• Journal of Conservation Science
• /
• v.26 no.2
• /
• pp.157-169
• /
• 2010

This study focused on the material characteristics and archaeometric relationship between the molten glass and bronze materials within the crucibles and gilt-bronze Bodhisattva statue excavated from the Ssangbukri site in Buyeo, Korea. Yellowish green to red brown vitreous material in the crucibles was identified as lead glass which contained scarce amount of BaO, and low $Al_2O_3$ and CaO. Metallic molten material was identified as bronze of copper-tin-lead alloy with low amount of impurities that indicated well-refined materials. Also, cassiterite was used for raw metal ore of tin. The Bodhisattva statue consisted of major copper with trace impurities in the core metal, and gold amalgam in the gilded layer. Though lead isotopic analysis showed contradictory results in each lead glass, bronze and Bodhisattva statue that required further examination, it could be stated that the statue was made in the Ssangbukri site based on the high-level technical skills of bronze production.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.203-215
• /
• 2007

Statement of problem: Titanium and its alloy, with their excellent bio-compatibility and above average resistance to corrosion, have been widely used in the field of dentistry. However, the excessive oxidization of titanium which occurs during the process of firing on porcelain makes the bonding of titanium and porcelain more difficult than that of the conventional metal-porcelain bonding. To solve this problem related to titanium-porcelain bonding, several methods which modify the surfaces, coat the surfaces of titanium with various pure metals and ceramics, to enable the porcelain adhesive by limiting the diffusion of oxygen and forming the adhesive oxides surfaces, have been investigated. Purpose: The purpose of this study was to know whether the titanium-porcelain bonding strength could be enhanced by treating the titanium surface with gold and TiN followed by fabrication of clinically applicable porcelain-fused-to-titanium crown Material and method: The porcelain-fused-to-titanium crown was fabricated after sandblasting the surface of the casting titanium coping with $Al_2O_3$ and treating the surface with gold and TiN coating followed by condensation and firing of ultra-low fusing porcelain. To compare with porcelain-fused-to-titanium crowns, porcelain-fused-to-gold crowns were fabricated and used as control groups. The bonding strengths of porcelain-fused-to-gold crowns and porcelain-fused-totitanium crowns were set for comparison when the porcelain was fractured on purpose to get the experimental value of fracture strength. Then, the surface were examined by SEM and each fracturing pattern were compared with each other Result:Those results are as follows. 1. The highest value of fracture strength of porcelain-fused-to-titanium crowns was in the order of group with gold coating, group with TiN coating, group with $Al_2O_3$ sandblasting. No statistically significant difference was found among the three (P>.05). 2. The porcelain-fused-to-gold crowns showed the highest value in bonding strength. The bonding strength of crowns porcelain-fused-to-titanium crowns of rest groups showed bonding strength reaching only 85%-94% of that of PFG, though simple comparision seemed unacceptable due to the difference in materials used. 3. The fracturing patterns between metal and porcelain showed mixed type of failure behavior including cohesive failure and adhesive failure as a similar patterns by examination with the naked eye and SEM. But porcelain-fused-to-gold crowns showed high incidence of adhesive failure and porcelain-fused-to-titanium crowns showed high incidence of cohesive failure. Conclusion: Above results proved that when fabricating porcelain-fused-to-titanium crowns, treating casting titanium surface with gold or TiN was able to enhance the bonding strength between titanium and porcelain. Mean value of masticatory force was found to showed clinically acceptable values in porcelain bonding strength in all three groups. However, more experimental studies and evaluations should be done in order to get better porcelain bonding strength and various surface coating methods that can be applied on titanium surface with ease.

• Resources Recycling
• /
• v.19 no.5
• /
• pp.25-30
• /
• 2010

Leaching of CMSX-4 superalloy was done in hydrochloric acid solutions. The leaching behaviors of main alloy components, such as Ni, Co, Cr, Al, was investigated by controlling acid concentration, temperature, leaching time and pulp density. Increasing acid concentration enhanced the leaching rate till the rate decreased over 3 M acid concentration. Raising temperature increased the leaching amount of the metal components. After the leaching for 60 minutes at $90^{\circ}C$ and 10 g/L pulp density in 4 M acid solution, 93.2% nickel, 89.9% aluminum, 80.4% cobalt, and 79.1% chromium were leached. Nickel and aluminum were preferentially leached out, while the leaching rate of cobalt and chromium were relatively high only after 60 minutes, Increasing pulp density lowered the leaching rate and especially serious on cobalt and chromium, The optimum leaching condition for CMSX-4 was obtained at $90^{\circ}C$, 120 minutes, and less than 125 g/L in 4 M hydrochloric acid solution.

