High strength 7xxx aluminum alloys have been applied to automotive bump back beam of the some limited model for light weight vehicle. The aluminum bump back beam is manufactured through extrusion, bending and welding. The residual stress given on these processes combines with the corrosive atmosphere on the road spreaded with corrosive chemicals to melt snow to occur the stress corrosion cracking. The composition of commercial 7xxx aluminum has Zn/Mg ratio about 3 and Cu over 2 wt% for better strength and stress corrosion cracking resistivity. But this composition isn't adequate for appling to the automotive bump back beam with high resistance to extrusion and bad weldability. In this study the composition of 7xxx aluminum alloy was modified to high Zn/Mg ratio and low Cu content for better extrusion and weldability. To estimate the resistivity against stress corrosion cracking of this aluminum alloy by slow strain rate test, the corrosion atmosphere and strain rate separate the stress corrosion cracking from conventional corrosion must be investigated. Using 0.6 Mol NaCl solution on slow strain rate test the stress corrosion cracking induced fracture was not observed. By adding 0.3% $H_2O_2$ and 0.6M $Na_2SO_4$ to 1M NaCl solution, the corrosion potential and current density of polarization curve moved to active potential and larger current density, and on the slow strain rate test the fracture energy in solution was lower than that in pre-exposure. These mean the stress corrosion cracking induced fracture can be estimated in this 1M NaCl + 0.3% $H_2O_2$ + 0.6M $Na_2SO_4$ solution. When the strain rate was below $2{\times}10^{-6}$, the stress corrosion cracking induced fracture start to be observed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.10a
• /
• pp.30-33
• /
• 2005

Although extruded aluminium bumper beam has been commonly used in advanced car makers, there are not so much precedent for it's localization. For the localization of aluminum bumper beam of 7XXX series, benchmarking, material modifications of 7XXX series aluminum alloy, section design of beam, impact analysis had been performed in this study. High fuel efficiency and weight reduction could be achieved by using aluminum bumper beam of which the weight is lighter than that of steel. Moreover, it is expected to reach higher recycling rate by substituting aluminum for steel.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.109-113
• /
• 2008

High strength 7xxx series Al-Zn-Mg alloy have been investigated for using light weight automotive parts especially for bump back beam. The composition of commercial 7xxx aluminum has the Zn/Mg ratio about 3 and Cu over 2 wt%, but this composition isn't adequate for appling to automotive bump back beam due to its high resistance to extrusion and bad weldability. In this study the Zn/Mg ratio was increased for better extrusion and Cu content was reduced for better welding. With this new composition we investigated the effect of composition on the resistivity against stress corrosion cracking. As the Zn/Mg ratio is increased fracture energy obtained by slow strain rate test was decreased, which means degradation of SCC resistance. While the fracture energy was increased with Cu contents although it is below 1%, which means improvement of SCC resistance. These effects of composition change on the SCC resistivity were identified by observing the fracture surface and crack propagation.

• Laser Solutions
• /
• v.14 no.2
• /
• pp.1-7
• /
• 2011

The latest trends of vehicle technology development are fuel efficiency improvement, body designs declining air resistance and lightweight of materials. Especially, as lightened weight of materials makes engine efficient so that vehicles keep the best performance, it is the best way to protect the environment and reduce fuel consumption. In this study, we conducted laser welding by using 3-dimension remote scanner that is 5J32 aluminium alloy. Furthermore, conduction experiment that was 3 times repeated for changing factors such as observing angle, laser power and welding speed. we observed exterior and cross section of weled part and tensile strength. When increasing laser power and decreasing laser speed, tensile strength increased. In order to evaluate factors that affect tensile strength qualitatively we conducted ANOVA. We assumed that the factors are observing angle, laser power and welding speed. Then we found that laser power and laser speed affect tensile strength. We conducted evaluation of weldability of aluminium alloy by above ways.