• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1147-1155
• /
• 1996

• Journal of the Korean Ceramic Society
• /
• v.29 no.1
• /
• pp.23-28
• /
• 1992

Alumina ceramics was reinforced by in-situ formation of La-${\beta}$-aluminate in ${\alpha}$-alumina matrix. The powder mixture of which composition is (100-12x)Al2O3+x(La2O3+11Al2O3) was prepared for the formation of La-${\beta}$-aluminate in ${\alpha}$-alumina matrix. The amount of La-${\beta}$-aluminate in the matrix was controlled by varing x which is number of moles. The dense composite was produced by sintering at 1600$^{\circ}C$ in air or hot-pressing at 1550$^{\circ}C$ under 30 MPa. Bending strength and fracture toughness were increased, resulting from the grain growth inhibition and the crack deflection and crack bridging mechanism when La-${\beta}$-aluminate was produced in ${\alpha}$-alumina matrix.

• Journal of the Korean Ceramic Society
• /
• v.35 no.6
• /
• pp.551-558
• /
• 1998

Detection of microcrack in {{{{ {Al }_{2 } {O }_{3 } }} ceramics were studided by AE(acoustic emission) technique with 4-point bending test in order to evaluate the fracture process and formation of microcrack. Fully-dense alu-mina ceramics having a different grain size were fabricated by varing the hot-pressing temperature. The grain size of alumina increased with increasing the hot-pressing temperature whereas the bending strength decreasd. The microcracks were observed by SEM and TEM. The generation of AE event increased with increasing the applied load and many AE event was generated at maximum applied load. Alumina with smaller grain size shows the generation of many AE event resulting in an increase of microcrack formation. An intergranular fracture is predominantly observed in fine-grained alumina whereas intragranular fracture occurs predominantly in coarse-grained alumina,. Analysis of micorstructure and AE prove that primary mi-crocracks occur within grain-boundaries of alumina. The larger microcracking were formed by the growth and/or coalesence of primary microcracks. Then the materials become to fracuture by main crack gen-eration at the maximum applied load.

• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.379-385
• /
• 1999

Minute boehmite crystals with high aspect rations, which were hydrothermally synthesized from gibbsite in $Ba(OH)_2$ solution, occluded Ba with the Ba/Al molar ratio of about 0.03 in their interlayers. Their surface areas were about 14$\m^2$/g. The Ba-intercalated bohemite samples were partly used for producing $BaAl_{12}O){19}$ with low sinterability by externally supplementing $Ba(OH)_2$, and for forming transient aluminas. The surface area of $BaAl_{12}O){19}$ obtained by firing at $1500^{\circ}C$ for 3 h was 5.3$\m^2$/g, which was significantly lower than 12$\m^2$/g of the sol-gel origin. While a mixture ${\gamma}$-alumina and BaO is known to from $BaAl_{12}O){19}$ at $1200^{\circ}C$, solid state reaction between η-alumina transformed from the Ba-intercalated boehmite and BaO formed from $Ba(OH)_2$ deposited on the boehmite started above $1300^{\circ}C$. This suggests that large sized $Ba^{2+}$ ion occluded in η-alumina considerably suppresses the diffusion of $Al^{3+}$ ion. The surface area of the Ba-intercalated boehmite fired at $1400^{\circ}C$ for 3h was as high as 14$\m^2$/g indicative of its potential applicability to combustion catalysts. But it was decreased to 5.0$\m^2$/g after firing at $1500^{\circ}C$ for 3 h, accompanied by abrupt formations of $\alpha$-alumina and $BaAl_{12}O){19}$ as main products. The suppression of $\alpha$-alumina formation up to $1400^{\circ}C$ also suggests the significant blocking effect of $Ba^{2+}$ ion on the diffusion of the component ions.

• Applied Chemistry for Engineering
• /
• v.9 no.7
• /
• pp.1030-1035
• /
• 1998

The porous alumina membrane was prepared from aluminum metal(99.8%) by anodic oxidation using DC power supply of constant current mode in an aqueous solution of sulfuric acid. To prevent the chemical dissolution of alumina membrane, $Al_2(SO_4)_3$, $AlPO_4$ and $Al(NO_3)_3$ which could be considered to supply $Al^{3+}$ ions were added to electrolyte solution at a reaction temperature of $20^{\circ}C$ and cumulative charge of $150C/cm^2$. Effects of these additives on the formation of porous alumina membrane were evaluated under various electrolyte concentration(5~20 wt%) and current densities($10{\sim}50mA/cm^2$). The membrane surfaces which were prepared in electrolyte solution with all the additives except $Al_2(SO_4)_3$ were damaged. However, when $Al_2(SO_4)_3$ was added to the $H_2SO_4$ solution, an uniform surface of porous alumina was obtained. Also, it was shown that the pore size of membrane was nearly independent on the quantity of $Al_2(SO_4)_3$ added at same electrolyte concentration and current density.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.597-608
• /
• 1994

