• 열처리공학회지
• /
• 제20권5호
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• 한국주조공학회지
• /
• 제31권1호
• /
• pp.18-25
• /
• 2011

Effect of Fe and Mn contents on the tensile properties has been studied in Al-9wt%Si-0.3wt%Mg alloy. As Fe content of Al-9wt%Si-0.3wt%Mg-0.5wt%Mn alloy increased from 0.15wt% to 0.45wt%, tensile strength of as-cast alloy decreased from 192 MPa to 174 MPa, and elongation of the alloy also decreased from 4.8% to 4.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with high Fe/Mn ratio of the alloy. However when Mn content of Al-9wt%Si-0.3wt%Mg-0.45wt%Fe alloy increased from 0.3wt% to 0.5wt%, tensile strength of T6 aged alloy increased from 265 MPa to 275 MPa, and elongation of the alloy increased from 2.3% to 3.6%. These improvements attribute to chinese script, ${\alpha}-Al_{15}(Mn,Fe)_3Si_2$ phase shape-modified from ${\beta}-Al_5FeSi$ phase with low Fe/Mn ratio of the alloy.

• 한국화재소방학회:학술대회논문집
• /
• 한국화재소방학회 2011년도 춘계학술논문발표회 논문집
• /
• pp.376-377
• /
• 2011

최근 Mg, Mg-Al합금, Al은 전자제품의 케이스, 차량의 휠 등의 신소재로서 활용성이 높아 사회적 수요가 급격히 늘고 있다. 이러한 수요 증가와 함께 관련 사업장에서는 취급 과정에서 폭발사고 위험성이 높아지고 있는데, 2010년도에는 국내 사업장에서 금속 분진에 의한 폭발사고가 4건이 발생하여 인명 및 재산피해가 발생하였다. Mg-Al합금의 폭발사고로 사망 1명과 부상 2명이 발생하였으며, Al분진의 폭발사고는 3건이 발생하여 사망 2명과 부상 3명의 인명피해로 이어졌다. 사고조사를 통하여 사업장에서의 금속분진에 대한 위험인식이 매우 낮은 것이 유사 사고가 반복되고 있는 가장 큰 이유로 알려지고 있는데, 이는 금속분진에 대한 부족한 안전기술정보와 밀접한 관련이 있다. 본 연구에서는 Mg, Mg-Al합금, Al등을 취급하는 관련 사업장에서 폭발사고 예방대책을 위하여 활용할 수 있는 폭발특성에 관한 안전기술정보 제공을 목적으로 하고 있다. 보다 구체적으로는 사고 다발 금속분진에 대한 위험성 이해에 도움을 될 수 있도록 동일 입경분포 조건에서의 위험성을 정량적으로 평가하였으며, 이를 위하여 각 금속분진의 동일 입경 조건에서 최대폭발압력, 폭발하한계 등의 폭발위험성 데이터를 실험적으로 조사 하였다. 조사한 시료는 평균입경 200 mesh의 Al, Mg, Mg-Al(60:40 wt%)로서 입도분석기(Beckman Coulter LSI 3320)를 사용하여 측정한 결과 평균입경은 약 $155{\mu}m$로 나타났다. Al분진의 농도변화에 따른 폭발압력을 조사한 결과, 최대폭발압력(Pmax)은 7.9 bar였으며 최대폭발압력상승속도 (dt/dP)max는 농도 $1500[g/m^3]$에서 322 [bar/s]로 최대가 되었으며 폭발 하한계(LEL)는 $70[g/m^3]$가 얻어졌다. 반면에 순수한 Mg의 LEL은 $30[g/m^3]$였으며 Pmax는 6.4 bar, (dP/dt)max는 100 [bar/s]가 얻어졌다. 이러한 결과로부터 LEL이 낮은 Mg는 Al보다 연소성이 큰 것으로 나타났으며, Al은 화염을 유지하는데 필요한 최저 열분해 가스농도를 확보하는데 Mg보다도 고농도의 분진이 필요함을 알 수 있었다. 또한 Mg-Al(60:40 wt%)의 LEL은 $50g/m^3$이었으며 Pmax는 9.4 bar, (dP/dt)max는 472 [bar/s]가 얻어졌다. 이러한 결과로부터 Mg-Al(60:40 wt%)합금의 연소성을 살펴보면 착화하기 쉬운 정도는 Mg와 Al의 성분비에 의해 변화하지만 Mg와 Al의 중간 정도로 나타나는 반면, Pmax는 Mg 또는 Al의 단독 물질 성분보다도 매우 큰 것을 알 수 있었다. 본 연구를 통하여 단일 성분의 Mg와 Al보다도 Mg와 Al이 일정 비율로 구성된 Mg-Al합금의 경우가 화재폭발 위험성이 증가한다는 사실을 알 수 있었으며, 이와 같은 폭발위험특성 자료를 활용하여 분진의 보관, 취급, 폐기 등의 지속적 관리가 필요하며 사업장 특성에 적합한 안전대책을 통한 사고예방대책이 요구된다.

