• 한국전기전자재료학회논문지
• /
• 제24권2호
• /
• pp.121-125
• /
• 2011

Ribbon silicon solar cells have been investigated because they can be produced with a lower material cost. However, it is very difficult to get good texturing with a conventional acid solution. To achieve high efficiency should be minimized for the reflectance properties. In this paper, acid vapor texturing and anti-reflection coating of $SiN_x$ was applied for EFG Ribbon Si Wafer. P-type ribbon silicon wafer had a thickness of 200 ${\mu}m$ and a resistivity of 3 $\Omega-cm$. Ribbon silicon wafers were exposed in an acid vapor. Acid vapor texturing was made by reaction between the silicon and the mixed solution of HF : $HNO_3$. After acid vapor texturing process, nanostructure of less than size of 1 ${\mu}m$ was formed and surface reflectance of 6.44% was achieved. Reflectance was decreased to 2.37% with anti-reflection coating of $SiN_x$.

• 공업화학
• /
• 제24권1호
• /
• pp.31-37
• /
• 2013

텍스쳐링에 의해 실리콘 웨이퍼의 표면반사율을 감소시키는 것은 실리콘 태양전지의 효율향상을 위해 매우 중요한 공정이다. 본 연구에서는 에칭속도 제어를 위해 촉매제를 포함한 산 용액으로 텍스쳐링 처리한 웨이퍼의 표면효과와 그 태양전지 특성을 평가 고찰하였다. 텍스쳐링 전 $HNO_3-H_2O_2-H_2O$ 용액의 전처리는 표면반사율의 초기 저감효과를 가져왔다. 이는 산화특성에 의해 유기 불순물이 제거되고 텍스쳐링을 위한 핵의 생성에 기인한다고 할 수 있다. 이후 공정에서 불산/질산 용액에 인산 및 초산과 같은 완충제를 첨가한 혼합용액을 제조하고, 적정 농도 조합과 그 처리시간의 최적화를 통해 개선된 텍스쳐링 효과를 얻을 수 있었으며 이 효과는 표면반사율 감소를 통해 확인할 수 있었다. 이렇게 제조된 실리콘 웨이퍼에 반사방지막 코팅 후 태양전지를 제작하여 그 변환효율을 측정한 결과 16.4%의 양호한 특성을 나타냈다. 이는 개선된 텍스쳐링 처리에 의해 저감된 표면특성에 의한 단락전류의 증가에 기인한 것으로 추정된다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.280-284
• /
• 2004

Multicrystalline silicon wafers were textured in an alkaline bath, basically using sodium hydroxide and in acidic bath, using mainly hydrofluoric acid (HF), nitric acid $(HNO_3)$ and de-ionized water (DIW). Some wafers were also acid polished for the comparative study. Comparison of average reflectance of the samples treated with the new recipe of acidic solution showed average diffuse reflectance less than even 5 percent in the optimized condition. Solar cells were thus fabricated with the samples following the main steps such as phosphorus doping for emitter layer formation, silicon nitride deposition for anti-reflection coating by plasma enhanced chemical vapor deposition (PECVD) and front surface passivation, screen printing metallization, co-firing in rapid thermal processing (RTP) Furnace and laser edge isolation and confirmed >14 % conversion efficiency from the best textured samples. This isotropic texturing approach can be instrumental to achieve high efficiency in mass production using relatively low cost silicon wafers as starting material.