• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.231-236
• /
• 1988

In order to investigate the effect of second phase on $Al_2O_3$ matrix, SiC particles were dispersed in $Al_2O_3$ matrix as a second phase over the content range of 5 vol.% to 20 vol.%. To this mixture, $Y_2O_3$ or $TiO_2$ powders were added as a sintering additive before isostatically pressing and pressurelessly sintering at 180$0^{\circ}C$ for 90 min in $N_2$ atmosphere. With increasing SiC content, relative densities of composites were decreased but mechanical properties of composites were improvjed. In the case of adding $Y_2O_3$ as a sintering additive, maximum values of flexural strength, hardness and fracture toughness were 525 MPa, 17.1 GPa, 4.1 MPa.m1/2 respectively. In the case of adding X$TiO_2$ as a sintering additive, maximum values of flexural strength, hardness were 285 MPa, 12.1 GPa respectively. Improved mechanical properties were found to be the results of grain growth control of $Al_2O_3$ matrix and crack deflection by the second phase SiC particles.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.12
• /
• pp.1017-1024
• /
• 2000

Effect of the microwave dielectric properties and the microstructure on a mole fraction(x=0.1~0.9) of (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$ ceramics was investigated. When (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$(x=0.1~0.9) ceramics were sintered at 130$0^{\circ}C$, 135$0^{\circ}C$ and 140$0^{\circ}C$ for 2hr, the microwave dielectric properties were obtained $\varepsilon$r=6.8~8.3, Q.f$_{0}$=36000~77600. On the other hand, the temperature coefficients of resonant frequency($\tau$$_{f}$) were obtained in the properties of -62ppm/$^{\circ}C$ to -49ppm/$^{\circ}C$. In order to adjust the temperature coefficient of resonant frequency($\tau$$_{f}$), CaTiO$_3$was added in (1-x)Mg$_2$SiO$_4$-xZnAl$_2$O$_4$ceramics. 0.7Mg$_2$SiO$_4$-0.2ZnAl$_2$O$_4$-0.1CaTiO$_3$ceramics sintered at 135$0^{\circ}C$ for 2hr showed the excellent microwave dielectric properties of $\varepsilon$r=7.7, Q.f$_{0}$=32000, and $\tau$$_{f}$=-7.9 ppm/$^{\circ}C$.EX>.>.EX>.

• Korean Journal of Metals and Materials
• /
• v.50 no.9
• /
• pp.677-684
• /
• 2012

A feasible way to fabricate in-situ Al/TiC composites was investigated. An elemental mixture of $Al-TiO_2-C$ pellet was directly added into an Al melt at $800-920^{\circ}C$ to form TiC by self-combustion reaction. The addition of CuO initiates the self-combustion reaction to form TiC in $1-2{\mu}m$ at the melt temperature above $850^{\circ}C$. Besides the CuO addition, a diluent element of excess Al plays a significant role in the TiC formation by forming a precursor phase, $Al_3Ti$. Processing parameters such as CuO content, the amount of excess Al and the melt temperature, have affected the combustion reaction and formation of TiC, and their influences on the microstructures of in-situ Al/TiC composites are examined.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.438-445
• /
• 2002

In this study, the glass frit of $PbO-TiO-2-SiO_2-BaO-ZnO-Al_2O-3-CaO-B_2O_3-Bi_2O_3-MgO$ system was manufactured. The glass was melted at $1,400{\circ}C$, quenched and attrition-milled. The glass frit powder was pressed and fired for 2h at the range of $750~1,000{\circ}C$. The crystallization of glass frit began at about $750{\circ}$ and at low temperature, the main crystal phases were hexagonal celsian($BaAl_2Si_2O_8$) and alumina. As the firing temperature increased, the crystal phases of monoclinic celsian, zinc aluminate, zinc silicate, calcium titanium silicate and titania appeared. And the increase of firing temperature led to transformation of hexagonal celsian to monoclinic. The only glass frit containing 15wt% PbO had the crystal phase of solid solution of $PbTiO_3-CaTiO_3$. At the frequency of 1 MHz, the dielectric constant of glass frit crystallized was in the range of 11~16 and the dielectric loss less than 0.020. But the glass frit containing 15wt% PbO had the dielectric constant of 17~26 and loss of 0.010~0.015 because of crystal phase of solid solution of $PbTiO_3-CaTiO_3$.

• Journal of Industrial Technology
• /
• v.20 no.A
• /
• pp.239-245
• /
• 2000

Sintered $Al_2TiO_5$ has a very low thermal expansion and an infrared radiative selectively emitting large amounts of far infrared rays. However, it is week in mechanical strength. Spectral infrared emittance, thermal expansion coefficient, and mechanical strength of $Al_2TiO_5$-clay composites were studied to develop a material for far infrared radiators. The composites containing 10~50 mass% Jungsan clay had high emittance in the range of 2,000~500cm-1. The bending strength of the $Al_2TiO_5$-clay composites increased with increasing clay content. The $Al_2TiO_5$-clay composites with a clay content of 50mass% and heat-treated at $1,200^{\circ}C$ had a large strength for infrared radiators ; 86MPa. The average linear thermal expansion coefficient from $200{\sim}1,000^{\circ}C$ of the 50mass% jungsan clay containing compo sited heat-treated at $1,200^{\circ}C$ was lower than $3.87{\times}10-6/^{\circ}C$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.10
• /
• pp.4672-4678
• /
• 2013

