• 한국주조공학회지
• /
• 제18권4호
• /
• pp.383-388
• /
• 1998

Effects of $CaCN_2$ addition on the grain refinement in the AM60 magnesium ingots were investigated. The effects of the $CaCN_2$ are estimated with different inoculation temperatures, inoculation contents, and holding time to find out the optimum condition. AM60 alloy was melted in the low carbon steel crucible by cylindrical electric furnace under an argon atmosphere. The melting and casting apparatus is specially designed for magnesium alloys. The grain size of AM60 magnesium alloy decreased significantly with an increase in $CaCN_2$ content and, at 0.8 wt% $CaCN_2$ or more, grain size becomes constant at about $85 {\mu}m$. The optimum condition was obtained in the 0.8 wt% $CaCN_2$ for holding molten metal of 30 min. at the temperature of $710^{\circ}C$. The tensile properties of AM60 magnesium alloys were improved due to grain refinement by addition of $CaCN_2$. In the optimum condition, the yield strength, tensile strength and elongation were ${\sigma}_{0.2}=107 MPa$, ${\sigma}_{T.S}=234 MPa$ and e=14.2%. The variation of stress with strain obeyed the relationship of the ${\sigma}=K{\varepsilon}^n$. The strain-hardening exponent, n and strength coefficient, K obtained in the 0.8 wt% $CaCN_2$ added AM 60 magnesium alloy were n=0.21 and K=390 MPa.

• 한국안전학회지
• /
• 제27권3호
• /
• pp.15-19
• /
• 2012

The fatigue behavior of AM60 magnesium alloy produced by equal channel angular pressing(ECAP) process was investigated through fatigue lifetime and fatigue crack propagation rate tests. The grain structure of the material was refined from 19.2 ${\mu}m$ to 2.3 ${\mu}m$ after 6 passes of ECAP at 493 K. The yield strength(YS) and ultimate tensile strength (UTS) increase after two passes but decrease with further pressing, although the grain size becomes finer with increasing pass number. The softening effect due to texture anisotropy overwhelmed the strengthening effect due to grain refinement after 2 passes. A large enhancement in fatigue strength was achieved after two ECAP passes. The current finding suggests that two passed material is better than the multi-passed material in view of the static strength and fatigue performance.

• 한국주조공학회지
• /
• 제32권1호
• /
• pp.44-49
• /
• 2012

In this study, three magnesium alloys were investigated; those are 1.5wt.% CaO added AM80, 1.0wt.% CaO added AM60, and conventional MRI153 alloys. Test specimens of three alloys were prepared by re-melting and casting into steel mold with ingots and machining. The mechanical properties and the creep behavior at 150 degrees Celsius of these specimens were determined and their microstructures were characterized using OM and SEM. For the application to die-casting, fluidity test were carried out with spiral mold. Compared with 1.0wt.% CaO added AM60 alloy, 1.5wt.% CaO added AM80 alloy exhibited good creep properties in all test conditions. Moreover, CaO added alloys showed better creep properties than MRI153 alloy at lower load condition. It is proposed that 1.5wt.% CaO added AM80 alloy is useful to apply to power-train parts such as transmission case in vehicles.

• 한국주조공학회지
• /
• 제29권3호
• /
• pp.144-149
• /
• 2009

In this study, we investigated optimum condition of cooling plate method to obtain semi-solid AM100A Mg alloy with fine and globular morphology. AM100A Mg alloy were hot extruded at $380^{\circ}C$ extrusion temperature under extrusion ratio of 25 : 1 and ram speed of 2.4 mm/sec. Vickers hardness test, optical microscopy, scanning electron microscopy, and image analyzer were performed to identify the optimum conditions of cooling plate method. Optimum conditions of cooling plate method to fabricate semi-solid AM100A Mg alloy with fine and globular microstructures were achieved at a pouring temperature of $602^{\circ}C$ and the angle of cooling plate of 60 degree.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 춘계학술대회 논문집
• /
• pp.415-418
• /
• 2005

In recent years, Magnesium (Mg) and its alloys have become a center of special interest in the automotive industry. Due to their high specific mechanical properties, they offer a significant weight saving potential in modem vehicle constructions. Most Mg alloys show very good machinability and processability, and even the most complicated die casting parts can be easily produced. The die casting process is a fast production method capable of a high degree of automation for which certain Mg alloys are ideally suited. Although Mg alloys are fulfilling the demands for low specific weight materials with excellent machining and casting abilities, they are still not used in die casting process to the same extent as the competing material aluminium. One of the reasons is that effects of various forming variables for die casting process is not closely examined from the viewpoint of die design. In this study, step die and flowability tests for AM60 were performed by die casting process according to various combination of casting pressure and plunger velocity. Microstructure and Victors hardness tests were examined and performed for each specimen to verify effects of forming conditions.

