• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.16 no.4
• /
• pp.9-15
• /
• 2017

In hot forming process, the dies in which excessive worn or crack occurs is reused after repair. Generally hot forming dies are recycled through a welding repair method. Welding repair methods are highly dependent on the skills of engineer. It causes process defects such as dimensional defects and structural defects. Recently, the metal 3D printing method has been applied to the repair of used dies. The aim of this study is to evaluate the wear characteristics of AISI H13 tool steel repaired by 3D printing method. Three kinds of wear specimens were fabricated by using 3D printing, welding, and initial material. A pin-on-disk wear test was carried out to evaluate the wear characteristics. From the result of wear test, the wear characteristics of 3D printing method was superior to that of the welded material, and was similar to that of the initial material.

• Transactions of the Korean hydrogen and new energy society
• /
• v.13 no.4
• /
• pp.313-320
• /
• 2002

The characteristics of the AISI bipolar plates have been investigated to replace the expensive graphite bipolar plates. It was found from the contact resistance evaluation of graphites, composites, and AISI that the contact resistance of AISI was the lowest, but it could approach to that of composites at higher compression forces. The single cell operation using the AISI bipolar plates revealed that the lower performance of the AISI single cell compared to the graphite one was due to not only the higher contact resistance but the flooding effect caused by high wettability of AISI. The performance of the AISI single cell could be improved if the channels were modified appropriately. The large size AISI single cell was operated to investigated the size effect on the performance.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.634-639
• /
• 1996

In oder to improve the wear resistance as well as oxidation resistance at high temperature a AISI H13 steel was treated by a duplex process of calorizing followed by plasma nitriding. The surface properties of the duplex-treated AISI H13 steel was characterized and compared with those treated by single surface process of calorizing and plasma nitriding, in terms of microstruture, microhardness, wear resistance at $500^{\circ}C$, and the oxidation behaviours at $700^{\circ}C$, Duplex process on H13 steel had created duplex layer of approximately $190\mu\textrm{m}$ on the surface, and surface microhardness was measured to be above 1450Hv(0.1Kgf). There was considerable improvement of the high temperature wear resistance at $500^{\circ}C$ in the duplex-treated steel when both wear volume and weight change due to oxidation were considered. In addition the duplex-treated steel showed an improved high temperature oxidation resistance than the plasma nitrided steel at $700^{\circ}C$.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.6
• /
• pp.307-314
• /
• 2021

Diamond-like carbon (DLC) is difficult to achieve sufficient adhesion because of weak bonding between DLC film and the substrate. The purpose of this study is to improve the adhesion between substrate and DLC film. DLC film was deposited on AISI H13 using linear ion source. To improve adhesion, the substrate was treated by dual post plasma nitriding. In order to define the mechanism of the improvement in adhesive strength, the gradient layer between substrate and DLC film was analyzed by Glow Discharge Spectrometer (GDS) and Scanning Electron Microscope (SEM). The microstructure of the DLC film was analyzed using a micro Raman spectrometer. Mechanical properties were measured by nano-indentation, micro vickers hardness tester and tribology tester. The characteristic of adhesion was observed by scratch test. The adhesion of the DLC film was enhanced by active screen plasma nitriding layer.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2006.10a
• /
• pp.71-72
• /
• 2006

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1193-1201
• /
• 2018

Dilatometry is a useful technique to obtain experimental data concerning transformation. In this paper, a dilation conversional model was established to calculate carbides fraction in AISI H13 hot-work tool steel based on the measured length changes. After carbides precipitation, the alloy contents in the matrix changed. In the usual models, the content of carbon atoms after precipitation is considered as the only element that affects the lattice constant and the content of the alloy elements such as Cr, Mo, Mn, V are often ignored. In the model introduced in this paper, the alloying elements (Cr, Mo, Mn, V) changes caused by carbides precipitation are incorporated. The carbides were identified using scanning electron microscope and transmission electron microscope. The relationship between lattice constant of carbides and temperature are measured by high-temperature X-ray diffraction. The results indicate that the carbides observed in all specimens cooled at different rates are V-rich MC and Cr-rich $M_{23}C_6$, and most of them are V-rich MC, only very few are Cr-rich $M_{23}C_6$. The model including the effects of substitutional alloying elements shows a good improvement on carbides fraction predictions. In addition, lower cooling rate advances the carbides precipitation for AISI H13 specimens. The results between experiments and mathematical model agree well.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.13 no.3
• /
• pp.7-13
• /
• 1993