• Restorative Dentistry and Endodontics
• /
• v.8 no.1
• /
• pp.89-96
• /
• 1982

The purpose of this study is to identify the phases of four different types, low-copper lathe cut (Type II, class 1) and spherical (Type II, class 2) amalgam alloys which are made by Caulk company and high copper Dispersalloy (Type II, class 3) made by Johnson & Johnson and Tytin (Type I, class 2) made by S.S. White and to determine the Vickers hardness number on the individual phase and four different types of dental amalgam. After each amalgam alloy and Hg measured exactly by the balance was triturated by the mechanical amalgamator (De Trey), the triturated mass was inserted into the cylindrical metal mold which was 4 mm in diameter and 12mm in height and was pressed by the Instron Universal Testing machine (Model 1125) at the speed of 1mm/minute with 143$kg/cm^2$ according to the A.D.A. Specification No. 1. The Specimen removed from the mold, mounted and stored in the room temperature for 7 days. The speciman was polished with the emery paper from #220 to #1200 and finally on the polishing cloth with 0.3 and 0.05 um $Al_2O_3$ powder suspended in water. And then each specimen was etched by Allan's method and washed with Sodium Bisulfinite for 30 seconds. Finally differentiation and metallography on each phase were obtained by using metallographical microscope (Versamet, Union) and microhardness was obtained by using microhardness tester (MVH-2, Torsee). The results were as follows: 1. In the low-copper amalgam, the ${\gamma}$, ${\gamma}_1$ and ${\gamma}_2$ phase were observed and in the high-copper amalgam, the ${\gamma}$, ${\gamma}_1$. ${\epsilon}$ and ${\eta}$ phases were observed but ${\gamma}_2$ phase was not observed. 2. Among the microhardness of each amalgam phase measured under pressing a vickers diamond indenter with 2.0gm load for 30 seconds, e phase has the highest V.H.N (314 ${\pm}$ 20), and in low-copper amalgam 12 phase has the lowest V.H.N. (29${\pm}$1) and ${\eta}$ phase which was observed in high-copper amalgam has 230${\pm}$13 V.H.N and this phase is considerd to contribute to strengthen the handness in amalgam. 3. The V.H.N. measured under pressing a Vickers diamond indenter with 300.0gm load for 30 seconds in low-copper amalgam was lower than that of high-copper amalgam.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1994.10b
• /
• pp.15-15
• /
• 1994

M MA ODS 합금의 보다 폭넓용 실용확훌 위해 크게 요구되고 있는 적정 접합기술 개발의 한 방안￡로, 마찰압접(Friction Welding) 방법의 가능성옳 조사하기 위하여 마찰압력과 시간, 마 찰 후 접촉압력(Upset Pressure) 풍을 다양하게 변화시켜 접합체톨 제조한 후, 접합체 강도에 대한 인장시험과 접합계연의 결합 및 미세구조에 대한 현미경 관찰, EDS에 의한 원소분석, 접 합이옴부의 경도분포와 파단면 분석 풍율 행하였다. 실험에 사용된 모재는 기계적 합금법으로 제조된 Inca사의 Ni기 MA 754 합금이었으며, 직경 l 10 mm, 길이 50 mm로 가공한 후, 아세통￡로 초음파 세척하여 접합에 사용하였다. 접합온 브 레이크식 마찰압접기틀 사용하여 행하였으며, 회전시험편의 회전수는 2400 rpm이었A며, 다른 한쪽의 고정시험편과의 마찰압력 및 마찰시간온 각각 50 - 500 MPa과 1-5초로, 또한 업셋압 력도 50 - 600 MPa로 변화시켰다. 이때 업셋압력은 모든 시편에 대해 일정하게 6초동안 가하 였다. 얻어진 접합체는 각 압접조건 당 2개 이상의 접합시험편에 대해 상온 인장강도톨 측정하 였으며, 파단이 일어난 위치를 확인한 후 파면에 대한 분석율 주사전자현미경(SEM)과 에너지 분산형 분광분석기mDS)릎 사용하여 행하였다. 컵합이옴부의 첩합성올 확인하기 위하여, 접합 체를 접합변에 수직으로 절단, 연마한 후 광학현미경과 SEM, EDS 퉁으로 관찰, 분석하여 접 합부의 형상과 결합형성 여부, 접합계면의 미세조직 퉁옳 조사하였다. 또한 마찰압접에 따론 모재와 접합계연부의 경도분포훌 접합이옴부로부터 모재쪽으로 일정 간격율 두어 마이크로 비 커스 경도기로 측정, 조사하였다. 이상의 설험 결과, 다옴과 같온 결론옳 얻었다. ( (1) 접합체 강도가 모채 강도의 95% 이상이 되는 양호한 렵합체흩 얻기 위한 마찰압력 조건 온, 2400 rpm의 회전속도와 6초의 업셋압력 유지시간에서 마찰압력과 업셋압력, 그리고 마찰시 간이 각각 400 MPa 이상과 500 MPa 이상,2초입율 확인하였다. ( (2) 컵합이옴부의 관찰 결과, 모든 마찰압접 조건에서 컵합이옴부는, 기폰 모재의 texture 조직 을 유지하고 있는 모재부 영역(영역 ill)과 첩합계면부에 인접하여 업셋압력이 주어질 때 단조 효과에 의해 계연 외부로 metal flow가 일어나면서 형성된 영역 II, 매우 미세한 결정립으로 구성된 중앙부의 영역 1 로 이투어져 있옴융 확인하였다. ( (3) 최적접합조건이 충족되지 않온 경우, 접합부의 영역 I 에서 관찰된 void와 균열, 불균일한 접합계면 통의 접합결함에 Al과 Y. Ti 퉁￡로 구성된 산화물률이 용집되어 있옴을 확인하였 다-( (4) 접합체의 파단 양상온 크게 접합부 파단과 모재부 파단, 이률의 혼합형 파단i로 나눌수 있었다. 모재부 파단의 경우, 파단면이 매끄럽고 파변상의 결정립도 매우 미세하였으며, 산확물 의 용집도 찾아보기 어려웠 나, 접합부 파단의 경우에는 파변의 굴곡이 비교척 심하고 연성 입계파괴의 형태를 보였￡며, 결정립도 모채부 파단의 경우에 비해 조대하였다. 조대하였다.