• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.147-151
• /
• 2016

The T91 steel (Fe-9%Cr-1%Mo) was corroded at 600 and $700^{\circ}C$ for 5 - 70 h in the $N_2$/(0.5, 2.5)%$H_2$Smixed gas at one atm. It was corroded fast, forming the outer FeS layer and the inner (FeS, $FeCr_2O_4$)-mixed layer. The formation of the outer FeS layer facilitated the oxidation of Cr to $FeCr_2O_4$ in the inner layer. Since the nonprotective FeS scale was present over the whole scale, T91 steel displayed poor corrosion resistance.

• Applied Chemistry for Engineering
• /
• v.9 no.7
• /
• pp.1023-1029
• /
• 1998

Small water leak experiment was carried out for the 5Cr-1Mo steel specimen in sodium atmosphere. Perfect re-open time for the leak path of a specimen, by micro leak, was 129 minutes, and its size observed about 2 mm diameter at sodium side. The halos phenomena appeared around of leak spot before the leak path has re-opened, and the size of halos observed was different from the real re-open size of a specimen. Also, the corrosion of a specimen initiated from sodium side, but it did not occur at steam side. In AES analysis, the segregation phenomena of Cr in the specimen was found much more than those of other elements. And also, the sodium compounds formed by sodium-water reaction and deposited onto the leak site of specimen were observed by EPMA analysis and SEM photograph. It is postulated that the corrosion products could be precipitated to form mixed Na Fe Cr compounds.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.3
• /
• pp.251-257
• /
• 2011

This paper deals with the statistical properties of parameters B and q in the creep crack growth rate (CCGR) law, da/dt=B$(C^*)^q$, in Mod. 9Cr-1Mo (ASME Gr.91) steel which is considered a candidate materials for fabricating next generation nuclear reactors. The CCGR data were obtained by creep crack growth (CCG) tests performed on 1/2-inch compact tension (CT) specimens under an applied load of 5000N at a temperature of $600^{\circ}C$. The CCG behavior was analyzed statistically using the empirical equation between CCGR, da/dt and the creep fracture mechanics parameter, $C^*$. The B and q values were determined for each specimen by the least-squares fitting method. The probability distribution functions for B and q were investigated using normal, log-normal, and Weibull distributions. As far as this study is considered, it can be appeared that B and q followed the log-normal and Weibull distributions. Moreover, a strong positive linear correlation was found between B and q.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.9
• /
• pp.2819-2832
• /
• 1996

The estimation of the remaining life for the aged components in power plant as well as chemical and petroleum plants has been recently concerned. The raw materials used in this study are the 1Cr-1Mo-0.25V steel which intensified P and S compositions along with the nominal compositions of ASTM A 470 standard. Five kinds of specimens with the different degradation levels were prepared by isothermal aging heat treatment at 630.deg.C. The mechanical properties and rotated bending fatigue strength of virgin and aged 1Cr-1Mo-0.25V steel have been investigated through the hardness, tensile, fatigue test, SEM fractograph and EDS analysis at 538.deg.C and room temperature, respectively. Thus the data of aged specimens were compared with those of virgin specimen to evaluate the aging effects. The main results obtained in this study are as follows ; The decrease of the yield and tensile strength due to degradation was distinguished until 50, 000hrs simulated service time. And it was confirmed that the considerable amount of P, Mn, Cr and S was precipitated at the grain boundary of aged material through the SEM and EDS analysis. The rotated bendingd fatigue strength at 538.deg.C of virgin, 25, 000, 50, 000, 75, 000 and 100, 000 hrs aged material was decreased 44.6 %, 49.6 %, 51.5 %, 52.4% and 53.8% than that of virgin material at 10$_{7}$cycles of room temperature, respectively. The major cracks of virgin and aged materials mainly initiated at the inclusions including Si, P and Mn compositions which were located at the outer periphery of the specimen.n.

• Proceedings of the KSME Conference
• /
• 2005.11a
• /
• pp.118.1-118.1
• /
• 2005

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.12-17
• /
• 2003

The effects of Cr content and film formation potential on electronic behaviors of the passive film on Fe-Cr alloys were investigated in borate buffer solution. Influence of pH on passive films of both Fe-Cr and Fe-Cr-Mo alloys was also investigated. Mott-Schottky and cyclic voltammetry techniques were used to elucidate electronic behaviors of passive films and their electrochemical characteristics. AES analysis of passive films was carried out. Results showed that doping density decreased as Cr content and film formation potentials increased. The addition of Mo to Fe-Cr alloy had little influence on donor densities in pH 9.2 solution but some effects on the decrease in donor densities in pH 1.6 acidic solution.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.111-116
• /
• 2001

Small punch-creep(SP-Creep) test technique has been applied for evaluating the creep characteristics for high temperature materials. However, in order to evaluate the damage and predict the remaining life, it is necessary to establish a quantitative correlation between SP-Creep and uniaxial-creep test results. This paper presents analytical and experimental results of useful correlation between SP-Creep and uniaxial-creep properties for 9Cr1MoVNb steel at $600{\sim}650^{\circ}C$ in terms of stress(load) and activation energy during creep deformation. Especially, the activation energy obtained from SP-Creep test is linearly related to that from uniaxial-creep test at $650^{\circ}C$ as follows: $Q_{sp-p}{\fallingdotseq}1.37\;Q_{TEN},\;Q_{sp-{\sigma}}{\fallingdotseq}1.53\;Q_{TEN}$.

• Korean Journal of Metals and Materials
• /
• v.47 no.10
• /
• pp.621-628
• /
• 2009

Thermomechanical processes were carried out to evaluate their effects on the mechanical and the microstructural property of a ferritic-martensitic steel. Modified 9Cr-1Mo steels were hot-rolled at a temperature of either $780^{\circ}C$ or $850^{\circ}C$ after normalizing at $1050^{\circ}C$ and then were air-cooled. Continuous annealing at $850^{\circ}C$ for 2 hours immediately after the hot rolling was also performed and they were compared to the specimens without thermomechanical process. The result showed that there were little differences between the hot rolled specimens in terms of the precipitation density and size. However, V content inside the MX precipitates increased in the case of the specimen rolled at $850^{\circ}C$. The application of the continuous annealing induced coarsening of the Nb-rich MX precipitation as well as an increase in the amount of V-rich MX precipitation, which is expected to enhance high temperature mechanical properties of the ferritic-martensitic steel.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.385-386
• /
• 2006

For attaining optimum fatigue resistance of PM steels, high density levels are necessary. In this work, sintered steels Fe-1.5%Mo-0.6%C and Fe-1.5%Cr-0.2%Mo-0.6%C were produced with density levels of 7.1 to $7.6\;g.cm^{-3}$. Ultrasonic fatigue testing with 20 kHz was performed in push-pull mode up to 10E9 cycles. It was shown that the fatigue endurance strength is strongly improved by higher density levels, but also higher sintering temperatures are beneficial. The Cr-Mo steels proved to be superior to the plain Mo alloyed, due to a more favourable as-sintered matrix microstructure.