• Journal of the Korean Wood Science and Technology
• /
• v.36 no.3
• /
• pp.47-54
• /
• 2008

To make up original defects of the wooden materials for decks, and to supply the wooden material for outdoor, we fabricated preservative treated plywood(PTP). Copper azole (CUAZ-1) preservative was treated with a normal full-cell process. Bond Strength of PTP was not affected after the preservative treatment. The anti-fungal efficiency and dimensional stability were obtained from PTP. A little discoloration of the surface was detected, but the dimensional change or peel bonded area off were not observed after accelerated weathering test. Although some strength of PTP was reduced after 17 months of field exposure, the PTP should be applicable for outdoor applications.

• Journal of Adhesion and Interface
• /
• v.24 no.2
• /
• pp.69-75
• /
• 2023

Recently, the application of paint protection films (PPFs) for automobiles having a self-recovery coating layer has been grown up. In this study, we report the evaluation results on the basic physical properties of a poly(vinyl chloride)- based PPF containing poly(urea-urethane) hybrid self-recovery coating layer. Depending on the main chemical composition and the thickness of poly(urea-urethane)-based coating layer for PPF, the self-recovery performance by an optical microscope and the stain resistance through color difference value are measured. To improve the surface properties and show its easy-cleaning effect against the polluted things, silicone-modified polyacrylate is introduced to the self-recovery coating composition. The contact angle of water on the coated surface is confirmed to show its hydrophobic surface. Finally, accelerated weathering test of paint protection film with poly(urea-urethane) hybrid coating layer is performed to check the possibility of discoloration and deformation due to long-term exposure on harsh condition.

• Journal of the Mineralogical Society of Korea
• /
• v.28 no.2
• /
• pp.135-145
• /
• 2015

In order to predict the deterioration of stone monument due to acid fog, an artificial fog test using pH4.0 and pH5.6 was applied to the Gyeongju Namsan granite, decite and marble. After the test had weathered Gyeongju Namsan granite a larger weight reduction due to acid fog than fresh one. Decite has shown the most significant changes among the tested rocks with about 0.005 % of weight reduction. Decite and weathered granite will have considerable weight reduction due to acid rain than the acid fog, whereas the marble was expected to show a weight reduction regardless of the phase of water. The porosity and water absorption rate of weathered granite had significantly increased. This result means that the weathered rock is predicted to be more susceptible to acid fog than the fresh rock. The absorption rate of the marble after the test had shown approximately 50 % increase. The color of the samples had slightly changed towards yellow, such tendency was greater shown in weathered rocks. The marble reacted with acid fog had an increased whiteness. A large amount of cation in the samples is caused mainly by the dissociation of minerals through the reaction with acid fog.

• Journal of the Mineralogical Society of Korea
• /
• v.29 no.4
• /
• pp.179-190
• /
• 2016

X-ray diffraction analysis, chromaticity measurement, execution and evaluation by Dancheong artisan, accelerated weathering test, and fire resistance test were conducted to test the applicability as a Dancheong pigment raw materials of Korean low grade kaolin in cultural properties. The ores that feldspar rich and composed of fine particles (< $38.1{\mu}m$) showing advantageous for the inherent purpose of the white pigment than that of high grade kaolin. And the test of whiteness, concealment force, outdoor exposure durability and fire resistance shows similar or better result than existing products (Hobun and Sanhwa jidang). In conclusion, it is expected that the use of fine feldspar rich white soil and low-grade kaolin can be used as a white pigment raw materials which have similar to better material properties and economic efficiency than existing products.

• Journal of Conservation Science
• /
• v.25 no.4
• /
• pp.373-381
• /
• 2009

To preserve steel cultural properties on display outdoors, the surface of these relics is processed with a covering treatment, which is a typical anti-corrosion method. Since the registered cultural heritage of Korea No. 78 Locomotive at Jangdan Station of Gyeongui Line will be treated by preservation process and displayed in the open outdoor area, effective surface covering agents were selected through testing to prevent the corrosion of the locomotive. The mixed wax are based on two types of microcrystalline wax which is one of regular surface covering agents for locomotives and bee‘s wax. For the weather resistance test, 3 types of wax were applied to each specimen of the locomotive and the specimens were tested in the Xenon-Arc Accelerated Weathering Tester for 1000 hours in accordance with the ISO 4892-1981 criteria and the test results were compared. As a result, on the surface of the specimen coated with the bee's wax, a whitening event appears after 400 hours which causes aging, and the specimens coated by the microcrystalline wax showed signs of a whitening event after 800 hours. The moisture contact angle with the microcrystalline wax coating was also less than with the bee's wax. Therefore, it was found that the high temperature microcrystalline wax is the most effective coating agent in terms of weather resistance and moisture blocking capability and the high temperature microcrystalline wax was adopted for coating the surface of the locomotive.

