• Journal of Korea Foundry Society
• /
• v.38 no.6
• /
• pp.121-131
• /
• 2018

The effect of additives on the castability of the AC2BS aluminum alloy, which contains 35% recycled scrap, was investigated. For the wide utilization of the recycled scrap AC2BS aluminum alloy, the research results were compared to those with the AC2B virgin alloy, which is typical Al-Si-Cu alloy system. It was confirmed that the addition of Al-5%Ti-1%B increased the ${\alpha}$-Al nucleation temperature during solidification and decreased the grain size through cooling curve and microstructural observations of the recycled alloy. It was also found that an addition of Al-10%Sr decreased the eutectic Si growth temperature during the solidification process and modified the shape of the eutectic Si of the recycled alloy. The characteristics of fluidity, shrinkage and solidification crack strength were evaluated. For the AC2BS aluminum alloy containing 35% recycled scrap, both ${\alpha}$-Al grain refinement due to Ti-B and eutectic Si modifications due to Sr contributed to the improvement of the fluidity. The macro- shrinkage ratio increased with additions of both Al-10%Sr and Al-5%Ti-1%B and the micro-shrinkage ratio increased with the addition of Al-10%Sr but decreased with the addition of Al-5%Ti-1%B. The casting characteristics of TiB and Sr-treated AC2BS aluminum alloy containing 35% recycled scrap are similar to those of AC2B virgin alloy. The improvement of the solidification crack strength of the AC2BS aluminum alloy was possible by the reduction of the grain boundary the stress concentration through the enhancement by both ${\bullet}{\cdot}$-Al refinement and eutectic Si modification. More extensive use of the AC2BS aluminum alloy containing 35% recycled scrap can be expected in the future.

• Journal of Korea Foundry Society
• /
• v.36 no.2
• /
• pp.67-74
• /
• 2016

The effects of scrap content on the hot tearing property and tensile property were investigated in AC2BS alloy. The hot tearing strengths were $16.4kgf/cm^2$, $15.2kgf/cm^2$, $14.9kgf/cm^2$ and $13.3kgf/cm^2$, respectively, under the constant solid fraction of 29.3% when the scrap contents of the specimens were 0%, 20%, 35% and 50%. In the same way, tensile strengths of the as-cast condition were $24.5kgf/mm^2$, $23.7kgf/mm^2$, $17.3kgf/mm^2$ and $16.0kgf/mm^2$, respectively, and the corresponding tensile strengths of the T6 heat treatment condition were $27.2kgf/mm^2$, $26.7kgf/mm^2$, $24.2kgf/mm^2$ and $23.9kgf/mm^2$. Hot tearing strength and tensile strength decreased as scrap content of the specimen increased. According to the evaluation of the quantitative hot tearing and tensile test results, the decrease of these strengths is due to the presence of oxide films which act as crack initiation site of the specimens. Therefore, elimination of oxide films of aluminum melt to maintain melt cleanliness is required.