• Journal of the Korean institute of surface engineering
• /
• v.47 no.4
• /
• pp.186-191
• /
• 2014

Double layer films which consisted of aluminum(Al) and magnesium(Mg) have been prepared by e-beam deposition. The structure, alloy phase, and corrosion resistance of the prepared films were investigated before and after heat treatment. The first (bottom) layer fixed with Al, and the thickness ratio between Al and Mg layers has been changed from 1 : 1 to 5 : 1, respectively. Total thickness of Al-Mg film was fixed at $3{\mu}m$. The cold-rolled steel sheet was used as a substrate. Heat treatment was fulfilled in an nitrogen atmosphere at the temperature of $400^{\circ}C$ for 2, 3 and 10 min. Surface morphology of as-deposited Al-Mg film having Mg top layer showed plate-like structure. The morphology was not changed even after heat treatment. However, cross-sectional morphology of Al-Mg films was drastically changed after heat treatment, especially for the samples heat treated for 10 min. The morphology of as-deposited films showed columnar structure, while featureless structure of the films appeared after heat treatment. The x-ray diffraction data for as-deposited Al-Mg films showed only pure Al and Mg peaks. However, Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ appeared after heat treatment of the films. It is believed that the formation of Al-Mg alloy phase affected the structure change of Al-Mg film. It was found that the corrosion resistance of Al-Mg film was increased after heat treatment.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.307-310
• /
• 1998

In this paper, $Al_2$O$_3$/MgO belayer was prepared with Electron-beam evaporation and the properties of the film was investigated in order to improve the property of MgO film, which is used for the protection layer in PDP(Plasma Display Panel). $Al_2$O$_3$/MgO belayer were improved of roughness and it were condensed by annealing, and the result of XPS analysis for $Al_2$O$_3$/MgO belayer unchanged binding energy. To investigate electric characteristics, discharge properties of $Al_2$O$_3$/MgO belayer were compared with discharge minimum voltage for MgO monolayer through Ar discharge experiments.

• Journal of Powder Materials
• /
• v.26 no.2
• /
• pp.138-145
• /
• 2019

In this study, Al-Si-Mg alloys are additively manufactured using a selective laser melting (SLM) process from AlSi10Mg powders prepared from a gas-atomization process. The processing parameters such as laser scan speed and laser power are investigated for 3D printing of Al-Si-Mg alloys. The laser scan speeds vary from 100 to 2000 mm/s at the laser power of 180 and 270 W, respectively, to achieve optimized densification of the Al-Si-Mg alloy. It is observed that the relative density of the Al-Si-Mg alloy reaches a peak value of 99% at 1600 mm/s for 180 W and at 2000 mm/s for 270W. The surface morphologies of the both Al-Si-Mg alloy samples at these conditions show significantly reduced porosities compared to those of other samples. The increase in hardness of as-built Al-Si-Mg alloy with increasing scan speed and laser power is analyzed due to high relative density. Furthermore, it was found that cooling conditions after the heat-treatment for homogenization results in the change of dispersion status of Si phases in the Al-Si matrix but also affects tensile behaviors of Al-Si-Mg alloys. These results indicate that combination between SLM processing parameters and post-heat treatment should be considered a key factor to achieve optimized Al-Si alloy performance.

• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.985-994
• /
• 1996

The initiation and growth of $\alpha$-Al2O3/metal composites by the directed oxidation of molten commercial AlZnMg-alloy at 1223-1423K were investigated. Spontaneous bulk growth did not occur on the alloy alone. but the uniform initiation and growth of the composite were obtained by putting a thin layer of SiO2 particles on the surface of the alloy. Without SiO2 the external surface of the oxide layer was convered by MgO and MgAl2O4. But with the SiO2 reaction initiate the porous ZnO layers were found on the growth surface. The higher process temperature yielded a lower metal content. The oxidation product of $\alpha$-Al2O3 was found to be oriented with c-axis parallel to th growth direction. The growth rates increased with temperature and the apparent activation energy was 111.8 kJ/mol.

• Journal of the Korean Ceramic Society
• /
• v.33 no.7
• /
• pp.832-838
• /
• 1996

Thermite reaction products of MgO and Al were added to MgO-C refractory to improve the properties of corrosion against the attack of slag, oxidation and mechanical spalling. Corrosion rate of MgO-C-MgAl2O4 spinel refractory at the ratio of 3.3(CaO/SiO2) slag was smaller than that of MgO-C and MgO-C-Al refractory. The excellent corrosion resistance of the MgO-C-MgAl2O4 spinel refractory against the slag attack was appeared by Al and MgAl2O4 spinel with high melting point and corrosion resistance and the high thermal conductivity and low thermal expansion of AIN. Hot M.O.R at 140$0^{\circ}C$ and the resistance of oxidation weight loss at 90$0^{\circ}C$ were 210kg/cm2 and -12% respectively.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.5
• /
• pp.454-460
• /
• 2016

