• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.4
• /
• pp.190-195
• /
• 2012

This study aims to investigate and compare the microstructures and room temperature tensile properties for AZ91 and ECO-AZ91 (AZ91+0.3%CaO) alloys in as-cast, T4 and T6 states, respectively. In as-cast state, the ECO-AZ91 alloy has finer microstructure than the AZ91 alloy. The AZ91 alloy exhibits greater ductility, while YS and UTS are inferior to those of the ECO-AZ91 alloy. After T4 treatment, most of ${\beta}$ compounds disappear in the AZ91 alloy, whereas ${\beta}$ phase is still observed in the ECO-AZ91 alloy due to its enhanced thermal stability, resulting in lower values of ductility and UTS. In T6 state, YS and UTS are better in the ECO-AZ91 alloy.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.4
• /
• pp.193-198
• /
• 2011

Effect of CaO addition on age hardening response has been studied by using optical microscopy, scanning electron microscopy and differential thermal analysis in AZ91 and CaO-containing ECO-AZ91 alloys. After solution treatment, the ${\beta}$($Mg_{17}Al_{12}$) phase formed during solidification mostly disappeared in the microstructure in the AZ91 alloy, whereas numerous ${\beta}$ precipitates containing Ca were still observed in the ECO-AZ91 alloy due to its enhanced thermal stability. The ECO-AZ91 alloy showed the delayed peak aging time and higher peak hardness compared with those of the AZ91 alloy. The activation energies for ${\beta}$ precipitation calculated by means of Kissinger method increased from 71.4 to 85.6 kJ/mole by the addition of CaO, which implies that CaO plays a role in reducing ${\beta}$ precipitation rate in the AZ91 alloy.

• Transactions of Materials Processing
• /
• v.31 no.3
• /
• pp.160-166
• /
• 2022

The purpose of this study is to investigate the effects of combined addition of Ca and Y on the precipitation and age-hardening behavior of an extruded AZ91 alloy by conducting the aging treatment at 200 ℃ for hot-extruded AZ91 and AZ91-0.3Ca-0.2Y alloys. In the AZ91 alloy, many Mg₁₇Al₁₂ discontinuous precipitate (DP) bands formed during air cooling immediately after extrusion are present, whereas in the AZ91-0.3Ca-0.2Y alloy, a few DP bands and numerous Al₂Y, Al₈Mn₄Y, and Al₂Ca phase particles are distributed along the extrusion direction. The peak-aging time of the AZ91-0.3Ca-0.2Y alloy is 16 hours, twice that of the AZ91 alloy. Although both alloys have similar hardness before aging treatment, the hardness after peak-aging treatment (i.e., peak hardness) of the AZ91-0.3Ca-0.2Y alloy is higher than that of the AZ91 alloy, as 93.1 and 88.7 Hv, respectively. The microstructures of both peak-aged alloys comprise DPs and continuous precipitates (CPs). However, the peak-aged AZ91-0.3Ca-0.2Y alloy has a smaller amount of DPs and a larger amount of CPs than the peak-aged AZ91 alloy. Additionally, the inter-particle spacings of DPs and CPs in the former are significantly narrower than those in the latter. These results demonstrate that the addition of small amounts of Ca and Y to a commercial AZ91 alloy considerably affects the formation rate, size, and amount of CPs and DPs during aging and resultant age-hardening behavior.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.6
• /
• pp.260-268
• /
• 2002

The effects of calcium and silicon on microstructure and aging characteristics of AZ91 magnesium alloy during T5 treatment was investigated. The addition of 0.88% calcium or 0.25% silicon to AZ91 alloy made dendrite cell smaller. Especially, silicon is more effectively acted as refinement of the dendrite cell than calcium. It is due to that $Mg_2Si$ precipitated at the dendrite cell boundary or in the matrix during T5 treatment of Si added AZ91 alloy retarded the growth of the secondary phase. In the mean while, without inducing the precipitates containing calcium, calcium was segregated mainly around secondary phase such as $Mg_{17}Al_{12}$ and partially dissolved in ternary eutectic (Mg-Al-Ca) structure. In the AZ91 alloy containing both silicon and calcium, more finely distributed $Mg_2Si$ in matrix homogeneously and much finer microstructure were obtained than those containing silicon or calcium. Hence, An AZ91 containing both silicon and calcium was more effective to retarding the growth of the secondary phase than the other AZ91 alloy such as AZ91 alloy containing silicon or AZ91 alloy containing calcium.

• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.619-624
• /
• 2003

This paper describes a method to control Mn and Fe contents in recycled AZ91D ingots, based on the mutual solubility of Mn and Fe in AZ91 alloy melts. For this purpose, Fe solubility with the change of Mn content and temperature was investigated in the homogenized and re-precipitated liquid AZ91 alloy. The increase of the amount of Mn added to the melt resulted in the decrease of Fe content. The data obtained in this study was adopted to the pilot plant for recycling of the scrap. As a result, Mn and Fe contents measured in the recycled ingot were in good agreement with ASTM B93 standard.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.4
• /
• pp.184-193
• /
• 2021

