가 1993년 Zr-Ti-Ni-Cu-Be 합금에서 수 ㎝ 크기의 비정질합금 제조가 보고되면서 전 세계적으로 많은 관심을 받게 되었다. Zr-Ti-Ni-Cu-Be계 벌크 비정질 합금이 보고된 후 Zr-(Nb,Pd)-Al-TM, Pd-Cu-Ni-P, Fe-Co-Zr-Mo-W-B, Ti-Zr-Ni-Cu-Sn등 여러 합금계에서 벌크 비정질 합금이 보고되었다. (중략)