• 한국전기전자재료학회논문지
• /
• 제32권2호
• /
• pp.147-150
• /
• 2019

There is a need for the development of transparent conductive materials that are economical and environmentally friendly with exhibit low resistivity and high transmittance in the visible spectrum. In this study, the deposition rate and uniformity of Al-doped ZnO-thin films were improved by changing the Z-motion of the sputtering system. The deposition rate and the uniformity were determined to be 3.44 nm/min and 1.23%, respectively, under the 10 mm Z-motion condition. During $O_2$ plasma treatment, the intrusion-type metal elements in the thin film were reduced, which contributed to an oxygen vacancy reduction in addition to structural stabilization. Moreover, the sheet resistance was more easily saturated.

• Transactions on Electrical and Electronic Materials
• /
• 제7권5호
• /
• pp.271-275
• /
• 2006

Al oped zinc oxide (AZO) films were prepared by Facing Targets Sputtering (FTS) system for TCO applications. The electrical, optical and structural properties of AZO thin films have been investigated with input current, oxygen gas flow ratio and substrate temperature. Deposition was carried out at room temperature and $200^{\circ}C$. Working gas pressures were fixed at 1mTorr. As a result, AZO thin film deposited with an optical transmittance over 80 % and a resistivity about $10^{-4}{Omega}{\cdot}cm$.

• 반도체디스플레이기술학회지
• /
• 제20권1호
• /
• pp.1-6
• /
• 2021

We have investigated the effect of the substrate temperature and hydrogen flow rate on the characteristics of AZO thin films for the TCO (transparent conducting oxide). For this purpose, AZO thin films were deposited by RF magnetron sputtering at room temperature and 300℃ with various H2 flow rate. Experiments were carried out while varying the hydrogen gas flow rate from 0sccm to 5.0sccm in order to see how the hydrogen gas affects the AZO thin films. AZO thin films deposited at 300℃ showed amorphous structure, whereas IZO thin films deposited at room temperature showed crystalline structure having an (222) preferential orientation. The electrical resistivity of the AZO films deposited at 300℃ was 4.388×10-3Ωcm, the lowest value. As the hydrogen gas flow rate increased, the resistivity tended to decrease.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.594-594
• /
• 2012

Al doped ZnO (AZO) thin films were deposited on textured glass substrate by magnetron sputtering method. Also, AZO films on textured glass were etched by hydrochloric acid (HCl). Average thickness of etched AZO films are 90 nm. We observed morphology of AZO film by AFM with various etchant concentration and etching time. Etched AZO films have low resistivity and high haze. The surface RMS roughness of AZO film was increased from 53.8 nm to 84.5 nm. The haze ratio was also enhanced in above 700 nm of wavelength due to light trapping effect was increased by rough AZO surface. The etched AZO films on textured glass are applicable to fabricate solar cell.

• 한국재료학회지
• /
• 제31권3호
• /
• pp.150-155
• /
• 2021

Zinc oxide (ZnO) based transparent conducting oxides (TCO) thin films, are used in many applications such as solar cells, flat panel displays, and LEDs due to their wide bandgap nature and excellent electrical properties. In the present work, fluorine and aluminium-doped ZnO targets are prepared and thin films are deposited on soda-lime glass substrate using a RF magnetron sputtering unit. The aluminium concentration is fixed at 2 wt%, and the fluorine concentration is adjusted between 0 to 2.0 wt% with five different concentrations, namely, Al2ZnO98(AZO), F0.5AZO97.5(FAZO1), F1AZO97(FAZO2), F1.5AZO96.5(FAZO3), and F2AZO96(FAZO4). Thin films are deposited with an RF power of 40 W and working pressure of 5 m Torr at 270 ℃. The morphological analysis performed for the thin film reveals that surface roughness decreases in FAZO1 and FAZO2 samples when doped with a small amount of fluorine. Further, optical and electrical properties measured for FAZO1 sample show average optical transmissions of over 89 % in the visible region and 82.5 % in the infrared region, followed by low resistivity and sheet resistance of 3.59 × 10-4 Ωcm and 5.52 Ω/sq, respectively. In future, these thin films with excellent optoelectronic properties can be used for thin-film solar cell and other optoelectronics applications.