Fracture behavior of pre-cracked compact tension specimens made of AISI 4130 steel was investigated using acoustic emission (AE) and ultrasonic C-scan measurements. While each specimen was loaded up to a certain level, various acoustic emission parameters were recorded together with the crack opening displacement (COD). An elastic-plastic finite element analysis was performed to calculate COD and the damage (plastic) zone size ahead of crack tip. Ultrasonic C-scans, in a pulse-echo, immersion mode, were done for mapping the damage zone size. The agreement between the finite element results and the measured COD was satisfactory. Based on AE results, the test specimens were found to show ductile behavior. The slope of the total ringdown counts vs. COD curve was useful to determine the crack initiation. The preliminary C-scan images showed evidence of changes in the amplitude of ultrasonic signal in the damaged region, and the shape and size of the damage zone matched qualitatively with the finite element results. A further work on the damage zone sizing was also pointed out.

• The Korean Journal of Ceramics
• /
• v.6 no.1
• /
• pp.27-31
• /
• 2000

A series experiments were performed to evaluate mechanical behavior of non-oxide boride type ceramics formed on the AISI 1040 plain carbon steel. Boronizing was performed in a slurry salt bath consisting of borax, boric acid, and ferro-silicon at $950^{\circ}C$ for 2-6h. The AISI 1040 steel used as substrate material was containing 0.4%C, 0.13%Si, 0.65%Mn, 0.02%P, 0.014%S. The presence of non-oxide boride type ceramics $Fe_2B $ and FeB formed on the surface of steel was confirmed by metallographic technique and X-ray diffraction (XRD) analysis. The hardness of borides measured via Vickers indenter with a load of 2N reached a microhardness of up to 1800 DPN. The hardness of unborided steel was 185 DPN. The fracture toughness of borides measured by means of Vickers indenter with a load of 10N was about 2.30 MPa.$m^{1/2}$. The thickness of boride layers ranged from 72$\mu\textrm{m}$ to 145$\mu\textrm{m}$. Boride layers have a columnar morphology.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.6
• /
• pp.343-350
• /
• 2020

The degradation of mechanical properties of nitride coatings to steel substrates is one of the main challenges for industrial applications. In this study, plasma nitriding treatment was used in order to increase the mechanical properties of Mo-Cu-N coating to the H13 tool steel. The nanostructured Mo-Cu-N coating was deposited using pulsed DC magnetron sputtering method with a single alloy Mo-Cu target. Mechanical properties of MoN-Cu coated samples after nitriding were found to be relatively better than non-nitrided MoN-Cu coating.

• Journal of the Korean institute of surface engineering
• /
• v.57 no.2
• /
• pp.105-114
• /
• 2024

Tempering behavior and mechanical properties in AISI H13 steel, quenched and tempered from 300 ℃ to 700 ℃ for different tempering time (1, 2, 5, 10, 20 hr) were quantitatively investigated by scanning electron microscopy (SEM), x-ray diffractometer (XRD), impact test machine, rockwell apparatus, ball-on-disk tester. Under the condition that the tempering time is 2 hours, the hardness increases slightly as the tempering temperature increases, but decreases rapidly when the tempering temperature exceeds 500 ℃, while the impact energy increases in proportion to the tempering temperature. Friction tests were conducted in dry condition with a load of 30 N, and the friction coefficient and wear rate according to tempering conditions were measured to prove the correlation with hardness and microstructure. In addition, primary tempering from 300 ℃ to 700 ℃ was performed at various times to establish a kinetic model to predict hardness under specific tempering conditions.