Double-layered Al-Mg films have been deposited by using an e-beam deposition method on a cold-rolled steel sheet(CR), which the structure of the film was Al/Mg/CR. The micro-structure, alloy phase, and corrosion resistance of the Al-Mg coated CR were investigated before and after heat treatment at $400^{\circ}C$ for 2, 3, and 10 min in a nitrogen atmosphere. Total thickness of Al-Mg films was fixed at $3{\mu}m$ and the thickness ratio of Al and Mg layers(Al:Mg) has been changed from 5:1 to 1:5. The cross-sectional morphology of the films, which had the thickness ratio of 2:1(Al:Mg), 1:1, and 1:2, was changed after heat treatment from columnar to featureless structure. The x-ray diffraction data for as-deposited films showed only pure Al and Mg peaks. Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ phase appeared after the heat treatment. The Al-Mg coating with the thickness ratio of 1:1(Al:Mg) showed the best corrosion resistance of up to 500 hours by salt spray test.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.308-308
• /
• 2014

본 연구에서 PVD법중 하나인 스퍼터링(sputtering)법에 의해 제작된 Al-Mg 코팅막은 SEM, GDS, XRD를 통해 표면 및 단면의 조성분포를 분석하였으며, 내식성을 평가하기 위하여 함량별, 열처리 조건별 Al-Mg 막을 각각 5% NaCl 염수분무 환경 및 3% NaCl 자연침지 환경에 노출시켰다. 막의 내식 특성에 영향을 미치는 열처리의 영향을 알아보기 위하여 열처리-비열처리간 재료 특성 및 내식성평가 결과의 연관성을 비교-분석하였다. 열처리 결과 Al-Mg계 금속간 화합물 $Al_3Mg_2$와 $Al_{12}Mg_{17}$이 관찰되었으며 내식성 평가 결과, 열처리 Al-Mg 막은 비열처리 Al-Mg 막과 비교하여 양호한 내식성을 나타냈었다. 열처리를 통해 마그네슘(Mg) 성분이 대부분 금속간 화합물상으로 존재함에 따라 균일하게 분포하여 치밀한 부식생성물을 형성하게 되고, 이에 따라 Al-Mg 막 내식성에 기여한 것으로 사료된다.

• Journal of Korea Foundry Society
• /
• v.31 no.5
• /
• pp.284-287
• /
• 2011

Microstructures and tensile properties at ambient and elevated temperatures were studied by substituting RE for Sr in Mg-6%Al-(3-X)%RE-X%Sr alloys (X = 0~3). With increasing Sr content, $Al_4Sr$ phase with lamellar morphology was newly introduced at interdendritic regions, with a gradual extinction of needle-shaped $Al_4RE$. The Mg-6%Al-3%Sr alloy shows dendritic grains and interdendritic eutectic phases containing bulky Mg-Al-Sr and lamellar $Al_4Sr$ with more continuous manner. The substitution of Sr for RE provided higher YS, UTS and creep resistance at $175^{\circ}C$, which indicates that Sr would be more beneficial in tensile properties and creep resistance at elevated temperature than RE for the Mg-Al based casting alloys.

• Journal of Power System Engineering
• /
• v.21 no.2
• /
• pp.14-19
• /
• 2017

The corrosion characteristics of Al-Si-Mg alloy were investigated in $O_2$ and $H_2S/H_2$ environments at high temperature. The weight gain and the reaction rate constant of the Al-Si-Mg alloy were measured in the oxygen and hydrogen sulfide environments at 773K. The weight gain of Al-Si-Mg alloy was showed parabolic increase in the oxygen and hydrogen sulfide environments. The reaction rate constants were confirmed to be $1.45{\times}10^{-4}mg^2cm^{-4}sec^{-2}$ in the oxygen environment and $6.19{\times}10^{-4}mg^2cm^{-4}sec^{-2}$ in the hydrogen sulfide environment respectively. As a result of XPS analysis on the specimen surface, $Al_2O_3$ and MgO compounds were detected in oxygen environment and $Al_2(SO_4)_3$ sulfate was detected in the hydrogen sulfide environment. Corrosion rate of Al-Si-Mg alloy was about 4.3 times faster in hydrogen sulfide environment than oxygen environment.

• Journal of Korea Foundry Society
• /
• v.31 no.2
• /
• pp.60-65
• /
• 2011

Molten magnesium alloys and magnesium products are easily oxidized and burned when they are exposed to high temperature for manufacturing process and by accident. In order to solve these problems, CaO addition in magnesium alloys has been developed. The ignition resistance of CaO added Mg-3Al, Mg-6Al, and Mg-9Al Eco-Mg alloys were investigated in comparison with those of magnesium alloys without CaO. The ignition resistance was examined by three methods : DTA, furnace chip ignition test, and torch ignition test. DTA was carried out for obtaining quantitative ignition temperature data with respect to specimen geometry and test environment; the furnace ignition test for burr and chip ignition temperature data; and the torch test for ignition temperature data for manufactured products. The ignition resistance of magnesium alloys under all conditions greatly increased by CaO addition.