• 열처리공학회지
• /
• 제11권3호
• /
• pp.168-176
• /
• 1998

The mechanical properties of mechanically alloyed Al-4wt%Mg alloys dispersed with $MgAl_2O_4$ dispersoilds at room and elevated temperatures were investigated. The powders in steady state during mechanical alloying consisted of Mg-supersatu rated Al solid solution and $Al_4C_3$ which resulted from the reaction of Al with C in process control agent (methanol). The hot-extruded materials consisted of uniformly dispersed fine $MgAl_2O_4$, ${\gamma}-Al_2O_3$, $Al_2O_3$ and matrix with extremly fine substructure. Tensile specimens prepared from the extruded bars were tested at room temperature to $400^{\circ}C$ under different strain rates. The tensile strength of alloys at room temperature ranged from 500 to 594MPa. At elevated temperatures, the tensile strengths and elongations decreased with increasing temperature. Adding 3% $MgAl_2O_4$ to Al-4wt%Mg increased the tensile strength of 50MPa at rowan temperature and 20MPa at $400^{\circ}C$.

• Journal of Plant Biology
• /
• 제37권3호
• /
• pp.301-308
• /
• 1994

The individual and combined effects of acidic rain, Mg deficiency (-Mg) and Al surplus (＋Al) on the growth of shoots and roots of pitch pine seedlings and the effect of humic substances (Lit) on Al toxicity were investigated. The growth of height and dry matter were not significantly less for pitch pine seedlings sprayed with simulated acid rain (SAR) of pH 3.5 than for those sprayed with SAR of pH 5.6. But treatments of Al and ＋Al-Mg in soil solution reduced the growth of seedlings in terms of height of shoots, and dry matter of shoots or roots. Effect of Mg deficiency on the growth of seedlings was apparent only when Al was treated simutaneously. The growth of seedlings, regardless of rain pH, decreased in the following order: control=-Mg>Lit＋Al>＋Al>＋Al-Mg. Treatments of Al and ＋Al-Mg in soil solution reduced the total length of secondary and teritary roots of seedlings regardless of rain pH, and decreased in the following order: the primary root

• 청정기술
• /
• 제20권3호
• /
• pp.330-336
• /
• 2014

Mg/Al 몰비를 1에서 3 범위에서 변화시켜 Mg-Al 혼합산화물을 공침법으로 제조하였다. 제조된 Mg-Al 혼합산화물은 X-선회절분석, 주사전자현미경분석, 질소흡착에 의한 비표면적 및 기공부피 측정, 이소프로판올의 승온탈착모델 반응으로 제조된 산화물의 특성분석을 수행하였다. 소성된 Mg-Al 혼합산화물은 이소프로판올의 탈수소/탈수반응에 적용하여 산염기 특성을 비교하였다. Mg-Al 혼합산화물에서 Al 함량이 증가함에 따라 비표면적 및 산점세기가 비례적으로 증가하였다. 이러한 산점세기 변화는 이소프로판올의 전환율 및 프로필렌 선택도에 직접적인 영향을 미쳤다.