• Economic and Environmental Geology
• /
• v.52 no.6
• /
• pp.587-593
• /
• 2019

This study were subjected to accelerated weathering test under freeze-thaw and pressure conditions to observe initiation and propagation of cracks using CLSM. Applied stress was set at 50 MPa, 55 MPa, 70 MPa for 3 samples each by using compressor and freeze-thaw experiment was conducted while samples maintained that condition. In freeze-thaw experiments, a temperature range was set to -20~40℃ which was 1 cycle for 6 hours. The freeze-thaw cycle was composed of time which reached to set temperature for 1 hour and holding time for 2 hours. On the basis of this cycle, surface of samples was observed by CLSM after each 20 freeze-thaw cycle. From this research, according to increase freeze-thaw cycle, there were 7, 10, 19 each cracks and High pressured sample's accumulate length was longer than low pressured sample's. High pressured sample's crack velocities were also faster than low pressured sample's which were calculated by accumulate length and freeze-thaw cycle.

• Journal of Conservation Science
• /
• v.36 no.3
• /
• pp.178-186
• /
• 2020

Verdigris is a traditional artificial pigment reported on old research papers and according to the methods mentioned in the literature, it is manufactured by the corrosion of copper or copper alloys using vinegar and by further scraping the generated rust. Since the Three Kingdoms Period, various household products with copper alloys, such as bronze and brass, have been used, and pigment analysis of these cultural heritage items has revealed the presence of tin, zinc, lead, and copper in green pigments. Based on these data, five types of verdigris were prepared from copper and copper alloys, and analyzed. the analysis results revealed a bluish green pigmentation, and the chromaticity, particle shape, and oil absorption quantity of each verdigris differed based on the type of copper alloy used in its preparation. The main components of verdigris are Cu, Sn, Zn and Pb, and their proportions depended on the type of copper alloy used during manufacturing. However, the main constituent mineral of the pigments is the same as 'hoganite[Cu(CH₃COO)₂·H₂O]', regardless of the copper alloy used. The result of accelerated weathering test for stability evaluation revealed that verdigris was discolored rapidly, thereby indicating that its stability was low, in particular, the pigments comprising lead presented relatively lower stability.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.6
• /
• pp.4237-4244
• /
• 2015

This study examined the efflorescence characteristics of a concrete sidewalk block manufactured using recycled stone powder sludge and photocatalytic generated by surface polishing during the sidewalk block manufacturing process. The study evaluated the characteristics of the sidewalk block in terms of its quality, based on the amount of stone powder sludge used, efflorescence, and further based on the mixing ratio and number of applications of the photocatalytic. The experimental results indicated that heavy metals such as lead, hexavalent chrome, cadmium, and mercury were not present in the concrete sidewalk block, thereby confirming the effectiveness of the recycled stone powder sludge. The optimum mixing ratio of used in the concrete sidewalk block (for satisfying KS standard values such as water absorption ratio and flexural strength) was found to be 20%. The concrete sidewalk block incorporating the stone powder sludge and photocatalytic exhibited a water absorption ratio of 5.4% and flexural strength of 5.2 MPa, thereby satisfying the quality standards. Additionally, when the photocatalytic was used, efflorescence did not occur even at the low temperature of $-5^{\circ}C$, and the by the sidewalk block was found to be 70% under normal conditions and 68% when subjected to an accelerated weathering test.

• Korean Journal of Heritage: History & Science
• /
• v.56 no.2
• /
• pp.148-169
• /
• 2023

Hayeob pigment is known as one of the traditional dark green pigments, but the color, raw material, and manufacturing method have not been clearly identified. However, comparing the analysis results of the particle shape and constituent minerals of Hayeob pigments revealed through pigment analysis studies of colored cultural properties such as Dancheong, Gwaebul, and paintings, Hayeob pigments appear to be the same as Dongrok pigments produced by salt corrosion. Therefore, in order to restore Hayeob pigment, the manufacturing method of Dongrok pigment was studied based on the records of old literature. The Dongrok pigment manufacturing method confirmed in the old literature records is a natural corrosion method in which copper powder and a caustic are mixed and then left in a humid condition to corrode. Based on this, artificial corrosion using a corrosion tester was adopted to corrode the copper powder more efficiently, and an appropriate mixing ratio was selected by analyzing the state of corrosion products according to the mixing ratio of the caustic agent. In addition, the manufacturing method of Dongrok pigment was established by adding a salt removal process to remove residual caustic agents and a purification process to increase chroma during pigment coloring. The prepared Dongrok pigments have a bluish green or green color, show an elliptical particle shape and a form in which small particles are aggregated, and a porous surface is observed. The main constituent elements are copper(Cu) and chlorine(Cl), and the main constituent mineral is identified as atacamite [Cu₂Cl(OH)₃]. As a result of an accelerated weathering test to evaluate the stability of the prepared Dongrok pigments, it was found that the greenness partially decreased and the yellowness significantly increased as deterioration progressed. Before deterioration, the Dongrok pigments had lower yellowness compared to the Hayeob pigments of the old Dancheong, but after deterioration, yellowness increased significantly, and it was found to have a similar chromaticity range as Dancheong's Hayeob pigments. As a result, the prepared Dongrok pigments were confirmed to be similar to Dancheong's Hayeob pigments in terms of color as well as particle shape and constituent minerals.