• Corrosion Science and Technology
• /
• v.6 no.3
• /
• pp.96-102
• /
• 2007

The resistance of the linepipe steel to hydrogen-induced cracking (HIC) and sulfide stress cracking (SSC) is very important for steel to be used in sour oil/gas environments. Welding of steels is necessary to the construction of pipe-line transporting oil/gas. In this study, HIC and SSC resistance of an electric resistance welded (ERW) steel plate which belongs to API X70 grade was evaluated by using NACE TM0284-96A and NACE TM0177-96A methods. HIC and SSC fracturing behavior was investigated by observing fractured surfaces using optical microscopy (OM) and scanning electron microscopy (SEM). It was discussed in terms of metallurgical parameters such as the distribution of primary microstructure, second phases and inclusions. Results showed that the weld joint of ERW steel is more sensitive than base metal to HIC and SSC. This is due to difference in the contribution of metallurgical parameters to HIC and SSC nucleation and propagation.

• Corrosion Science and Technology
• /
• v.2 no.3
• /
• pp.109-116
• /
• 2003

It is well known that SSCC (sulfide stress corrosion cracking) is caused by drastic ingression of hydrogen during the service and accumulation of hydrogen near the potential crack initiation site in the material. It is important to characterize the hydrogen trapping behavior to evaluate the service performance of the high strength pipeline steels. In this study. the relationship between the hydrogen trapping behavior and SSCC susceptibility is evaluated in terms of alloy composition, microstructure and carbide behavior. The hydrogen trapping behavior was measured by electrochemical hydrogen permeation test cell (Devanathan cell). The SSCC susceptibility is evaluated by constant extension rate test and constant strain lest method. The hydrogen trapping behavior is affected greatly by microstructure and nature of carbide particles. The fine TiC, and NbC in the matrix of ferritic structure acts as strong irreversible trap sites whereas the bainitic structure acts as reversible trap site. The SSCC susceptibility is closely related to not only the hydrogen trapping behavior but also the loading condition. As the activity of reversible trap site increases, SSCC susceptibility decreases under static loading condition below yield strength, whereas SSCC susceptibility increases under dynamic loading condition or above yield strength. As the activity of irreversible trap site increases. SSCC susceptibility increases regardless of loading condition. It is cased by the mixed effect of dislocation on hydrogen diffusion and trapping behavior.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2004.11a
• /
• pp.291-296
• /
• 2004

The paper describes a test program on welded K-joints fabricated from circular hollow section brace members and chords made with API 2W 50 grade steel produced by POSCO. The K-joints were tested for three loading conditions at RIST. The specimens were tested in reaction frame that allowed vertical uniform loading to the structure. From the test, the crack initiation and development were observed and the fatigue failure could be predicted. The results were also compared with the provided S-N curves by DnV.