• Corrosion Science and Technology
• /
• 제15권3호
• /
• pp.120-124
• /
• 2016

The effect of alloying element Ca (0, 1, and 2 wt%) on corrosion resistance and bioactivity of the as-received and anodized surface of rolled plate AM60 alloys was investigated. A plasma electrolytic oxidation (PEO) was carried out to form anodic oxide film in $0.5mol\;dm^{-3}\;Na_3PO_4$ solution. The corrosion behavior was studied by polarization measurements while the in vitro bioactivity was tested by soaking the specimens in Simulated Body Fluid (1.5xSBF). Optical micrograph and elemental analysis of the substrate surfaces indicated that the number of intermetallic particles increased with Ca content in the alloys owing to the formation of a new phase $Al_2Ca$. The corrosion resistance of AM60 specimens improved only slightly by alloying with 2 wt% Ca which was attributed to the reticular distribution of $Al_2Ca$ phase existed in the alloy that might became barrier for corrosion propagation across grain boundaries. Corrosion resistance of the three alloys was significantly improved by coating the substrates with anodic oxide film formed by PEO. The film mainly composed of magnesium phosphate with thickness in the range $30-40{\mu}m$. The heat resistant phase of $Al_2Ca$ was believed to retard the plasma discharge during anodization and, hence, decreased the film thickness of Ca-containing alloys. The highest apatite forming ability in 1.5xSBF was observed for AM60-1Ca specimens (both substrate and anodized) that exhibited more degradation than the other two alloys as indicated by surface observation. The increase of surface roughness and the degree of supersaturation of 1.5xSBF due to dissolution of Mg ions from the substrate surface or the release of film compounds from the anodized surface are important factors to enhance deposition of Ca-P compound on the specimen surfaces.

• 한국주조공학회지
• /
• 제18권4호
• /
• pp.364-372
• /
• 1998

Effects of Si and Ca additions on the mechanical properties of AM60 based Mg alloys have been investigated. Hardness of the AM60 based Mg alloys reached a maximum value after aging for approximately 33 hours but the amount of hardness increase was negligible. The poor age hardening response of the alloys was due to low Al content, which implies that Al content must be >6 wt.% to observe age hardening effect. The tensile and yield strength increased with increasing Al, Si, and Ca content but elongation decreased with increasing Al and Si content. The best mechanical properties obtained in AM 40-2.5Si-0.2Ca alloy after T4 heat treatment were as follows; tensile strength 193.4 MPa, yield strength 79.2 MPa, and elongation 11.2%. High temperature property obtained from creep test was also improved by introducing $Mg_2Si$ which has high hardness, high melting temperature and low thermal expansion coefficient.

• 한국주조공학회지
• /
• 제31권5호
• /
• pp.293-301
• /
• 2011

Representative magnesium alloys applied to the die-casting are AZ91, AM60, etc., and the application of these alloys is restricted to components operating at moderate temperatures, due to grain boundary siding of ${\beta}$-phase($Mg_{17}Al_{12}$) at temperatures above $120^{\circ}C$. Heat-resistant magnesium alloys such as AE42, AE44 have been developed, but that have been too burdensome to produce because of the expensive rare earth materials. Research work for the development of low-priced heat-resistant magnesium alloy is actively in progress and positive results are being reported. This study aims to investigate the effect of Ca additions on mechanical properties of Mg-4Al-2Sn heat resistant magnesium alloys. Mg-4Al-2Sn alloys with Ca (0wt.%, 0.3wt.%, 0.7wt.%, 1wt.%) have been produced through the die-casting process for the development of low-priced heat-resistant magnesium alloy, and high temperature tensile tests are performed using the specimens. The results showed that mechanical properties of Mg-4Al-2Sn-xCa increased with the addition of Ca up to 0.7wt.% Ca and further addition of Ca deteriorated the mechanical properties of the alloys. A significant amount of porosity was observed at the sample with 1wt%. Ca and the longer freezing range of the alloy was believed to cause the formation of porosity.