• Macromolecular Research
• /
• v.17 no.11
• /
• pp.879-885
• /
• 2009

A macroazoinitiator (MAI) containing a poly(ethylene glycol) (PEG) segment was intercalated in the gallery of sodium montmorillonite (Na-MMT). Acrylic monomers were polymerized using this MAI intercalated in Na-MMT to prepare the acrylic copolymer nanocomposite (AN), which is a multiblock copolymer composed of two segments, an acrylic copolymer and PEG intercalated in Na-MMT (Na-MMT/PEG). When AN was used to modify the reactive hot melt polyurethane adhesive (RHA), the acrylic copolymer segment and Na-MMT/PEG synergistically enhanced the initial bond strength evolution and reduced the set time, even when the amount of Na-MMT in RHA was < 1 wt%. The viscosity of RHA increased and the tensile properties of the cured RHA film decreased due to modification with AN. These variations were more evident as the Na-MMT content in AN was increased.

• Applied Chemistry for Engineering
• /
• v.7 no.4
• /
• pp.679-690
• /
• 1996

Acrylic copolymer was synthesized from 2-dimethylaminoethyl methacrylate and alkylmethacrylate containing long chain hydrocarbon group. To facilitate emulsification in water, acrylic copolymer was treated with acetic acid, and therefore acetated acrylic copolymer was produced. Acetated acrylic copolymer was perfectly emulsified in water and showed increased emulsion stability. Polymer as a cement dispersion agent(PDCM-PSD) was prepared by blending the newly synthesized acetates acrylic copolymer with sodium gluconate, oleic acid, and triethanolamine. The applicability of the blended polymer was examined, and it was found that the effects of dispersion and water-proof(0.3~0.5) were excellent.

• Journal of the Korean Home Economics Association
• /
• v.46 no.6
• /
• pp.13-19
• /
• 2008

In this paper, the dyeing ability of the volcanic ash dyeing on cotton knitted fabrics were investigated. Acrylic copolymer was used to improve the depth of fabric color in the dyeing process. K/S values of dyed fabrics were measured to examine the dyeing properties. Two different classes of dyeing process were tested; (1) volcanic ash dyeing after pretreatment and (2) simultaneous co-treatment with volcanic ash and acrylic copolymer. In the first process, the effects of parameters such as the concentration of volcanic ash, concentration of Na2S04, dyeing time, dyeing temperature and pH of dyebath were noted. In the second process, the effects of parameters such as concentration of acrylic copolymer, dyeing time and temperature, and drying temperature were noted. Experimental results showed that the co-treatment of acrylic copolymer improved the dyeing properties of cotton knitted fabrics with volcanic ash. For the first dyeing experiment, concentration of dispersing agent was 0.1%, concentration of volcanic ash was 4%, treatment time was 20minutes, concentration of $Na_2SO_4$ was 2%, treatment temperature was $60^{\circ}C$ and treatment pH of dyebath was neutral. In the second dyeing experiment, concentration of acrylic copolymer was 2%, treatment temperature was $80^{\circ}C$, treatment time was 40 minutes, and treatment drying temperature was $150^{\circ}C$.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.111-116
• /
• 2010

The treatment of heavy metal, in the waste ash from incinerator and mine solid waste, by using alkali-soluble acrylic copolymer emulsion, that is effective in the absorption of heavy metal has been studied. It seemed that alkali soluble acrylic copolymer emulsion was very effective in the absorption of Hg, Pb, Cd and Cu in this test. Also, eco-friendly thixotropic grout, using alkali soluble acrylic copolymer emulsion, that is effective in the absorption of heavy metal, for the recycling of waste ash from incinerator and mine solid waste has been tested. It was observed that waste ash could be used as a raw material of eco-friendly thixotropic grout mortar due to the effectiveness of alkali soluble acrylic copolymer emulsion in the fixation of heavy metals including $Cr^{6+}$ from waste ash in this test.