• 한국재료학회지
• /
• 제20권12호
• /
• pp.629-635
• /
• 2010

Abstract In this study characteristics of Al-doped ZnO thin film by HIPIMS (High power impulse sputtering) are discussed. Deposition speed of HIPIMS with conventional balanced magnetic field is measured at about 3 nm/min, which is 30% of that of conventional RF sputtering process with the same working pressure. To generate additional magnetic flux and increase sputtering speed, electromagnetic coil is mounted at the back side of target. Under unbalanced magnetic flux from electromagnet with 1.5A coil current, deposition speed of AZO thin film is increased from 3 nm/min to 4.4 nm/min. This new value originates from the decline of particles near target surface due to the local magnetic flux going toward substrate from electromagnet. AZO film sputtered by HIPIMS process shows very smooth and dense film surface for which surface roughness is measured from 0.4 nm to 1 nm. There are no voids or defects in morphology of AZO films with varying of magnetic field. When coil current is increased from 0A to 1A, transmittance of AZO thin film decreases from 80% to 77%. Specific resistance is measured at about $2.9{\times}10-2\Omega{\cdot}cm$. AZO film shows C-axis oriented structure and its grain size is calculated at about 5.3 nm, which is lower than grain size in conventional sputtering.

• 센서학회지
• /
• 제22권2호
• /
• pp.105-110
• /
• 2013

We fabricated an a-IGZO thin film transistor (TFT) with AZO/Ag/AZO transparent multilayer source/drain contacts by rf magnetron sputtering. a-IGZO TFT with AZO/Ag/AZO multilayer S/D electrodes (W/L = 400/50 ${\mu}m$) showed a subs-threshold swing of 3.78 V/dec, a minimum off-current of $10^{-12}$ A, a threshold voltage of 0.41 V, a field effect mobility of $10.86cm^2/Vs$, and an on/off ratio of $9{\times}10^9$. From the ultraviolet photoemission spectroscopy, it was revealed that the enhanced electrical performance resulted from the lowering of the Schottky barrier between a-IGZO and Ag due to the insertion of an AZO layer and thus the AZO/Ag/AZO multilayer would be very appropriate for a promising S/D contact material for the fabrication of high performance TFTs.

• 전기학회논문지
• /
• 제58권10호
• /
• pp.1976-1981
• /
• 2009

Transparent conducting aluminum-doped zinc oxide (AZO) thin films were deposited on Coming glass substrate using an Gun-type rf magnetron sputtering deposition technology. The AZO thin films were fabricated with an AZO ceramic target (Zn: 98wt.%, $Al_2O_3$: 2wt.%). The AZO thin films were deposited with various growth conditions such as the substrate temperature, oxygen pressure. X -ray diffraction (XRD), UV/visible spectroscope, atomic force microscope (AFM), and Hall effect measurement system were done in order to investigate the properties of the AZO thin films Among the AZO thin films prepared in this study, the one formed at conditions of the substrate temperature $100^{\circ}C$, Ar 50 sccm, $O_2$ 5 sccm and working pressure 5 motor showed the best properties of an electrical resistivity of $1.763{\times}10^{-4}\;[{\Omega}{\cdot}cm]$, a carrier concentration of $1.801{\times}10^{21}\;[cm^{-3}]$, and a carrier mobility of $19.66\;[cm^2/V{\cdot}S]$, which indicates that it could be used as a transparent electrode for thin film transistor and flat panel display applications.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.169-169
• /
• 2016

In this paper, we report electrical, optical and structural properties of Al-doped zinc oxide (AZO) thin films deposited at different substrate temperatures and pressures. The films were prepared by radio frequency (RF) magnetron sputtering on glass substrates in argon (Ar) ambient. The X-ray diffraction analysis showed that the AZO films deposited at room temperature (RT) and 20 Pa were mostly oriented along a-axis with preferred orientation along (100) direction. There was an improvement in resistivity ($3.7{\times}10^{-3}{\Omega}-cm$) transmittance (95%) at constant substrate temperature (RT) and working pressure (20 Pa) using the Hall-effect measurement system and UV-vis spectroscopy, respectively. Our results have promising applications in low-cost transparent electronics, such as the thin-film solar cells and thin-film transistors due to favourable deposition conditions. Furthermore our film deposition method offers a procedure for preparing highly oriented (100) AZO films.

• 반도체디스플레이기술학회지
• /
• 제15권4호
• /
• pp.36-40
• /
• 2016

The 2 wt.% Al-doped ZnO(AZO) thin films were fabricated on PET substrates with various RF power 20, 35, 50, 65, and 80W by using RF magnetron sputtering in order to investigate the structure, electrical and optical properties of AZO thin films in this study. The XRD measurements showed that AZO films exhibit c-axis orientation. At a RF power of 80W, the AZO films showed the highest (002) diffraction peak with a FWHM of 0.42. At a RF power of 65W, the lowest electrical resistivity was about $1.64{\times}[10]$ ^(-4) ${\Omega}-cm$ and the average transmittance of all films including substrates was over 80% in visible range. Good transparence and conducting properties were obtained due to RF power control. The obtained results indicate that it is acceptable for applications as transparent conductive electrodes.