This study demonstrates formation behavior and morphological changes of PEO (Plasma Electrolytic Oxidation) films on AZ91 Mg alloy as a function of pre-treatment time in 1 M HF solution at 25 ± 1 ℃. The electrochemical behavior and morphological changes of AZ91 Mg alloy in the pre-treatment solution were also investigated with pre-treatment time. The PEO films were formed on the pre-treated AZ91 Mg alloy specimen by the application of anodic current 100 mA/cm² of 300 Hz AC in 0.1 M NaOH + 0.4 M Na₂SiO₃ solution. Vigorous generation of hydrogen bubbles were observed upon immersion in the pre-treatment solution and its generation rate decreased with immersion time. It was also found that 𝛽-Mg₁₇Al₁₂ in AZ91 Mg alloy was dissolved and a protective thin film of MgF₂ was formed on the AZ91 Mg alloy surface during the pre-treatment process in the 1 M HF solution. PEO film did not grow on the AZ91 Mg alloy specimen when the surface was not pre-treated and irregular PEO films with nodular defects were formed for the specimens pre-treated up to 1 min. Uniform PEO films were formed when the AZ91 Mg alloy specimen was pre-treated more than 3 min. The growth rate of PEO films on AZ91 Mg alloy increased significantly with increasing pre-treatment time.

• Transactions of Materials Processing
• /
• v.32 no.4
• /
• pp.173-179
• /
• 2023

In this study, the age-hardening behavior and tensile properties of a cast AZ91-0.3Ca-0.2Y (SEN9) alloy are investigated and compared with those of a commercial AZ91 alloy. Even after homogenization heat treatment, the SEN9 alloy contains numerous undissolved secondary phases, Al₈Mn₄Y, Al₂Y, and Al₂Ca, which results in a higher hardness value than the homogenized AZ91 alloy. Under aging condition at 200 ℃, both the AZ91 and SEN9 alloys exhibit the same peak-aging time of 8 h, but the peak hardness of the latter (86.8 Hv) is higher than that of the former (83.9 Hv). The precipitation behavior of Mg₁₇Al₁₂ phase during aging significantly differs in the two alloys. In the AZ91 alloy, the area fraction of Mg₁₇Al₁₂ discontinuous precipitates (DPs) increases up to ~50% as the aging time increases. In contrast, in the SEN9 alloy, the formation and growth of DPs during aging are substantially suppressed by the Ca- or Y-containing particles, which leads to the formation of only a small amount of DPs with an area fraction of ~4% after peak aging. Moreover, the size and interparticle spacing of Mg₁₇Al₁₂ precipitates of the peak-aged SEN9 alloy are smaller than those of the peak-aged AZ91 alloy. The homogenized AZ91 alloy exhibits a higher tensile strength than the homogenized SEN9 alloy due to the finer grains of the former. However, the peak-aged SEN9 alloy has a higher tensile elongation than the peak-aged AZ91 alloy due to the smaller amount of brittle DPs in the former.

• Journal of the Korean institute of surface engineering
• /
• v.55 no.1
• /
• pp.24-31
• /
• 2022

This study investigated the effect of pre-treatment on the PEO film formation of AZ91 Mg alloy. The pre-treatment was conducted for 10 min at room temperature in 0.5 M oxalic acid (C₂H₂O₄) solution containing various ammonium fluoride (NH₄F) concentrations. The pre-treated AZ91 Mg specimens were anodized at 100 mA/cm² of 300 Hz AC for 2 min in 0.1 M NaOH + 0.4 M Na₂SiO₃ solution. When AZ91 Mg alloy was pretreated in 0.5 M oxalic acid with NH₄F concentration less than 0.3 M, continuous dissolution of the AZ91 Mg alloy occurred together with the formation of black smuts and arc initiation time for PEO film formation was very late. It was noticed that corrosion rate of the AZ91 Mg alloy became faster if small amount of NH₄F concentration, 0.1 M, is added. The fast corrosion is attributable to fast formation of porous fluoride together with porous oxides in the reaction products. On the other hand, when AZ91 Mg alloy was pretreated in 0.5 M oxalic acid with sufficient NH₄F more than 0.3 M, a thin and dense protective film was formed on the AZ91 Mg alloy surface which resulted in faster initiation of arcs and formation of PEO film.

• Laser Solutions
• /
• v.18 no.1
• /
• pp.1-6
• /
• 2015

High welding speed and narrow weld seam are favorable for welding of magnesium alloy. Magnesium alloy is recommended for the smart frame because it has several advantages such as low density, high thermal conductivity, EMI shielding capability and good cast ability. This study is for the assembly welding of the magnesium smart frame with high productivity, good performance and low cost. The window for battery on AZ91D frame produced by die-casting was prepared by CNC machining. Corresponding AZ31 blank of 0.2mm thickness was prepared by die-blanking cut. All system set was fixed at the stationary bed but the laser beam was manipulated by scanner up-to 1,000mm/s speed. The weld joint between AZ31 sheet and AZ91D frame was welded by fiber laser on 850~1,000W output power. The joint showed penetration enough but some humping bead. The distortion by the weld heat was almost free because of the quick dissipation of the heat by small beam size and fast welding. Consequently, the thinner magnesium foil was assembled successfully to the magnesium frame of mobile phone.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.328-331
• /
• 2007

It was carried out to evaluate microstructure and mechanical properties of friction stir welded(FSW) on magnesium alloys. Two types magnesium alloy was used in this work, AZ31 wrought and AZ91 cast magnesium alloy. Microstructure near the weld zone showed general weld structures such as stir zone(SZ), thermo-mechanically affected zone(TMAZ) and heat affected zone(HAZ). In the AZ91 alloy, the SZ had a fine grain size and $\beta$ phase particles which were well distributed in matrix. It was characterized to redistribute by partial or full re-solution of the $\beta$ phase which is coarse in base metal during FSW processing. The hardness of the SZ slightly increase than the base metal in AZ31 Mg alloy.