• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.393-400
• /
• 2014

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.127-134
• /
• 2001

Misch metal (rare earth element, Ce, La, Nd, Pr) which has large influence on high-temperature stability and toughness was added to the Al-5%Ni-5%Mg alloy, and squeeze casting was used for Al-5%Ni-5%Mg-(Mm) alloys. The effect of applied pressure and misch metal additions on mechanical properties in Al-5%Ni-5%Mg alloy by direct squeeze casting has been investigated. The applied pressure were 0 MPa(gravity casting), 25, 50 and 75 MPa. Squeeze-cast Al-5%Ni-5%Mg-(Mm) alloys had better mechanical properties than those of non-pressurized cast alloys because of the increased cooling rate by the application of pressure during solidification. By the addition of misch metal in Al-5%Ni-5%Mg alloy, better combination of strength and elongation was obtained. The addition of 0.3%Mm in Al-5%Ni-5%Mg alloy improved the heat resistant property due to the formation of fine eutectic phases.

• Proceedings of the KSME Conference
• /
• 2007.05b
• /
• pp.2050-2054
• /
• 2007

This study numerically and experimentally investigated on thermal strain analysis of aluminum alloy casting mold using metal foundry. To predict the numerical result of thermal strain in Al alloy casting mold during the cooling process, it is performed the investigation of temperature distribution, stress and displacement based on the physical properties of Al alloy. In results of this study, Al alloy casting mold represented rapidly cooling graph during initial 20minutes after beginning cooling process, therefore value of stress and displacement is rapidly changed during initial 20minutes after beginning cooling process. In addition to, temperature distribution obtained by experiment confirmed corresponding pattern then compared numerical analysis with experiment. These results are distribute to make the effective and the high precision casting mold.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.1
• /
• pp.23-28
• /
• 2004

In this work, the effect of Sc and Mm(misch metal) on the high temperature behavior of Al-Mg alloys was observed. Hardness was increased due to appearance of fine $Al_3Sc$ precipitates. The elongation of Al-Mg-Sc alloy at high temperature was higher than that of Al-Mg-Sc-Mm alloy because Al-Mg-Sc alloy has finer grain sizes than Al-Mg-Sc-Mm alloy. The strain rate sensitivity factor, "m" of Al-Mg-Sc and Al-Mg-Sc-Mm at $475^{\circ}C$ and $1{\times}10^{-2}s^{-1}$ were 0.33 and 0.46, respectively. The activation energy of Al-Mg-Sc and Al-Mg-Sc-Mm alloy for superplastic deformation was 133KJ/mol and 103KJ/mol respectively. The elongation of Al-Mg-Sc alloy at high temperature was decreased by the addition of Mm, but the strength at high temperatures and low strain rate was improved.

• Journal of Advanced Marine Engineering and Technology
• /
• v.17 no.1
• /
• pp.66-72
• /
• 1993

The brazing of Al to Al using Al-Si alloy filler metal was performed under different bonding conditions such as ratio of lap length to plate thickness, surface roughness and joint clearance of the lap joint. The adopted thickness of the base metal in this experiments were two kinds of 4mm and 7mm which were most commonly used in various field. Influence of several bonding conditions of Al/Al joint was quantitavely evaluated by bonding strength test, and microstructural analysis at the interlayer were performed by optical microscope. From above experiments, the optimum bonding conditions of the brazing bonding of Al/Al using Al-Si alloy filler metal was determined. The major results obtained are as follows. 1) The fracture occurs at brazed joint in the conditions of that the ratio of lap length to plate thickness is less than 2 in case of 7mm plate thickness. 2) The ratio of lap length to plate thickness which the fracture occurs at base metal is decreased with the decreasing of the plate thickness. 3) The joint strength is not affected by the surface roughness and joint clearance of the brazed part. 4) The heat-treatment of the brazed joint contribute to eliminate the boundary between the base metal and filler metal. However, the joint strength is not affected by the heat-treatment.