Aluminum dross is formation at the surface of the molten metal as the latter reacts with the furnace atmosphere and it was an unavoidable by-product of the aluminum production process. However aluminum dross was usually landfilled or disposed without treatment, causing much environmental damage. The purpose of this study is to investigate the possibility of ceramic catalyst support using recycled Al dross. The recycled Al dross was made into SCR catalyst by mixing with $WO_3$, $V_2O_5$ and $TiO_2$. The $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR catalyst was observed with XRF, XRD and BET. $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR strength was measured by Universal Testing Machine(UTM). As the added $Al_2O_3$, streagth is increased. And the NOx removal activity was observed by MR(Micro-Reactor). The temperatures ranging from $350^{\circ}C$ and $400^{\circ}C$, $V_2O_5-WO_3/TiO_2-Al_2O_3$ SCR catalyst De-NOx performance result of showed excellent activity over 90% at application condition.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.552-560
• /
• 1994

A composite of TiB2-Al2O3 system was successfully prepared from a mixture of TiO2, B2O3, and Al by self-propagating high temperature synthesis (SHS) with a novel characteristic, utilizing the internal oxidation heat of aluminium metal of the mixture, instead of by a conventional technique, externally heating a mixture of Ti, B and Al2O3. From a mixture with B/Ti molar ratio of =2.0, pure two phases of TiB2 and $\alpha$-Al2O3 with good crystallinity and small, uniform sizes were formed. However, when the B/Ti molar ratio of the mixture goes to a value less than 2.0, in addition to the above main minerals, a small smounts of metastable phases such as TiB and Ti3B4 were formed. It was found that about 60%, the optimum green density of compacts gave their highest reaction rate and temperature during SHS process. TiB2-Al2O3 system composite with B/Ti molar ratio of =2.0 could be pressurelessly sintered even at 190$0^{\circ}C$ under Ar gas flows without any addition of sintering aids, showing their good properties such as 91.2% in relative density, 2750 kgf/$\textrm{mm}^2$ in Vickers hardness and 2620 kgf/$\textrm{cm}^2$ in flexural strength.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.161-161
• /
• 2012

결정질 TiCrN과 AlSiN 나노층이 교대로 구성하는 나노 다층 TiAlCrSiN 박막은 음극 아크 플라즈마 증착법에 의해 증착되었다. 나노 다층 TiAlCrSiN 박막의 산화특성들은 $600{\sim}1000^{\circ}C$사이에서 대기 중 최대 70시간동안 연구 되었다. 형성된 산화물들은 주로 $Cr_2O_3$, ${\alpha}-Al_2O_3$, $SiO_2$ 그리고 rutile-$TiO_2$들로 구성되었다. 나노 다층 TiAlCrSiN 박막이 산화하는 동안, 가장 바깥쪽의 $TiO_2$층은 Ti 이온의 외부확산에 의해, 외부 $Al_2O_3$층은 Al이온의 외부확산에 의해 형성되었다. 동시에, 내부($Al_2O_3$, $Cr_2O_3$) 혼합층과 가장 안쪽의 $TiO_2$층은 산소이온의 내부확산에 의해 형성되었다.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.398-402
• /
• 2000

Three kinds of $Al_3Ti-Cr$ alloys, namely, $Al_{67}Ti_{25}Cr_8,\;Al_{66}Ti_{24}Cr_{10}\;and\;Al_{59}Ti_{26}Cr_{15}$, were prepared by induction melting followed by the thermomechanical treatment. The corrosion behavior in 3.5% NaCl solution and the high-temperature oxidation behavior at 1000, 1100 and $1200^{\circ}C$ for the prepared alloys were investigated. Electrochemical results indicated increased resistance to localized corrosion with increasing Cr content. Cr additions were found to prevent passive film from undergoing brittle fracture. XPS results revealed the passive films of $Al_3Ti-Cr$ alloys were composed mainly of $Al_2O_3$ that coexisted with $TiO_2$ and $Cr_2O_3$. The overall oxidation resistance of the prepared alloys were excellent. Specifically, the oxidation resistance increased in the order of $Al_{59}Ti_{26}Cr_{15},\;Al_{66}Ti_{24}Cr_{10}\;and\;Al_{67}Ti_{25}Cr_8$. As the Al content in the base alloys increased, the $Al_2O_3$ formation was facilitated leading to the increased oxidation resistance.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.5
• /
• pp.235-244
• /
• 1993

The oxidation behavior of a two-phase(Ti3Al+TiAl) intermetallic compound, Ti-33.8wt%Al, has been in-vestigated in air at 800, 900 and $^1000{\circ}C$. Though the isothermal oxidation behavior followed a parabolic law up to 100$0^{\circ}C$ indicating that protective oxide scales were formed, the cyclic oxidation behavior followed a lin-ear law in the entire temperature range tested because flaky or stratified scales were usually spalled from the surface during cooling. During oxidation at 80$0^{\circ}C$, the alloy showed excellent oxidation resistance because continuous protective Al2O3 films were formed on the outermost surface of the alloy. However, above $900^{\circ}C$, the oxidation resistance of the alloy was decreased gradually because relatively non-protective TiO2 scales as well as some of Al2O3 scales were formed on the outer oxide scale. The oxidation mechanism of the alloy at different temperature was proposed.