• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.506-513
• /
• 2020

In this study, the mechanical properties, absorption, and reduction performance of NOx in the mortar containing mineral admixture like zeolite and active hwangtoh were evaluated. Zeolite and active hwangtoh were used as binder, and zeolite and active hwangtoh were substituted for cement. The substitution ratio of two types of mineral admixtures was considered as 20 and 30% respectively. As a result of evaluating the compressive strength and flexural strength of each mortar specimen, the highest strength in the plain mixture was evaluated. As the substitution ratio of zeolite and active hwangtoh increased, the compressive and flexural strength decreased. In addition, the difference of compressive and flexural strength between active hwangtoh and zeolite mixing was evaluated to be insignificant. To evaluate the absorption rate, the mixture was designed to lower the W/B ratio of the existing mixture and set the substitution ratio of active hwangtoh and zeolite at 25%. The highest absorption ratio in the mortar with zeolite was evaluated, and the difference in absorption ratio between the remaining two mortar mixtures was small. The assessment of reduction performance of NOx considering the application of photocatalyst showed a clearly decreasing reduction behavior, even if they were the same mortar mixture. Zeolite and active hwangtoh also showed a higher NOx reduction than the Plain mixture, because of their porosity properties. In the case of active hwangtoh, the absorption ratio was lower than that of zeolite mixture, but the reduction of NOx performance was better than the result of zeolite mixture.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.520-527
• /
• 2020

Hwangtoh is the rich resource that accounts for about 15.0% of the domestic soil, and can be used as the admixture of concrete with Pozzolan characteristics if activated by rapidly freezing after burning with high temperature. In this study, the mortar curbs containing active hwangtoh were produced, based on the mixture for the mortar curbs sold on the market. The substitution rate of active hwangtoh were considered 10.0% and 25.0%, and the test items were selected to compressive and flexural strength tests, freezing/thawing resistance tests, accelerated carbonation tests, and accelerated chloride diffusion tests. In the results of the mechanical performance, it was showed that the highest strength was evaluated in OPC mixture, and the increase in strength was small by the increase of age, which was believed to be due to the fact that most of the strength in each mixture was created in three days of steam curing. The results of the freezing/thawing tests for 28 aged days showed the reduction rate of compressive strength was 85.0% or higher for all specimen, meeting the criteria presented. The accelerated carbonation tests were carried out on the specimen at 28 days of age, and the results showed that the mortar with active hwangtoh had lower carbonation resistance performance than mortar with OPC. The passed charge of each mixture was assessed in accordance with ASTM C 1202 on 28 and 91 aged days. The OPC mixture had "Low" rate and the mortar with active hwangtoh had "Moderate" rate. So it was thought that the mortar with active hwangtoh had appropriate resistance performance for chloride attack.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.405-412
• /
• 2019

In this study, the physical and chemical properties of mortar are evaluated by micro-analysis, taking into account the substitution rate(20%, 30%, and 40%) of zeolite with porous properties and active hwangtoh. First, the physical and chemical properties of zeolite and active hwangtoh are reviewed to confirm that the specific surface area of those is similar with ordinary portland cement, and the main chemical composition is SiO₂, Al₂O₃, Fe₂O₃, etc.. So, it is thought that they have the properties of pozolan reactive materials. As the results of the strength test considering the amount of substitution based on that of cement, It is confirmed that strength decreases with the increase of the replacement amount of zeolite and active hwangtoh, and the strength of mortar with replacement rate of 20% is higher than OPC mortar. It is confirmed that the amount of porosity is increased due to chemical properties of zeolite and active hwangtoh, and in particular, the size of the pore is greater than 1㎛ in mortar mixed with active hwangtoh.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.483-489
• /
• 2020

Particulate matter is divided into PM10 (particle diameter of 10 ㎛ or less) and PM2.5 (particle diameter of 2.5 ㎛ or less), which are approximately 1/5 of the thickness of the hair. Due to its effect on the human body, lung disease, arteriosclerosis and heart It is known as a carcinogen that causes various diseases such as diseases. It is known that the main cause of such fine dust is nitrogen dioxide (NOx), which is emitted from automobiles in about 57.3% of urban roadsides. Therefore, in this study, as part of the development of functional construction materials to reduce NOx generated from road transport pollutants, comparative evaluation of NOx reduction performance was conducted according to the replacement rate of cement mortar in which cement was replaced with a porous material. In addition, the NOx reduction performance of cement mortar according to the photocatalyst application method and the number of applications was compared an d evaluated. As a result of the experiment, when activated ocher was substituted by 30%, it showed a reduction effect of about 32.7%, showing the best reduction performance.