• 한국세라믹학회지
• /
• 제27권4호
• /
• pp.501-512
• /
• 1990

Al2O3 and 0.25wt% MgO-doped Al2O3 powders were made from the alcohol solution of Al(NO3)3.9H2O and Mg(NO3)2.6H2O by spray pyrolysis method. Each powder was prepared at 900 and 100$0^{\circ}C$. Powders prepared at 90$0^{\circ}C$ were amorphous phase, but prepared at 100$0^{\circ}C$ wre mainly ${\gamma}$-Al2O3 crystalline form. Particle size of the MgO-doped Al2O3 powders was in the range of 0.2-2${\mu}{\textrm}{m}$, but undooped powders shwoed comparatively wider range of particle size. All the powders prepared at 900 and 100$0^{\circ}C$ were transformed to $\alpha$-Al2O3 crystalline form by calcination at 110$0^{\circ}C$ for 1hr. Each powder was sintered at 1600, 1650 and 1$700^{\circ}C$ for 2hrs. MgO-doped Al2O3 body sintering at 1$650^{\circ}C$ showed 99% of relative density but undooped Al2O3 showed 95% of relative density, even sintered at higher temperature of 1$700^{\circ}C$.

• 한국주조공학회지
• /
• 제33권2호
• /
• pp.55-62
• /
• 2013

Effect of Fe and Mn contents on the castability of Al-4wt%Mg-0.9wt%Si system alloy has been studied. According to the analysis of cooling curve for Al-4wt%Mg-0.9wt%Si-0.3wt%Fe-0.3/0.5wt%Mn alloy, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ and ${\beta}-Al_5FeSi$ phases crystallized above eutectic temperature of $Mg_2Si$. Therefore, these phases affected both the fluidity and shrinkage behaviors of the alloy during solidification. As Fe and Mn contents of Al-4wt%Mg-0.9wt%Si system alloy increased from 0.1 wt% to 0.4 wt% and from 0.3 wt% to 0.5 wt% respectively, the fluidity of the alloy decreased by 26% and 33%. When Fe content of the alloy increased from 0.1 wt% to 0.4 wt%, 23% decrease of macro shrinkage and 19% increase of micro shrinkage appeared. Similarly, Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, 11% decrease of macro shrinkage and 14% increase of micro shrinkage appeared. Judging from the castability of the alloy, Al-4wt%Mg-0.9wt%Si alloy with low content of Fe and Mn, 0.1 wt% Fe and 0.3 wt% Mn, is recommendable.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.628-631
• /
• 2002

$Al_2O_3$ capping layer and MgO protective layer were deposited by electron beam evaporation method using single crystal source. Thickness of the capping layer, $Al_2O_3$, was varied from 5 nm to 10 nm. Surface morphology was observed by SEM and AFM before and after hydration. And microstructure of deposited $Al_2O_3$ layer and chemical shift of electron binding energy were also observed by high resolution TEM and XPS, respectively, after hydration. From these results, it was found that Mg atoms diffused into $Al_2O_3$ layer, reacted with moisture and formed $Mg(OH)_2$ during hydration. As thickness of $Al_2O_3$ increased, extent of hydration increased. $Al_2O_3$ capped MgO thin films and uncapped MgO thin films were deposited on AC-PDP test panel to characterize discharge properties. Although $Al_2O_3$ has poor discharge properties rather than MgO, because of many hydrated species on the surface of MgO, similar discharge properties were observed.

• 한국기계기술학회지
• /
• 제20권6호
• /
• pp.818-823
• /
• 2018

In this study, the effect of pre-aging treatment for inhibition of natural aging of Al-4.8Zn-1.3Mg alloy by extrusion process was investigated. Firstly, the as-cast microstructure of Al-4.8Zn-1.3Mg alloy billet and its evolution during homogenization($460^{\circ}C$, $4h+510^{\circ}C$, 5h) were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), hardness analysis. The as-cast microstructures of Al-4.8Zn-1.3Mg alloy reveal $Mg_2Zn$, $Al_5Cu$, $Al_{13}Cu$ formed between dendrities. After homogenization, MgZn, $Al_4Cu$, $Al_{13}Cu$ phases precipitated into the matrix. In addition, standard deviation of homogenized billet was improved than as-cast billet from 2.62 to 0.99. According to pre-aging($100^{\circ}C$, 1h) Al-4.8Zn-1.3Mg alloy by extrusion process, yield strength and tensile strength deviation improved more than condition by natural aging.