• Journal of Korea Foundry Society
• /
• v.20 no.1
• /
• pp.29-37
• /
• 2000

The purpose of this study is to investigate the effect of misch metal addition on the microstructure and mechanical property of rapidly solidified AZ91 alloy by melt spinning process. As the contents of misch metal(rare earth element:Ce,La, Nd, Pr)was increased, the microstructure of RS ribbons and extrudates became finer than those of AZ91, and RE related phases($Al_{11}RE_3$, $Al_2RE$) were formed. At room temperature, the rapidly solidified AZ91+1 wt%Mm alloy showed the highest tensile strength, 430 MPa due to precipitation strengthening of${\beta}(Mg_{17}Al_{12})$ phase and Al11RE3 phase. At the elevated temperature, the mechanical property of AZ01+3 wt%Mm alloy was higher than those of other Mg alloys. The reasons were that $Al_{11}La_3$ phase was thermally stable and suppressed the grain growth. In contrast with $Al_{11}La_3$ phase, ${\beta}$ phase was thermally unstable and could not suppress the grain growth at the elevated temperature. Therefore, Al11RE3 phase contributed to improve the thermal stability of RS AZ91 Alloy.

• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.985-994
• /
• 1996

The initiation and growth of $\alpha$-Al2O3/metal composites by the directed oxidation of molten commercial AlZnMg-alloy at 1223-1423K were investigated. Spontaneous bulk growth did not occur on the alloy alone. but the uniform initiation and growth of the composite were obtained by putting a thin layer of SiO2 particles on the surface of the alloy. Without SiO2 the external surface of the oxide layer was convered by MgO and MgAl2O4. But with the SiO2 reaction initiate the porous ZnO layers were found on the growth surface. The higher process temperature yielded a lower metal content. The oxidation product of $\alpha$-Al2O3 was found to be oriented with c-axis parallel to th growth direction. The growth rates increased with temperature and the apparent activation energy was 111.8 kJ/mol.

• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.512-519
• /
• 2001

Sink roll has been used in molten Zn-0.2%Al alloy bath of continuous galvanizing line in sinking and stabilizing process of the steel strip in molten metal bath. In this process, although the scraper scraps off the sink roll surface, the dross compounds is builded up on the sink roll surface and the life time of the sink roll is shorten by the dross compounds. The present study was investigated the application of the spray coating layer on sink roll body for improving durability In molten Zn-0.2%Al alloy. Through the durability tests in molten Zn-0.2%Al alloy with various ceramic and cermet coating layer, the optimum bond and top coating material was obtained. As the results, the system of STS430F base metal, WC-l7Co bond and $ZrO_2-SiO_2$ top coating was clarified to be the best quality of durability in molten Zn-0.2%Al alloy.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.478-481
• /
• 1996

Disproportionation reaction is very important and interesting reaction to be applied to such surface treatment as metal, alloy, compound coating, a surface etching and so on. In gaseous system, the reaction of Al chloride is applied to Al and Al alloy coating, and the similar reaction of Ti chloride is also used for Ti, Ti alloy and Ti compound coating. As for aqueous system, this reaction is utilized to such metal coat as Sn etc. and metal etching such as Cu, Fe and so on. Also in molten salts system, this reaction has many application for surface treatment like metal, alloy and compound coatings for corrosion, wear, heat resistance and so forth. For instance, carbide film, nitride film, boride film, alloy film, quite new different film from the components of substrate material are coated in single and multiple component film system by the disproportionation reaction.

• Journal of Powder Materials
• /
• v.8 no.3
• /
• pp.157-162
• /
• 2001

An optimum route to fabricate the ferrous alloy dispersed $Al_2O_3$ nanocomposites such as $Al_2O_3$/Fe-Ni and $Al_2O_3$/Fe-Co with sound microstructure and desired properties was investigated. The composites were fabricated by the sintering of powder mixtures of $Al_2O_3$ and nano-sized ferrous alloy, in which the alloy was prepared by solution-chemistry routes using metal nitrates powders and a subsequent hydorgen reduction process. Microstructural observation of reduced powder mixture revealed that the Fe-Ni or Fe-Co alloy particles of about 20 nm in size homogeneously surrounded $Al_2O_3$, forming nanocomposite powder. The sintered $Al_2O_3$/Fe-Ni composite showed the formation of Fe$Al_2O_4$ phase, while the reaction phases were not observed in $Al_2O_3$/Fe-Co composite. Hot-pressed $Al_2O_3$/Fe-Ni composite showed improved mechanical properties and magnetic response. The properties are discussed in terms of microstructural characteristics such as the distribution and size of alloy particles.