A new process for the production of high purity ${\alpha}-Al_2O_3$ from ammonium aluminium sulfate solution abtained through the sulfation of low grade bauxite ore with $(NH_4)_2SO_4$, and leaching of the sulfated product was investigated. This process is consisted of solvent extraction for Fe component removal from ammonium aluminum sulfate solution and homogeneous precipitation of Al containing precipitate from the refined ammonium aluminium sulfate solution by using urea as precipitator. The optimum conditions of solvent extraction with Alamine 336 as extractant were shaking time of 4min, organic phase ratio to aqueous phase of 0.25. The types of precipitation products from this precipitation were amorphous alumina gel, pseudo-boehmite and crystalline boehmite in the lower temperature of $100^{\circ}C$, in the range from $125^{\circ}C$ to $150^{\circ}C$, and above $150^{\circ}C$, respectively. And also amorphous alumina gel hydrate in $1000^{\circ}C$ and crystalline boehmite in $1250^{\circ}C$ were tranfered to ${\alpha}-Al_2O_3$, respectively. This alumina was identified as ${\alpha}-Al_2O_3$ of purity 99.7%.

• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.834-842
• /
• 1997

Controlled Ca impurity implanted inner crack-like pore in the high purity alumina single crystal, sapphire, had been created by micro-fabrication technique, which includes ion implantation, photo-lithography, Ar ion milling, and hot press technique. The morphological change and the healing of cracklike pore in Ca doped high purity single crystal alumina, sapphire, during high temperature heat treatment in vacuum were observed using optical microscopy. The dot-like surface roughening was developed and hexagon like crystal appeared on inner surface of crack-like pore after heat treatment. Bar type crystals, probably CaO.6Al2O3, were observed on the inner surface after 1 hour heat treatment at 1, 50$0^{\circ}C$, but this bar type crystal disappeared after 1 hour heat treatment at 1, $600^{\circ}C$. This disappearance means that there should be a little increase of Ca solubility limit to alumina at this temperatures.

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.939-945
• /
• 2004

Glasses of $SiO_2-B_{2}O_3-Al_{2}O_3-CaO-La_{2}O_3$ with various amounts of $La_{2}O_3$ were infiltrated into a porous alumina to make an alumina-glass composite. The infiltration characterization and bending strength of the composite were examined in terms of glass composition. $La_{2}O_3$ in the glass decreased the high temperature viscosity and this enhanced the wetting behaviour of this glass to alumina, and made glass infiltration easier. The infiltrated glass dissolved the alumina skeleton, and $Al_{2}O_3$ component in the glass melt reprecipitated on the alumina. The grain growth occurred to a specific crystal direction. The glass containing $20mole\%$ of $La_{2}O_3$ was crystallized after infiltration, and this enhanced the bending strength of the composite.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.638-645
• /
• 2009

High alumina refractory used in a coal gasifier was analyzed and the degradation mechanism by molten slag was investigated. The depth of refractory severely damaged by slag varied between 12~40 mm, including the adhered slag layer. The sample also showed the cracks formed in parallel to the slag/refractory interface. The degree of degradation varied with the micro-structures in the refractory. Fused alumina grains showed the uneven boundary and pore formation just along the edges, while the tablet alumina showed the slag penetrated between sintered alumina around which the formation of Al-Fe phase was observed. Calcium aluminate cements were not observed at the high temperature zone near the slag/refractory interface, probably due to dissolution into molten slag. Around large grains of alumina, rod shape alumina, which appeared to be recrystallized during cooling, were observed, and large pores were also formed around those grains. Therefore, in high alumina refractories, hot molten slag dissolves the bonding phase and rod-shape alumina phase is recrystallized upon cooling. During this process, cracks are developed due to structural change, and the degradation occurs by physical causes such as structural spalling.

• The Korean Journal of Ceramics
• /
• v.2 no.3
• /
• pp.142-146
• /
• 1996

The molten carbonate fuel cell matrices, which are usually made of high surface, fine particle size ${\gamma}-LiAlO_2$ are reinforced with coarse particles of the same material and alumina fibers. An the effects of reinforcing materials on pore characteristics, sintering properties and mechanical properties of the matrices are examined.Among the matrices examined, the highest mechanical reinforcement has been achieved in the one containing 10 wt.% coarse particles and 20 wt.% alumina fibers.