• Corrosion Science and Technology
• /
• v.20 no.5
• /
• pp.315-323
• /
• 2021

In this study, we examined corrosion behaviors of two types of Pb alloys for a lead acid battery comparatively. One containing 6.6 wt% Sn, 36 mg/kg Bi, and 612.4 mg/kg Ca was prepared by twin-roll continuous casting. The other containing 5.2 wt% Sn, 30.5 mg/kg Ag, and 557 mg/kg Ca was made by twin-belt continuous casting. Potentiodynamic polarization tests were performed to evaluate corrosion resistance. Cyclic voltammetry was done to examine oxidation and reduction reactions occurring on the surface of each alloy in 4.8 M H₂SO₄ solution. Electrochemical test results implied that the Pb alloy prepared with the twin-belt casting method was less stable than that cast with the twin-roll method. Such results might be due to precipitations formed during the casting process. Rolling did not appear to affect the corrosion behavior of the twin-roll samples with Ag < 10 mg/kg, while it reduced the anodic reaction of Ag on the surface of the twin-belt sample with 30.5 mg/kg Ag.

• Journal of the Korean Magnetics Society
• /
• v.8 no.3
• /
• pp.131-137
• /
• 1998

The thickness dependence of the microstructure and the giant magnetoresistance behavior of co-evaporated Co-Ag granular alloy films were investigated. The maximum magnetoresistance ratio of 24% was observed in the the as-deposited state of the 40 at. % Co alloy having 200 nm thickness. The surface scattering contributed about 20% to the total resistivity in the 20 nm thick films. The MR ratio dropped sharply when the film thickness was below 50 nm. The reduction in the Co particle size and the increase in solid solubility of Ag in fcc Co when the film thickness decreased were observed using a high resolution TEM. The aspect ratio of the Co particles was also affected by the film thickness. Those microstructural changes as well as the surface induced spin flipping play a significant role in the $\Delta$p change.

• Korean Journal of Metals and Materials
• /
• v.47 no.8
• /
• pp.461-465
• /
• 2009

We study the diffusion of Ag based bimetallic nanoclusters supported on graphite. Using a molecular dynamics simulation, we reveal that the Ag clusters show rapid diffusion because of their hexagonal bottom layer. In order to decrease the rate of diffusion, we added Pt and Ni to distort the structure of the alloy cluster (i.e., the alloying method). We expected Pt to provide a stronger force on Ag atoms, and Ni to shorten the bond length and thereby change the structure of Ag cluster. However, the attempt was unsuccessful, because Pt and Ni atoms formed cores inside the Ag clusters. We therefore designed a collision system where large Ag clusters collide with small Pt or Ni clusters. Upon collision with Pt clusters, the diffusion showed little change, because Pt atoms are substituted at the Ag atomic site and form a perfectly ordered structure. The collision with Ni, however, deforms the bottom layer as well as the overall cluster structure and decreases diffusion. This outcome appoints toward the possibility of further application to the manufacture of durable nanocatalysts.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1994.10a
• /
• pp.18-19
• /
• 1994

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.268-270
• /
• 2001

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.8-8
• /
• 1998

• Journal of Climate Change Research
• /
• v.7 no.3
• /
• pp.231-236
• /
• 2016

Electrocatalytic reduction can produce useful chemicals and fuels such as carbon monoxide, methane, formate, aldehydes, and alcohols using carbon dioxide, the green house gas, as a reactant through the supply of electrical energy. In this study, tin-lead (Sn-Pb) alloy electrodes are fabricated by electrodeposition on a carbon paper with different alloy composition and used as cathode for electrocatalytic reduction of carbon dioxide into formate in an aqueous system. The prepared electrodes are measured by Faradaic efficiency and partial current density for formate production. Electrocatalytic reduction experiments are carried out at -1.8 V (vs. Ag/AgCl) using H-type cell under ambient temperature and pressure and the gas and liquid products are analyzed by gas chromatograph and liquid chromatograph, respectively. As results, the Sn-Pb electrodes show higher Faradaic efficiency and partial current density than the single metal electrode. The Sn-Pb alloy electrode which have Sn:Pb molar ratio=2:1, shows the highest Faradaic efficiency of 88.7%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.235-238
• /
• 2000

There have been a lot of studies to improve the characteristic of Bi-2223 tape by PIT method which is considered as one of the best way for applying superconductor. These improved characteristic of Bi-2223 tape is able to be acqured by control of mechanical deformation and heat treatment. In this work, we studied HTS tapes with the sheath(Ag and Ag-alloy)of tapes that affect mechenical strength and critical current, with each two kind of purity(99.9% and 99.999%) and with two kind of tapes(single and double concentric). These charateristics affect Jc of tapes seriously that is the most important factor of superconductor tapes.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.103-117
• /
• 1997

The purpose of this experiment was to determind whether the gold electrodeposit on Pd-Ag and Ni-Cr alloys influences on the shear bond strength between veneering resin and silicoated metal surface. All the metal specimens were sandblasted with $250{\mu}m$ aluminum oxide and followed by silicoating and resin veneering. According to the metal surfaces to be veneered, experimental groups were divided into five. Group Prec : Gold alloy without gold coating Group Semi : Pd-Ag alloy without gold coating Group Base : Ni-Cr alloy without gold coating Group Semi-G : Pd-Ag alloy with gold coating Group Base-G : Ni-Cr alloy with gold coating All specimens were thermocycled 1,000 times at temperature of $5^{\circ}C$ to $55^{\circ}C$. The effects of gold electrodeposit on the shear bond strength between resin and metal interface were measured and fractured surface of the resin veneered metal was examined under the scaning electron microscope. The following results were obtained 1. The shear bond strength between resin and metal was $64.51{\pm}11.11Kg/cm^2$ in Prec group, $62.77{\pm}11.23Kg/cm^2$ in Base group and $58.97{\pm}9.20Kg/cm^2$ in Semi Group. There was no significant difference among the groups. 2. The bond strength in groups Semi-G and Base-G decreased about 17%, compared to the nongold-electrodeposit groups(Semi, Base). 3. In groups of non electrodeposit(Prec, Semi, Base), fracture occurred at the interface between alloy and resin, while fracture interface was observed between gold coating and resin in group Semi-G, and between metal substrate and gold coating in group Base-G respectively.

• Korean Journal of Metals and Materials
• /
• v.47 no.10
• /
• pp.605-612
• /
• 2009

The suitability of twin roll strip casting for Ag-27.5%Cu-20.5%Zn-2.5%Mn-0.5%Ni brazing alloy (known as HS-49D) was examined in the present work and the mechanical properties and microstructure of the strip were also investigated. The effect of annealing heat treatment on the properties was also studied. The new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analyses of the Ag-27.5%Cu-20.5%Zn-2.5%Mn-0.5%Ni strip revealed a eutectic microstructure of an Ag-rich matrix (FCC) and a Cu-rich phase (FCC) regardless of heat treatment. The results of mechanical tests showed tensile strength of 434 MPa and 80% elongation for the twin roll casted strip. Tensile results showed decreasing strengths and increasing elongation with annealing heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.