• Journal of the Korean Applied Science and Technology
• /
• v.13 no.3
• /
• pp.83-94
• /
• 1996

EMA-co-DAMA were synthesized from 2-diethylaminoethyl metacrylate and ethylhexyl metacrylate in acrylmonomer. To facilitate water emulsification, acrylic copolymer was cationized by acetic acid to produce acetated acrylic copolymer. The structures of the synthesized copolymer and acetated copolymers were confirmed by IR, NMR, and molecular weight was measure by GPC, and C.H.N elemental analysis. Acetated acrylic copolymers were perfectly emulsified in water and showed increased emulsion stability. Polymer dispersion for cement modifier[(PDCM-PED) water proof agent of cement for concrete in building construction] was prepared by blending of the guaternized acrylic copolymer syndisized above, sodium silicate, sodium gluconate and oleic acid emulsion. The result with prepared polymer dispersion of cement modifier was examined, and it was found that excellent waterprooffing effect ; Water permeability ratio is 0.50 under the water pressure of $100g/cm^2$ and 0.60 under $3kg/cm^2$, and water absorption ratio is $0.42{\sim}0.50$ and $1.0{\sim}1.02$ compressive strength ratio at mixed of water/PDCM-PED is 50 times.

• Macromolecular Research
• /
• v.12 no.6
• /
• pp.593-597
• /
• 2004

A new ionomeric polymer-metal composite (IPMC) was prepared using a cast membrane of acrylic copolymer, which was synthesized by radical copolymerization of fluoroalkyl acrylate and acrylic acid (AA). To examine its performance as a new electroactive polymer, the current and displacement responses to a step voltage applied across the IPMC were measured. The largest responses were observed when the AA content in the copolymer was $10.6\;wt\%$.

• Journal of Adhesion and Interface
• /
• v.10 no.3
• /
• pp.134-140
• /
• 2009

The acrylic copolymers with variation in side chain were synthesized based on molecular design. Wettability and adhesion properties on the wafer surface were investigated for these acrylic copolymer pressure sensitive adhesives. Three-dimensional networks of linear acrylic copolymers were produced with epoxy-type Tetra-DX cross-linking agent. The effect of cross-linking on adhesion characteristics was investigated. The side chain of acrylic copolymer played more important role in wettability than the interfacial interaction. As the degree of cross-linking increased, both probe tack and peel strength decreased. Also, heat resistance measured by SAFT increased with cross-linking; however, it showed the deterioration when excess cross-linking agent was added.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.31 no.1
• /
• pp.79-88
• /
• 1999

The stability and performance (peel strength) of the acrylic copolymer and various modified rosin systems were investigated. The peel strength was measured over a wide range of scaling rates, and the influence of the viscoelasticity of the PSA(pressure sensitive adhesive) was considered. In the case of miscible systems, the peak of peel strength (PSA performance) over wide peel rates was changed and modified systematically with increasing glass transition temperature of the blends. The peak of the peel strength for blended systems shifts toward the lower rate side as glass transition temperature ($T_g$) of the blend increased. The influence of esterification of the rosin on performance and stability against deterioration was greatly modified by blending with rosin of glycerol ester and rosin pentaerythritol ester. The failure mode of the blend varies with the combination with acrylic copolymer and modified rosin, and cohesive failure was found at a lower peel rate while interfacial failure was found at a high peel rate. A few systems where a single Tg could be measured, despite the fact that two phases were observed microscopically, were detected.

• Polymer(Korea)
• /
• v.24 no.4
• /
• pp.469-476
• /
• 2000

The miscibility between acrylic copolymers and tackifier resins influenced on adhesion properties of PSA. PSA with high molecular weight and narrow molecular weight distribution of acrylic copolymers showed systemical modification of adhesion properties of PSA by tackifier resins only in case of miscible system. It is concluded that the investigation of the miscibility between two Components is very important to adhesion properties of PSA.

• Polymer(Korea)
• /
• v.29 no.5
• /
• pp.463-467
• /
• 2005

In order to enhance the actuation force of ionic polymer-metal composite (IPMC) made with the acrylic copolymer of fluoroalkyl methacryate, acrylic acie, and 2-hydroxyethyl methacrylate(HEMA), the hydroxy group of HEMA was corsslinked with 1,3-diethoxy-1,1,3,3-tetramethyldisiloxane. The water uptake was reduced and the mechanical strengths and the actuation force of the membrane was improved by crosslinking. However, current and deformation responses of IPMC were decreased by crosslinking.