• Journal of Welding and Joining
• /
• v.10 no.3
• /
• pp.40-53
• /
• 1992

고온고압장치(High Temperature and Pressure Vessels)의 적용을 위한 기초연구로서 9Cr-1Mo강 용접부의 연화특성에 대하여 검토하였다. 9Cr-1Mo 강재에 Bead-on-Plate용접을 실시한 후, 용접부의 기계적 성질과 그 현미경조직관찰 및 미세경도를 측정한 결과, As-Welded 및 용접 후열처리(PWHT)등의 조건에 관계없이 용접열향부의 변태역과 템퍼링역의 경계에서 모재의 경 도보다 낮은 경도값(연화역)을 나타내었으며 이러한 원인은 결정립계(Grain boundary)에 석출 되는 탄화물의 형성에 의한 뜨임 현상임이 판명되었다.

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.637-642
• /
• 2003

The Modified 9Cr-1Mo steel identified as T91, P91 and F91 in the ASME specification has been widely used for the construction of modern power plants. The available data on the influence of process parameters during manufacturing and fabrication on its properties are not sufficient. In this study, the influence of various thermal cycles on the hardness and the creep rupture strength was analyzed in the base metal and the weldments made in tube and pipe of a Mod.9Cr-1Mo steel. The low hardness, 155Hv, showed low creep rupture strength below the allowable stresses of T91 base metal in the ASME specification. This low value was attributed to the fully recovered dislocation structure and the weakening of precipitation hardening associated with the abnormal thermal cycles.

• Journal of Welding and Joining
• /
• v.14 no.3
• /
• pp.75-85
• /
• 1996

In this paper the influence of postweld heat treatment on mechanical properties of SMAW and FCAW stainless steel weldments was examined and the obtained results are as follows ; (1) The amount of $\delta$-ferrite formed by SMAW and FCAW process decreased with increasing holding temperature and time in post weld heat treatment(PWHT), and it was found that the reduced ferrite was transformed into sigma phase after $800^{circ}C{\times}50hr$ PWHT. This sigma phase, even though it was very small, resulted in brittleness of dissimilar weldment between carbon steel and stainless steel in bending test, however in similar weldment between stainless steel and stainless steel was not occured. (2) The chemical composition of sigma phase was measured to 28-30%Cr, 7-9%Mo, 4-6Ni in 316L weldment, and also 35-37%Cr, 0.9-1.0Mo, 6-8%Ni in 309L weldment by EDS analysis.