• 한국해양공학회지
• /
• 제6권2호
• /
• pp.76-84
• /
• 1992

In this study, corrosion fatigue test of SAPH45 steel was performed by the use of plane behavior of base metal (BM) and heat affected zone (HAZ) of SAPH45. The main results obtained are as follows: 1) The more aspect ratio (b/t) of corner crack decreases, the more aspect ratio (b/a) takes greatly effect by corrosion. 2) The correlation between the stress intensity factor range ($\Delta$k) and crack growth rate (da/dN) for weldment in seawater is given by Paris rule as follow: da/dN=C($\Delta$K) super(m). Where m is constant, and the value is 3.82-3.84. 3) The accelerative factor ($\alpha$) of BM and HAZ under seawater is about 1.1-1.9, and ($\alpha$) of HAZ increases more and more under the low $\Delta$K region. 4) HAZ is more susceptible to corrowion than BM because of potential of electrode (E sub(c)) of HAZ becomes more less noble potential than that of BM.

• 수산해양교육연구
• /
• 제9권2호
• /
• pp.198-208
• /
• 1997

Recently, with rapid increase of gas demand, there occurs much interest their security of safety in the gas storage tanks and pressure vessels etc. In order to solve the problems, the occurrence of corrosion fatigue crack and the propagation behavior must be investigated. Especially the occurrence of corrosion fatigue crack and the propagation behavior in the part which has concentrated stress or defects, must be studied more carefully. In this paper, the high-tensile steel of SPV 50 which is much used for building the LPG storage tanks was tested by the use of a plane bending corrosion fatigue tester under the various marine environment and in the air. These experiments were carried out to investigate the surface crack propagation behavior, the value of experimental constant for Paris' rule(da/dN=$C(K)^m$), the crack depth propagation rate and the accelerative factor of the surface crack propagation rate. The main results obtained are as follows ; 1) As the specific resistances of marine environment decreases, the exponential value of slope m of Paris' rule(da/dN=$C(K)^m$) decreases and the value of intercept C increases. 2) The surface crack propagation rate and the crack depth propagation rate are delayed, as the specific resistances of marine environment is increased. 3) The accelerative factor of the surface crack propagation rate by corrosion fatigue is higher, according as the stress intensity factor range ${\Delta}K_A$ is small.

• Journal of Advanced Marine Engineering and Technology
• /
• 제15권1호
• /
• pp.51-58
• /
• 1991

Corrosion fatigue test was performed by the use of plane bending fatigue tester in marine environment having various specific resistance from 25(natural sea water) to 5000.ohm.cm. It is in order to investigate the effects of marine environmental factor on the corrosion fatigue fracture of SS41 steel. The main results obtained are as follows; 1. The aspect ratio(b/a) of corner crack growing in natural sea water is lower than that in air. 2. The surface crack growth rate(da/dN) in marine environment is faster than that in air and da/dN delaies with the specific resistance increased. 3. The experimental constant m of paris rule [da/dN=C(${\delta}$K)$^m$] decrease with the specific resistance decreased and the effect of corrosion in proportion to the specific resistance is more sensitive than that of stress intensity factor range(${\delta}$K) under region II. 4. The accelerative factor(${\alpha}$) in marine environment is about 1.1-2.7 and .alpha. is increase under the low region of stress intensity factor range(${\delta}$K). 5. The electrode potential($E_0$) gets less noble potential with the specific resistance decreased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 제2회 학술대회 논문집 일렉트렛트 및 응용기술전문연구회
• /
• pp.25-28
• /
• 2000

In this paper, the technology for accelerating degradation & life estimation on the traction motor was introduced with the stator form-winding sample coils of the 200 Class insulation system The accelerative degradation was performed in 10 cycles, which were composed of thermal stress, fast rising surge voltage, vibration, water immersion and overvoltage applying. After aging of 10 cycles, condition diagnosis test such as insulation resistance & polarization index, capacitance & dielectric loss and partial discharge properties were investigated in the temperature range of $20{\sim}160^{\circ}C$. Relationship between degradation conditions and diagnosis results were analyzed to find an dominative degradation factor at the end-life point

• 수산해양기술연구
• /
• 제28권3호
• /
• pp.286-294
• /
• 1992

In this paper, the corrosion fatigue crack propagation behavior of structure rolled steel (SWS 41C) was investigated by changing the thickness, and this experiment was done by the three point bending corrosion fatigue tester. The main results obtained are as follows: 1) As the thickness of specimen becomes thicker, the corrosion sensitivity to initial stage crack becomes some sensitive, and that the fatigue life becomes more sensitive. 2) The crack growth rate to initial stage crack (da/dN) was retarded as the thickness of specimen becomes thicker. But after initial stage crack, as the thickness of specimen is more thicker, da/dN is more rapid. 3) As the corrosion fatigue crack length grows, the accelerative factor of thick specimen (t=12mm) is more higher than that of thin specimen (t=6mm). 4) As the corrosion fatigue crack length grows, the corroson potential of both thick specimen and thin specimen becomes more less noble potential, however thick specimen (t=12mm) tends to more less noble potential than that of thin specimen(t=6mm).

• 한국전기전자재료학회논문지
• /
• 제15권1호
• /
• pp.93-101
• /
• 2002

In this study, the stator form-winding sample coils based on silicone resin and polyimide were made for fault prediction and reliability estimation on the C-Class(200$\^{C}$ ) insulation system of traction motors. The complex accelerative degradation was periodically performed during 10 cycles, which was composed of thermal stress, fast rising surge voltage, vibration, water immersion and overvoltage applying. After aging of 10 cycles, the condition diagnosis test such as insulation resistance '||'&'||' polarization index, capacitance '||'&'||' dielectric loss and partial discharge properties were investigated in the temperature range of 20 ∼ 160$\^{C}$. Relationship among condition diagnosis tests was analyzed to find a dominative degradation factor and an insulation state at end-life point.

• 전기학회논문지P
• /
• 제53권3호
• /
• pp.148-151
• /
• 2004

For turn on high pressure sodium vapor lamp, Starting Voltage is very important factor. This starting voltage supply to high pressure sodium vapor lamp as electric discharge lamp, Electric field is producted in electric discharge tube, So accelerative electron collide against vapor atom and second electron is generated, And rapidly the current flow to electric discharge tube. This starting voltage is high voltage and source for melting contact that relay is according as turn on/off high pressure sodium vapor lamp. Consequently, This paper propose that the prevention of melting contact in accordance relay of controller for turn on/off high pressure sodium vapor lamp.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.763-766
• /
• 2000

In this paper, stator form-winding sample coils based on silicone resin and polyimide were made for fault prediction and reliability estimation on the 200 Class insulation system of traction motors. The complex accelerative degradation was performed by periods during 10 cycles, which was composed of thermal stress, fast rising surge voltage, vibration, water immersion and overvoltage applying. After aging of 10 cycles, condition diagnosis test such as insulation resistance & polarization index, capacitance & dielectric loss and partial discharge properties were investigated in the temperature range of 20∼160$^{\circ}C$. Relationship among condition diagnosis test was analyzed to find an dominative degradation factor and an insulation state at end-life point.